血清肌酸激酶活性与运动复合伤及其干预效果的关系

目的探讨血清肌酸激酶(Ck)活性与运动复合伤的关系及其干预效果。方法监测16名女子排球运动员血清Ck活性和运动损伤部位的数量,分析两者之间的关系及干预前后血清Ck活性的变化。结果 16名运动员均发生过不同程度的运动损伤,人均4.4个部位,血清Ck活性与损伤部位数呈正相关(r=0.68),当Ck≥500 u/l时,运动损伤的风险明显加大;干预后血清Ck活性平均由(774.01±769.02)u/l下降至(240.53±186.50)u/l,差异有统计学意义(P<0.05)。结论定期监测血清Ck活性对预警、预防运动损伤,调节运动总负荷具有重要的参考意义

一期翻修术治疗膝关节假体周围感染的疗效分析

目的探讨一期膝关节翻修术治疗膝关节假体周围感染的安全性及有效性。方法选取2015年1月～2018年6月厦门大学附属福州第二医院因膝关节假体周围感染接受一期膝关节翻修术的患者28例。收集患者的人口统计学资料、感染病原,并回顾性分析患者术前及术后KSS、HSS与OKS评分及影像学资料,评估膝关节假体周围感染接受一期膝关节翻修术的安全性及临床疗效。结果 28例接受一期膝关节翻修术的患者,男14例,女14例,平均年龄(65.3±10.1)岁,截止到末次随访,除1例患者死亡(死于心肌梗死)失访外,其余27例患者平均随访25.7个月(13～39个月),未发现假体松动及假体周围感染复发。患者术前KSS评分平均(34.19±13.00)分,末次随访时平均(76.37±16.46)分;术前HSS评分平均(36.03±13.39)分,末次随访时平均(71.24±16.39)分;术前OKS评分平均(16.62±3.47)分,末次随访时平均(27.43±6.02)分,差异有统计学意义(P <0.05)。结论在选择合适适应证情况下,膝关节置换术后假体周围感染的患者通过一期膝关节翻修术可以有效控制感染并重建膝关节功能。福建省自然科学基金项目(2017J01333

喷印柔性压力传感器试验研究

柔性压力传感器是智能机器人和生物医疗等典型应用领域中的关键部件。针对10～50 kPa中等压力下对柔性压力传感器的高灵敏度、良好压力分辨率和快速响应需求,提出在PDMS基底上直写喷印石墨烯纳米片(GNPs)/多壁碳纳米管(MWCNT)构建S型折线图案化敏感单元,结合封装层微结构阵列,制备中压高灵敏度、低检测限的柔性压力传感器。试验结果表明,在压力为0～15 kPa和15～40 kPa的条件下,该传感器灵敏度分别为0.114 kPa–1和1.41 kPa–1,响应/恢复速度快(约100 ms/50ms)。同时,其也可检测低至约3Pa的微小压力。同时,该传感器更是能对不同发声进行准确的区分识别,对不同的指压信号进行精确稳定反馈。可见,喷印制造柔性压力传感器将为语音识别、人工假肢、制备高性能电子皮肤和医疗康复器件等提供可能的优选方案

Effect of Stress on Electrochemical Behaviour of Various Thermal History Zones and Different Phase Structures on the Weldment for Low Alloy Steel

采用微区相电化学测试技术，测量和研究了１６Ｍｎ钢焊接接头上不同热经历区在硝酸盐溶液中的微区相电化学行为（包括自腐蚀电位、自腐蚀电流密度和极化曲线）以及外加载荷（应力）的影响．此外，还分别测量了各区中铁素体和珠光体的电化学行为，尤其是加载状态下的行为．结果表明，加载后各热经历区以及各区中铁素体和珠光体的自腐蚀电位均比未加载前负移，相应的自腐蚀电流密度增大，铁素体和珠光体之间电位差明显减小．加载后各热经历区中自腐蚀电位最负和次负的仍处在熔合线区和不完全正火区，从而成为焊接接头腐蚀电池中的率先腐蚀区．应力促进腐蚀并非是通过增大铁素体和珠光体之间的电位差，而是通过提高各微区相组织自身的电化学活性来实现的．The electrochemical behaviour of various thermal history zones on the weldment for steel 16Mn and also of the ferrite,pearlite in various zones was measured by use of a self-developed measuring technique for investigating the electrochemicl behaviour of single and mixed phase structures in metal materials.Especially the effect of stress on this electrochemical behaviour was investigated.The results showed that by comparison with non-stress condition,the free corrosion potential of the various thermal history zones and of the ferrite,pearlite under stress condition was shifted in negative direction,correspondingly their free corrosion current density was increased,the free corrosion potential difference between ferrite and pearlite was decreased obviously. After applying stress the negativest and the second negativest free corrosion potentiats between vavious thermal history zones were still for the fusion line zone and the incomplete normallized zone,which thereby were become the preferrentially corroded locations on the weldment as a corrosion cell.The stress accelerated corrosion course that did act not through inceasing free corrsion potential difference between ferrite and pearlite,but through enhancing the electrochemical activity of the relevant micro zone and/or phase strueture.作者联系地址：北京科技大学表面科学与腐蚀工程系Author's Address: Univ. of Science and Technology Beijing, Beijing 100083, Chin

塔里木河流域适应气候变化的水热调节技术研究

本成果来自于国家科技支撑计划项目“全球环境变化应对技术研究与示范”之06课题“典型脆弱区域气候变化适应技术示范”之04专题“西北生态脆弱区适应气候变化技术示范”(2007BAC03A06-04)。课题于2007年11月立项,于2010年11月30日通过国家科技部的验收。针对塔里木河流域气候变化影响关键科学问题,建立了山区水库—平原水库联合调节、绿洲地表水—地下水联合开发、膜下滴灌的作物立体种植模式、下游生态恢复与洪水(融雪水)沙漠造林生物固碳等大型原位可控的技术示范基地;构建了区域气候变化优势适应技术筛选与评估流程,集成了塔里木河流域气候变化适应技术行动实施方案与功能区划图,首次提出了塔里木河..