Hydrodesulfurization of 4,6-dimethyldibenzothiophene and the diesel oil fraction on NiMo catalysts supported over proton-exchanged AlMCM-41 and TiMCM-41 extrudates

NiMo catalysts supported on mesoporous MCM-41 type materials shaped with binder were tested for activity in the hydrodesulfurization of 4,6-dimethyldibenzothiophene (4,6-DMDBT) and the diesel fuel fraction (0.92 wt% of sulfur). The aim of the investigation was to evaluate the effect of ion exchange with protons of Al- or Ti-substituted MCM-41 mesoporous supports. The subjected catalytic systems were NiMo/HAlMCM-41 and NiMo/HTiMCM-41, and for comparison purposes NiMo/AlMCM-41 and NiMo/TiMCM-41. The samples were characterized by N2 sorption (at 77 K), XRD, TEM, XPS, SEM and Py–IR. It was found that the functionalization of AlMCM-41 and TiMCM-41 with protons increased the conversion of 4,6-DMDBT and the pseudo-first-order rate constant. Correspondingly, 4,6-DMDBT HDS reactions over the NiMo/HTiMCM-41 catalyst proceeded to a similar extent via hydrogenation and direct desulfurization, whereas over the NiMo/HAlMCM-41 they proceeded mainly via direct desulfurization. Furthermore, the ion-exchanged catalysts displayed two-fold higher efficiency in direct desulfurization than their non-modified counterparts. The NiMo/HTiMCM-41 catalyst exhibited the highest catalytic efficiency in the HDS of 4,6-DMDBT and the diesel oil fraction. The high activity of the NiMo/HTiMCM-41 catalyst is mainly attributed to its appropriate acidity, as well as the metal–support interaction providing both the high dispersion of the active phase and the desirable multilayered stacking morphology of the active phase slabs

Effect of Missing-Linker Defects and Ion Exchange on Stability and Proton Conduction of a Sulfonated Layered Zr-MOF

The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.3c03873.Intentionally introduced defects into solid materials create opportunities to control and tune their diverse physicochemical properties. Despite the growing interest in defect-engineered metal-organic frameworks (MOFs), there are still only a handful of studies on defective proton-conducting MOFs, including no reports on two-dimensional ones. Ion-conducting materials are fundamentally of great importance to the development of energy storage and conversion devices, including fuel cells and batteries. In this work, we demonstrate the introduction of missing-linker defects into a sulfonated proton conductive 2D zirconium-based MOF (JUK-14), using a facile post-synthetic approach and compare the stability and performance of the resulting materials, including proton conductivity, as well as adsorption of N2, CO2, and H2O molecules. We also discuss the associated presence of interlayer counterions and their effect on the properties and stability. Our approach to defect engineering can be extended to other layered MOFs and used for tuning their activity.Narodowe Centrum Nauki 2019/35/B/ST5/01067 NC

Hydrothermal stability and catalytic performance of desilicated highly siliceous zeolites ZSM-5

Highly siliceous zeolites, namely MFI type have attracted the great attention due to their higher hydrothermal stability, higher selectivity to organic compounds, and often better catalytic properties in comparison with Al-rich zeolites. The native zeolite (Si/Al = 164) and its desilicated analogues were deeply characterized with regard to their structural and textural properties by X-ray diffraction, low temperature adsorption of nitrogen and solid-state Al-27 MAS NMR. Their acidic properties were evaluated in quantitative IR studies. Finally, the catalytic performance of desilicated zeolites ZSM-5 was evaluated in the cracking of n-decane, 1,3,5-tri-iso-propylbenzene and vacuum gas oil. In this article, it is shown that high silica zeolites prepared by NaOH and NaOH&TBAOH leaching presented good hydrothermal stability with only slightly lower resistance when comparing to native steamed zeolite. The mesoporosity was preserved after the steaming treatment. The influence of the generated mesoporosity on the higher activity was evidenced in both 1,3,5-tri-isopropylbenzene and diesel oil cracking of steamed hierarchical zeolites. In spite of their lowered acidity, the mesopores system benefited the diffusion of the bulky molecule and finally provided higher activity of hierarchical zeolites. (C) 2016 Elsevier Inc. All rights reserved.This work was financed by Grant No. 2015/18/E/ST4/00191 from the National Science Centre - Poland. F. Rey and J. Martinez-Triguero thank for the support of the Spanish Government-MINECO through "Severo Ochoa" (SEV 2012-0267), MAT2015-71842-P and CTQ2015-68951-C3-1-R.Tarach, KA.; Martínez-Triguero, J.; Rey Garcia, F.; Góra-Marek, K. (2016). Hydrothermal stability and catalytic performance of desilicated highly siliceous zeolites ZSM-5. Journal of Catalysis. 339:256-259. https://doi.org/10.1016/j.jcat.2016.04.023S25625933