Long-term consumption of fatty foods is associated with obesity, macrophage activation and inflammation, metabolic imbalance, and a reduced lifespan. We took advantage of Drosophila genetics to investigate the role of macrophages and the pathway(s) that govern their response to dietary stress. Flies fed a lipid-rich diet presented with increased fat storage, systemic activation of JAK-STAT signaling, reduced insulin sensitivity, hyperglycemia, and a shorter lifespan. Drosophila macrophages produced the JAK-STAT-activating cytokine upd3, in a scavenger-receptor (crq) and JNK-dependent manner. Genetic depletion of macrophages or macrophage-specific silencing of upd3 decreased JAK-STAT activation and rescued insulin sensitivity and the lifespan of Drosophila, but did not decrease fat storage. NF-κB signaling made no contribution to the phenotype observed. These results identify an evolutionarily conserved “scavenger receptor-JNK-type 1 cytokine” cassette in macrophages, which controls glucose metabolism and reduces lifespan in Drosophila maintained on a lipid-rich diet via activation of the JAK-STAT pathway
The effect of Ti or Zr additions on the microstructure and magnetic properties of MnAl-C alloys
As-transformed and hot-deformed samples of MnAl-C alloys with Ti or Zr additions have been produced and characterized using magnetometry, X-ray diffraction, scanning electron microscopy and transmission electron microscopy. Both Ti and Zr additions in MnAl-C alloys form carbide primary phases, TiC and ZrC, which consume the carbon meant to be dissolved in the metastable τ-phase to stabilize it against decomposition. With these two additions, the Curie temperature of τ-phase increases while its stability against decomposition decreases. After hot deformation, the MnAl-C alloys with Ti or Zr additions have lower polarisation and remanence due to the reduced stability of the τ-phase. Adding extra carbon along with Ti to a MnAl-C alloy in order to compensate for the C lost on formation of TiC restored the original stability of the τ-phase. After hot-deformation, this alloy exhibited a lower polarisation and remanence owing to the unexpected formation of the γ2-phase
Fast Food Shutdown: From disorganisation to action in the service sector
This article discusses the Fast Food Shutdown, a strike on 4 October 2018 that involved Wetherspoon, McDonald’s, TGI Fridays and UberEats workers in the United Kingdom. It compares the different strategies of the Bakers Food and Allied Workers’ Union at Wetherspoon and Industrial Workers of the World at UberEats. The two case studies, drawing on the authors’ ongoing ethnographic research, provide important examples of successful precarious worker organising. In particular, the argument focuses on the role of action in organising, as well as the relationship between the rank-and-file and the union. While these could point the way to the recomposition of the workers movement – both in greenfield sectors and within existing unions – there remain important questions about how these experiences can be generalised
Recommended from our members
The Influence of Cu-Additions on the Microstructure, Mechanical and Magnetic Properties of MnAl-C Alloys
Alloys of the form (Mn54Al44C2)100-xCux (with x = 0, 1, 2, 4 and 6) were produced by induction melting. After homogenisation and quenching, most of the alloys consist entirely of the retained ε-phase, except for x = 6, in which the κ-phase was additionally present. After subsequent annealing, the alloys with x ≤ 2 consist entirely of a Cu-doped, ferromagnetic τ-phase, whereas the alloys with x > 2 additionally contain the κ-phase. The polarisation of the alloys at an applied field of 14 T decreases with increasing Cu-content, which is attributed i) to the dilution of the magnetic moment of the τ-phase unit cell by the Cu atoms, which do not carry a magnetic moment, and ii) at higher Cu-contents, to the formation of the κ-phase, which has a much lower polarisation than the τ-phase and therefore dilutes the net polarisation of the alloys. The Curie temperature was not affected by the Cu-additions. The stress needed to die-upset the alloys with x ≤ 2 was similar to that of the undoped alloy, whereas it was much lower for x = 4 and 6, due to the presence of intergranular layers of the κ-phase. The extrinsic magnetic properties of alloys with x ≤ 2 were improved by die-upsetting, whereas decomposition of the τ-phase during processing had a deleterious effect on the magnetic properties for higher Cu-additions
Recommended from our members
Microstructural defects in hot deformed and as-transformed τ-MnAl-C
In this study, detailed microstructural characterisation has been conducted in both as-transformed and hot deformed samples of τ-MnAl-C using transmission electron microscopy. After hot deformation, true twins, dislocations, intrinsic stacking faults and precipitates of Mn3AlC are the main defects in the recrystallised grains. True twins and order twins were distinguished based on differences in their diffraction patterns. A significant fraction of non-recrystallised grains existed, which had microstructures based on combinations of high densities of true twins, dislocations, and deformation bands. The formation of the Mn3AlC precipitates was confirmed and related to the reduction of saturation magnetization and the increase in the Curie temperature of τ-MnAl-C after hot deformation. Antiphase boundaries, which are believed to act as nucleation sites for reverse domains, were not observed in the hot deformed sample
Genomic plasticity and rapid host switching can promote the evolution of generalism : a case study in the zoonotic pathogen Campylobacter
This work was supported by the Biotechnology and Biological Sciences Research Council (BBSRC) grant BB/I02464X/1, the Medical Research Council (MRC) grants MR/M501608/1 and MR/L015080/1, and the Wellcome Trust grant 088786/C/09/Z. GM was supported by a NISCHR Health Research Fellowship (HF-14–13).Peer reviewedPublisher PD
- …