Physical and Mechanical Properties of Three Polystyrene Impregnated Indonesian Wood Species

The disadvantage of fast-growing species is that they have inferior physical and mechanical properties. Polystyrene impregnation can be applied to improve physical and mechanical properties. Wood samples, which were dried until 10% moisture content were put into impregnating tank and vacuum pressured at 20-mm Hg for two hours. During the gradual release of vacuum, styrene monomers, vinyl acetate monomers and terburyl-peroxide catalyst was streamed into the tank. Afterwards, the pressure inside the tank was allowed to decrease to 500 mm Hg and kept for 60 minutes. Wood samples which had been impregnated were subsequently immersed in water, then wrapped in aluminum foils and put in the oven for 24 hours at 60°C. The samples were then tested for the polymer loading and their physical and mechanical properties. The results showed that the polymer loadings in wood plastics with the species of origin (i.e. consecutively sengon, pine and rubber wood) were 118%, 72% and 44%, respectively. Impregnation with polystyrene (copolymer of styrene and vinyl acetate monomers) could improve the physical and mechanical properties of wood plastics, i.e. specific gravity, moisture content, water absorption, shrinkage/ swelling, compression parallelto the wood grain, MOR and MOE. Greater use of vinyl acetate decreased physical and mechanical properties

Sifat Papan Partikel Dari Kayu Kulit Manis (Cinnamomum Burmanii Bl)

Kayu kulit manis (Cinnamomum burmannii BL) merupakan salah satu komoditas potensial untuk dikembangkan. Kulit kayunya memiliki bau yang khas, banyak digunakan untuk berbagai keperluan, seperti penyedap rasa makanan atau kue. Bagian batang kulit manis tersebut berupa kayu belum dimanfaatkan optimal selain untuk kayu bakar. Pada proses pengolahan dolok kulit manis menjadi kayu gergajian dihasilkan limbah berupa serbuk dan slab yang dapat dijadikan serpih sebagai bahan baku pembuatan papan partikel. Penelitian untuk mengetahui sifat papan partikel yang dibuat dari limbah tersebut dilakukan dengan cara; partikel kulit manis baik dalam bentuk serbuk gergaji atau serpih, masing-masing dikeringkan dalam oven pada suhu 70 - 90 C sampai mencapai kadar air sekitar 5%, kemudian dicampur dengan serbuk gergaji (sebagai partikel halus) atau terdiri hanya dari partikel saja atau serpih (sebagai partikel kasar), lalu dicetak menjadi lembaran papan partikel menggunakan perekat urea formaldehida (UF), dikempa panas selama 10 menit pada suhu 140 C dengan tekanan 25 kg/cm2. Papan partikel yang dibuat berukuran 30 cm x 30 cmx 1,5 cm dengan kerapatan target masing-masing 0,6, 0,7 dan 0,8 g/cm3. Hasil penelitian menunjukkan bahwa kadar air, kerapatan, pengembangan tebal, keteguhan lentur, keteguhan rekat internal dan kuat memegang sekrup papan partikel yang dihasilkan sudah memenuhi persyaratan Standar Nasional Indonesia, kecuali untuk kerapatan 0,6 g/cm3dan 0,7 g/cm3yang dibuat dari campuran serpih dan serbuk gergaji

The Possibility of Using Timber From Plantation Forest Treated with Plastic and Ccb for Marine Construction

Recently, timber estate or plantation forest plays an important role on wooden based industries. However, the plantation timber quality is relatively low. Some treatments have been developed to improve its low quality, such as preservation with CCB (Chromate Copper Boron) and impregnation with plastic compounds. This study is to compare the durability of timber treated with plastic and CCB, non-treated from plantation forest timber as well as from natural forest. The plantation timber studied were jeungjing (Paraserianthes falcataria), damar (Agathis sp.), pinus (Pinus merkusii), and rubberwood (Hevea Brasilliensis). Non-treated timbers that usually used for marine construction were ulin (Eusideroxylon zwageri), jati/teak (Tectona grandis), laban (Vitex pubescens) and merbau (Instia bijuga). After 6 and 12 months, the results showed that CCB preserved timber were more durable than plastic impregnated timber and non- treated timber. Wood samples were mostly attacked by marine borer organisms from the family of Pholadidae and Teredinidae. The experiment results revealed the possibility of using those plantation forest timber species for marine construction purposes

