КОРРОЗИОННАЯ СТОЙКОСТЬ ЛЕГИРОВАННЫХ ВАНАДИЕМ ГАЛЬВАНИЧЕСКИХ ЦИНКОВЫХ ПОКРЫТИЙ

The possibility of vanadium-alloyed zinc coatings electrochemical deposition from alkaline electrolyte containing 5.5 g/l Na3VO4 has been shown. Vanadium content in zinc coating depends on cathodic current density and is 1.5–4.1% under cathodic deposition current 1–3 A/dm2. The process of chemical passivation of galvanic coating have been studied in sodium vanadate solution at 20–40 °C temperature, with pH 3 kept constant by phosphoric acid. It has been shown by XRD method that conversion coatings formed consist of Zn, ZnO, V2O5, V(HPO4)2, Zn3(PO4)2. The corrosion current of passivated alloyed zinc coatings deposited at 2 A/dm2 was 4.1–12.6 times less than corrosion current of alloyed zinc in 3% NaCl solution. Conversion coatings demonstrate high protective ability when treated with lead acetate solution (50 g/dm3 ). Показана возможность электрохимического осаждения легированного ванадием цинкового покрытия из щелочного электролита с содержанием 5,5 г/дм3 Na3VO4. Содержание ванадия в цинковом покрытии находится в пределах 1,5–4,1 % при катодной плотности тока осаждения покрытия 1–3 А/дм2 . Изучен процесс химической пассивации гальванических покрытий в растворе ванадата натрия при температуре 20–40 °С, значение рН которого поддерживалось равным 3 ортофосфорной кислотой. Методом РФА в составе образованных конверсионных покрытий обнаружены Zn, ZnO, V2O5, V(HPO4)2, Zn3(PO4)2. Ток коррозии пассивированных легированных цинковых покрытий, осажденных при 2 А/дм2, в 3 %-ном растворе хлорида натрия снижается в 4,1–12,6 раза по сравнению с непассивированным покрытием. Показано, что конверсионные покрытия на основе ванадия обладают высокой защитной способностью при воздействии раствора ацетата свинца (50 г/дм3 ).

Влияние цитратного электролита меднения, его компонентов и добавок ультрадисперсных алмазов на поверхностные свойства стали

The state of the steel substrate (steel 3) was studied before the application of composite copper coatings from citrate copper-plating electrolyte. The properties of steel base in the investigated copper-plating electrolyte with the addition of ultradispersed diamonds (UDD) have been studied. A component-by-component analysis of the citrate copper-plating electrolyte was carried out, and the effect of each component on the properties of the steel electrode was evaluated. The possibility of using the considered electrolyte for coating directly on steel is shown, which significantly distinguishes it from currently used ethylenediamine, pyrophosphate, acid and other electrolytes. Electrochemical impedance spectroscopy and cathodic polarization were used as research methods. It was found that the lowest resistance of the steel surface (about 15 Ω) corresponded to the sample immersed in citrate copper-plating electrolyte with the addition of 1.0 g/l of UDD. Diffusion current density for suspensions with 1.0 g/l UDD in citrate copper-plating electrolyte was 2.6 A/dm2. Ultradispersed diamonds in citrate copper-plating electrolyte shielded the surface of the steel sample, while reducing the total resistance of the passive layer of steel 3. Equivalent electrical circuits of the surface of steel samples immersed in citrate copper-plating electrolyte and its components are also presented.  Проведены исследования состояния стальной подложки (Ст 3) перед нанесением композиционных медных покрытий из цитратного электролита меднения. Изучены свойства стальной основы в исследуемом электролите меднения с добавкой ультрадисперсных алмазов (УДА). Проведен покомпонентный анализ цитратного электролита меднения и оценено влияние каждого компонента на свойства стального электрода. Показана возможность применения рассматриваемого электролита для нанесения покрытий непосредственно на сталь, что значительно отличает его от используемых в настоящее время этилендиаминовых, пирофосфатных, кислотных и других электролитов. В качестве методов исследования применяли электрохимическую импедансную спектроскопию и катодную поляризацию. Установлено, что наименьшее сопротивление поверхности стали (около 15 Ом) отвечало образцу, погруженному в цитратный электролит меднения с добавлением 1,0 г/л УДА. Диффузионная плотность тока для суспензий с 1,0 г/л УДА в цитратном электролите меднения составила 2,6 А/дм2. Ультрадисперсные алмазы в цитратном электролите меднения экранировали поверхность стального образца, при этом снижая общее сопротивление пассивного слоя стали Ст 3. Также представлены эквивалентные электрические схемы поверхности стальных образцов, погруженных в цитратный электролит меднения и составляющие его компоненты.

