Abstract
BiVO4, Ca3(VO4)2 and mixed Ca3(VO4)2 BiVO4 vanadates of chemical composition have been synthesized by solvo-thermal method. Dispersibility of obtained BiVO4 pigment is 3,33-0,20 цгп-1, oil adsorption for BiVO4, Ca3(VO4)2 and mixed Ca3(VO4)2 BiVO4 pigments is 24, 23 and 21 g for 100 g of the pigment respectively, density of all synthesized pigments is in range of 4,4-4,7 g/dm3. pH value of aqueous suspensions for all obtained pigments is in range of 7,0 ± 0,5 that provides immunity of steel substrate in contact with pigments. In presence of pigments (5g/l in 3% sodium chloride solution), corrosion current decreases 2,4 times with BiVO4; 5,8 times with Ca3(VO4)2 BiVO4 and 7,6 times with Ca3(VO4)2.Сольвотермическим методом синтезированы ванадаты BiVO4, Ca3(VO4)2, а также смешанный ванадат Ca3(VO4)2 BiVO4. Дисперсность синтезированного пигмента BiVO4 составляет 3,33-0,2 мкм-1. Значения маслоемкости первого рода для синтезированных пигментов BiVO4, Ca3(VO4)2BiVO4 и Ca3(VO4)2 составляют 24, 23 и 21 г/100г соответственно, плотности порошков находятся в интервале 4,4-4,7 г/дм3. Значения рН водных суспензий для всех исследуемых ванадатов находятся в интервале 7,0 ± 0,5, что обеспечивает устойчивость стальной подложки при контакте с пигментами. При введении порошков пигментов в количестве 5 г/дм3 в 3 %-ный раствор хлорида натрия ток коррозии углеродистой стали уменьшается в 2,4 раза в присутствии BiVO4; в 5,8 раза в присутствии Ca3(VO4)2 BiVO4; в 7,6 раза в присутствии Ca3(VO4)2