Sifat Fisis dan Mekanis Kayu Jati Super dan Jati Lokal dari Beberapa Daerah Penanaman

Penelitian sifat fisis dan mekanis kayu jati (Tectona grandis L.f.) jenis lokal dan super dari daerah Binjai, Maros, Parung, Panajam, Kutai, Lampung, Bengkulu dan Palembang bertujuan untuk melihat perbedaan karakteristik sifat fisis dan mekanis kayunya. Hasil penelitian menunjukkan bahwa rata-rata berat jenis (BJ) kayu jati super lebih tinggi daripada kayu jati lokal, sedangkan BJ tertinggi pada kayu jati super adalah dari Binjai dan terendah dari Maros. Jenis jati lokal dan super berpengaruh nyata terhadap berat jenis basah kayu tersebut, sedangkan lokasi penanaman jati tidak memberikan pengaruh yang nyata terhadap berat jenis. Kayu yang terkuat adalah jati lokal dari Palembang, diikuti berturut-turut kayu jati super dari Lampung, jati lokal dari Kutai, jati super dari Bengkulu, jati super dari Kutai, jati lokal dari Binjai, jati super dari Parung, jati super dari Binjai, jati supr dari Palembang, jati lokal dari Lampung, jati lokal dari Sulawesi dan yang terendah jati super dari Sulawesi. Perbedaan BJ tersebut berpengaruh nyata pada kekakuan dan keteguhan tekan sejajar serat, sedangkan lokasi tanaman berpengaruh nyata terhadap kekakuan dan kekuatan patahnya. Kayu jati yang diteliti tergolong kelas kuat III-IV

Penurunan Sifat Fisis dan Mekanis Tiga Jenis Kayu dan Kayu Kelapa terhadap Serangan Penggerek di Laut

Tiga jenis kayu dan kayu kelapa dari Sukaburni, Jawa Barat diuji terhadap penggerek di laut untuk diketahui penurunan sifat fisis dan mekanisnya.Penelitian ini dilakukan di perairan Pulau Rambut dengan contoh uji yang berukuran 5 cm x 5 cm x 106 cm. Contoh uji direnteng dengan tali plastik dan diamati setelah tiga bulan. Hasil penelitian menunjukkan bahwa sebagian besar contoh uji diserang oleh penggerek di laut, sehingga menurunkan sifat fisis dan mekanisnya. Rasamala yang tidak direndam termasuk dalam kelas kuat II dan setelah direndam menjadi kelas kuat III. Kelapa yang tidak direndam termasuk kelas kuat II-III, setelah direndam menjadi kelas kuat IV Karet dan nangka yang tidak direndam termasuk kelas III, setelah direndam kekuatan kayu karet menjadi kelas kuat V dan nangka tetap termasuk dalam kelas kuat III

Daur Teknis Pinus Tanaman Untuk Kayu Pertukangan Berdasar Sifat Fisis Dan Mekanis

Penelitian sifat fisis dan mekanis kayu pinus (Pir111smerkusiiJungh et de Vr.) dengan umur 17, 21, 23, 27 dan 28 tahun dilakukan untuk menentukan daur teknis tanaman tersebut. Hasil penelitian menunjukkan kecenderungan yang sama, yaitu pada umur 17 sampai 19-20 tahun sifat kayu cenderung menurun, kemudian meningkat sampai mencapai maksimum pada sekitar umur 23 tahun dan kembali menurun lagi. Kecenderungan tersebut mengikuti pola hiperbolik. Keteguhan lentur patah kayu pinus yang diteliti tertinggi pada kayu umur 27 tahun dan terendah pada kayu umur 17 tahun. Demikian pula pada kekakuan, keteguhan tekan sejajar serat dan kekerasannya. Perbedaan umur tidak mempengaruhi sifat mekanis kayu. Kerapatan kayu pinus yang diteliti tidak dapat menjadi penduga terbaik untuk MOR-nya, akan tetapi dapat menjadi penduga terbaik untuk keteguhan tekan sejajar serat. Sedangkan MOE dapat menjadi penduga terbaik untuk MOR. Kayu pinus tingkat umur 17 tergolong kelas kuat rv, sedangkan umur 21, 23, 27 dan 28 tahun tergolong kelas kuat III. Menurut sifatnya, maka pinus umur 17 tahun sesuai untuk konstruksi ringan, sedangkan kayu umur 21, 23, 27 dan 28 tahun dapat digunakan untuk kayu bangunan. Daur teknis kayu pinus yang ditentukan berdasarkan sifat fisis dan mekanisnya adalah antara umur 23-26 tahun

