Solubility of power plant fly ashes in high-alkali environment

Tato práce se zabývá studiem alkalicky aktivovaných popílků z vysokoteplotního a fluidního spalování uhlí ve třinácti uhelných elektrárnách České republiky. Užitým alkalickým aktivátorem je v tomto případě 50% roztok hydroxidu sodného. Jelikož dvěma nejzastoupenějšími složkami těchto druhotných surovin jsou křemík a hliník, hlavním úkolem této práce je zkoumání závislosti jejich uvolňování do roztoku na době rozpouštění. Druhým cílem je srovnání fázového složení popílků před alkalickou aktivací a po ní.This work deals with study of alkali activated ashes from high-temperature and fluidized bed coal combustion in thirteen powerplants in Czech republic. A solution of 50% sodium hydroxide was used as an alkali activator in this case. Because the two main elements of these secondary raw materials are silica and aluminum, the main part of the work is study of their evolution to solution and dissolve time dependence. The second part is comparing of the phase composition of powerplant ashes before alkali activation and after that.

Low-Cost Filtration Barriers for Ultrafine Particles Separation

V mnoha oborech jsou stále využívána anorganická filtrační media založená na materiálech, jejichž výroba využívá primární suroviny. Jejich výroba je tedy energeticky náročná a v důsledku nákladná a neohleduplná k životnímu prostředí. Cílem této práce je ověřit možnost využití alkalicky aktivovaných materiálů na bázi sekundárních surovin, především vysokopecních strusek (BFS) a popílků z uhelných elektráren (FA), pro výrobu porézních médií schopných v budoucnosti nahradit keramické a jiné anorganické filtry. Výzkum je rozvinut skrze experimentální design založený na výpočetním schématu samostatně vyvinutém s pomocí programu MATLAB. Toto schéma počítá vhodná složení směsí na základě poměrů obsahu nejdůležitějších oxidů ve vstupních surovinách. Tak je zajištěno zohlednění proměnlivého složení vstupních surovin a práce je tím hodnotnější, že její výsledky jsou skrze početní nástroj zohledňující základní oxidové složení surovin zobecnitelné. Zároveň byly však pro srovnání a lepší názornost závislostí vlastností na složení navrhnuty a připraveny i série vzorků založené vždy pouze na jedné ze surovin. Z výsledků vyplývá, že pevnost vzorků z těchto směsí (vytvrzených 24 hodin při 70 °C) ve čtyřbodové ohybové zkoušce dle ČSN EN 12390 5 může přesáhnout 7,6 MPa. Dosažením co možná nejvyšší porozity však zákonitě negativně ovlivňuje pevnost materiálu a výsledný materiál tedy dosahuje pevnosti těsně nad hranicí 6,3 MPa. Výsledky obecně dokazují, že nejvíce je pevnost materiálů ovlivněna poměrem SiO2/Al2O3 a množstvím alkalického aktivátoru. Z výsledků vyplývá, že alkalicky aktivované materiály (AAM) na bázi strusky dosahují i více než dvojnásobné pevnosti analogických materiálů na bázi elektrárenského popílku. Velikost pórů materiálů připravených z tříděných surovin s velikostí zrna od desítek po lehce přes sto mikronů se ve většině případů pohybuje v rozmezí desetin ž jednotek mikronů, v případě výsledného materiálu je to pak přibližně 0,2 mikronu. Celková porozita lisovaných těles se pohybuje těsně pod 40 %, což je v tomto případě téměř dvojnásobek ve srovnání s totožnými materiály na bázi netříděných surovin. Výsledky rovněž ukazují, že materiály na bázi strusky vykazují nižší porozitu než ty na bázi popílku, což je patrně způsobeno rozdílnou morfologií částic obou materiálů – částice strusky jsou nepravidelně hranaté a částice popílku kulaté. V průběhu experimentální činnosti byla pozorována tvorba výkvětů u materiálů na bázi elektrárenských popílků. Pomocí Energo-disperzní spektroskopické analýzy (EDS) byly výkvěty identifikovány jako hydroxid sodný procházející karbonatací za účasti vzdušného CO2. Test permeability vyžadoval, kvůli velmi jemné povaze porézní struktury, přípravu asymetrických filtračních přepážek. Tyto přepážky dosáhli propustnosti 138 L/h.m2.bar pro vodu a 1320 L/h.m2.bar pro vzduch.A lot of applications use inorganic filtering media based on materials that use primary resources and their production is energy-intensive and thus costly and environmentally harmful. The aim of this study is to verify whether alkali-activated materials based on secondary resources, namely blast furnace slag (BFS) and fly ash (FA), can be used to produce porous media which could possibly replace ceramic and other inorganic filters. The research question was addressed using an experimental design based on an in-house developed MATLAB calculation scheme for composition mixtures based on the most important oxide ratios in the input raw materials. This way, the greatest control of the variable composition of the inputs was ensured. In addition, the work is more relevant in general because this computational tool takes the basic oxide composition of the resources into account, so the results can be generalized. The author also designed a pure one solid component mixture series for a comparison and better characterization of the effects of composition changes on the resulting product properties. The findings show that the strength of the 24-hour, 70 °C cured materials can exceed 7.6 MPa under a four point bending tensile test (in accordance with ČSN EN 12390 5), but to achieve a good porosity, the strength is always decreased. In the final composition slightly above 6.3 MPa was achieved. In general, the results show that the SiO2/Al2O3 ratio and the amount of alkali activator affect the strength the most. Pure BFS-based mixtures show more than twice the strength of the pure FA-based samples within the given compositions used for the experiments. The fineness of the pores achieved using fractionated raw materials (particle sizes in the range of tens to slightly over a hundred microns) is in the order of tenths to units of microns in most cases and approximately 0.2 microns in the final composition. The total porosity of the pressed bodies is closely under 40% which compared to the unclassified resource based materials, is nearly twice that much. Pure BFS-based samples show lower total porosities than the FA-based samples, apparently due to their entirely different particle morphology – irregularly angular in BFS and round in FA. The efflorescence phenomenon was mostly observed on FA-based materials. Energy-dispersive spectrometry (EDS) confirmed sodium hydroxide crystals undergoing gradual carbonation by atmospheric CO2. Permeability testing required asymmetrical barriers preparation due to the very fine porosity of the material. The asymmetrical barriers achieved water permeability of 138 L/h.m2.bar and air permeability of 1320 L/h.m2.bar.