АНТИКОРРОЗИОННЫЕ СВОЙСТВА ПИГМЕНТОВ НА ОСНОВЕ ВАНАДАТОВ ВИСМУТА И КАЛЬЦИЯ

BiVO4, Ca3(VO4)2 and mixed Ca3(VO4)2 BiVO4 vanadates of chemical composition have been synthesized by solvo-thermal method. Dispersibility of obtained BiVO4 pigment is 3,33-0,20 цгп-1, oil adsorption for BiVO4, Ca3(VO4)2 and mixed Ca3(VO4)2 BiVO4 pigments is 24, 23 and 21 g for 100 g of the pigment respectively, density of all synthesized pigments is in range of 4,4-4,7 g/dm3. pH value of aqueous suspensions for all obtained pigments is in range of 7,0 ± 0,5 that provides immunity of steel substrate in contact with pigments. In presence of pigments (5g/l in 3% sodium chloride solution), corrosion current decreases 2,4 times with BiVO4; 5,8 times with Ca3(VO4)2 BiVO4 and 7,6 times with Ca3(VO4)2.Сольвотермическим методом синтезированы ванадаты BiVO4, Ca3(VO4)2, а также смешанный ванадат Ca3(VO4)2 BiVO4. Дисперсность синтезированного пигмента BiVO4 составляет 3,33-0,2 мкм-1. Значения маслоемкости первого рода для синтезированных пигментов BiVO4, Ca3(VO4)2BiVO4 и Ca3(VO4)2 составляют 24, 23 и 21 г/100г соответственно, плотности порошков находятся в интервале 4,4-4,7 г/дм3. Значения рН водных суспензий для всех исследуемых ванадатов находятся в интервале 7,0 ± 0,5, что обеспечивает устойчивость стальной подложки при контакте с пигментами. При введении порошков пигментов в количестве 5 г/дм3 в 3 %-ный раствор хлорида натрия ток коррозии углеродистой стали уменьшается в 2,4 раза в присутствии BiVO4; в 5,8 раза в присутствии Ca3(VO4)2 BiVO4; в 7,6 раза в присутствии Ca3(VO4)2

Электрохимическое осаждение желтой латуни в условиях импульсного электролиза

Electrodeposition of copper-zinc alloy of non-cyanide sorbate electrolyte at current densities of 1,0-3,5 A/dm2 allows to produce yellow brass with a copper content of about 63-64 wt.°%. Using pulsed current allows to intensify the process of deposition 1,3-1,6 times and to increase the current efficiency of the alloy by 1,2-4,2 %. Coatings obtained by pulsed electrolysis have fine-grained structure, more compact and with good adhesion to the steel substrate. Imposition of pulsed current allows deposition of homogeneous phase coating and eliminates formation of intermetallic compounds.Приведены результаты исследований бесцианистого сорбатного электролита латунирования и полученных из него покрытий. Исследованы кинетические особенности совместного осаждения меди и цинка. Изучено влияние импульсного тока и параметров нестационарности на диапазон рабочих плотностей тока и качество латунных покрытий. Выбраны оптимальные режимы осаждения латунных покрытий в условиях импульсного электролиза. Приведены результаты исследования влияния импульсного тока на фазовый состав и микроструктуру осажденного сплава

Pre-hypertension and cardiovascular risk in young men from the Far East Military Region

Aim. To study the prevalence of arterial pre-hypertension (pre-AH), its risk factors (RFs) and associated clinical states (ACS) in young and middle-aged male officers — contract workers in the Far East Military Region (FEMR).Material and methods. In total, 1250 men — contract workers in the FEMR were examined (mean age 33,0±0,22 years), with 95,7% response rate (n=1197). The examination included questionnaire survey, blood pres­sure (BP) measurement, anthropometry and medical history analysis, with the following completion of the “BP monitoring participant chart”.Results. Among young men, most participants had optimal or normal BP. High normal BP was registered in every 10 th person. It total, 612 individuals were diagnosed with pre-AH (74,73%). Overweight (OW), obesity, and hyper­cholesterolemia were significantly more prevalent in pre-AH patients. Mean body mass index and total cholesterol levels were also higher in pre-AH individuals. Among pre-AH patients, 381 (62,25%) had low cardiovascular risk, and 13 (2,12%) — moderate cardiovascular risk.Conclusion. Pre-AH is widely prevalent in young male officers from the FEMR. Considering the professional specifics and high RF prevalence, these people need active monitoring by the military medical service