Pengaruh Susunan Lamina Kayu Karet Tua terhadap Sifat Kekuatan Balok Silang-i Laminasi

Perakitan balok silang-I laminasi dilakukan menggunakan kayu karet tua (Hevea Brasiliensis) asal pohon karet yang sudah tidak produktif lagi menghasilkan getah lateks (umur sekitar 25-30 tahun). Mula-mula, dolok kayu karet (diameter sekitar 10-25 cm) terlebih dulu dibentuk menjadi lamian (bilah- bilah) melalui penggergajian. Rendemen bilah tersebut (36-39%) masih lebih rendah dari pada rendemen yang umum dari kayu berdiameter besar. Bilah yang dihasilkan dirakit menjadi balok silang-I menggunakan perekat fenol-resorsinol-formaldehida pada suhu kamar. Hasil perakitan menunjukkan kekuatan balok silang-I laminasi dengan profil rekatan horisontal antar lamina dibagian tubuh atau badan (keteguhan lengkung pada batas proporsi = 132.97 kg/cm2, MOR = 184.13 kg/cm2, MOE = 54425.196 kg/cm2, dan keteguhan geser horisontal = 2.9397 kg/cm2) lebih rendah dari pada sifat balok kayu karet utuh berdimensi kecil bebas cacat, tetapi lebih tinggi dari pada balok silang-I laminasi dengan profil rekatan vertikal dan produk balok laminasi (glulam) juga dari kayu karet tua dengan profil rekatan horisontal antar lamina. Di samping itu terdapat korelasi nyata negatif antara sudut jari-jari kayu - bidang rekatan dengan sifat mekanis/ kekuatan balok silang-I laminasi. Ini mengindikasikan prospek positif pembuatan balok silang-I laminasi laminasi dari kayu karet tua dengan profil rekatan vertikal tersebut untuk tujuan konstruksi, karena dapat lebih menghemat pemakaian bahan baku

Daur Teknis Pinus Tanaman untuk Kayu Pertukangan Berdasar Sifat Fisis dan Mekanis

Penelitian sifat fisis dan mekanis kayu pinus (Pir111smerkusiiJungh et de Vr.) dengan umur 17, 21, 23, 27 dan 28 tahun dilakukan untuk menentukan daur teknis tanaman tersebut. Hasil penelitian menunjukkan kecenderungan yang sama, yaitu pada umur 17 sampai 19-20 tahun sifat kayu cenderung menurun, kemudian meningkat sampai mencapai maksimum pada sekitar umur 23 tahun dan kembali menurun lagi. Kecenderungan tersebut mengikuti pola hiperbolik. Keteguhan lentur patah kayu pinus yang diteliti tertinggi pada kayu umur 27 tahun dan terendah pada kayu umur 17 tahun. Demikian pula pada kekakuan, keteguhan tekan sejajar serat dan kekerasannya. Perbedaan umur tidak mempengaruhi sifat mekanis kayu. Kerapatan kayu pinus yang diteliti tidak dapat menjadi penduga terbaik untuk MOR-nya, akan tetapi dapat menjadi penduga terbaik untuk keteguhan tekan sejajar serat. Sedangkan MOE dapat menjadi penduga terbaik untuk MOR. Kayu pinus tingkat umur 17 tergolong kelas kuat rv, sedangkan umur 21, 23, 27 dan 28 tahun tergolong kelas kuat III. Menurut sifatnya, maka pinus umur 17 tahun sesuai untuk konstruksi ringan, sedangkan kayu umur 21, 23, 27 dan 28 tahun dapat digunakan untuk kayu bangunan. Daur teknis kayu pinus yang ditentukan berdasarkan sifat fisis dan mekanisnya adalah antara umur 23-26 tahun