Genesis of new ultra-fine particles of milling stock in the course of the mill exposure.

Tato práce se zabývá studiem suchého mletí vápence a korundu s využitím promíchávaného mlýna atritorového typu se vsádkovým režimem mletí. Pro experimentální část užitými povrchově aktivními látkami byli stearin a polyethylenglykol, mlecími elementy ocelová kulová tělesa. Těžištěm práce bylo prověřit chování zvoleného typu meliva při dlouhodobější expozici mlecích sil za zvolených podmínek ultrajemného suchého mletí, směřujících do submikronové oblasti. K charakterizaci vzorků bylo využito metod laserové granulometrie, rentgenové práškové difrakční analýzy, plamenové atomové absorpční spektrometrie, objektivního stanovení barevnosti a měření elektrokinetického potenciálu. Z naměřených dat vyplývá, že ve všech případech došlo, i když v různých fázích dezintegračního procesu a ve vzájemně odlišné míře, k reaglomeraci částic meliva. V submikronové velikosti částic lze také, dle výsledků analýz, usoudit na rozrušování krystalových struktur a s ním spojené zvyšování amorfního podílu vzorků.This work deals with the study of limestone and corundum dry milling using attritor-type stirred mill in a batch mode. There were stearin and polyethylene glycol used as surfactants and spherical shaped steel grinding elements used for the experimental part of the work. The main idea was to examine behavior of the selected grinding stock type within a long-term grinding forces exposure in selected conditions of ultrafine dry milling leading up to the submicron area. Characterization of samples was performed by laser granulometry, X-ray powder diffraction analysis, flame atomic absorption spectroscopy, objective color determination and electrokinetic potential measurement. Experimetaly measured data implies that in all cases there was a re-agglomeration of the grinding stock particles occurring, although in different stages of the disintegration process and in mutually various degree. The analysis results denote that a larger erosion of the crystal structures with the associated increase of the amorphous phase in the submicron particle size took place in the grinding stock.

Solubility of power plant fly ashes in high-alkali environment

This work deals with study of alkali activated ashes from high-temperature and fluidized bed coal combustion in thirteen powerplants in Czech republic. A solution of 50% sodium hydroxide was used as an alkali activator in this case. Because the two main elements of these secondary raw materials are silica and aluminum, the main part of the work is study of their evolution to solution and dissolve time dependence. The second part is comparing of the phase composition of powerplant ashes before alkali activation and after that

Pentamethinium Salts Nanocomposite for Electrochemical Detection of Heparin

This study presents a simple route to heparin detection and develops a voltammetric approach using supramolecular principles and nanomaterials. Nanocomposites, including gold nanoparticles (AuNPs) and γ-substituted pentamethinium salts (PMS) deposited on a glass carbon (GC) electrode surface (GC/AuNPs/PMS) and covered by a plasticized poly(vinyl chloride) (PVC) membrane, are proposed for heparin detection. The conductivity of the nonconducting PVC-plasticized membrane is guaranteed by AuNPs, and the selectivity is provided by the interaction between γ-substituted PMS and anionic analytes. In order to extend the linear range, it is necessary to apply a solvent compatible with PVC-plasticized membrane, namely tetrahydrofuran. The proposed voltammetric sensor showed a concentration dependence from 1.72 up to 45.02 IU mL−1 heparin and was used for heparin detection in saline and biological samples with recovery of 95.1–100.9%