Size-Tailored Physicochemical Properties of Monodisperse Polystyrene Nanoparticles and the Nanocomposites Made Thereof

The latex monodisperse polystyrene (PS) colloids are important for different advanced applications (e.g. in coating, biotechnology etc.). However, the size dependency of their structural properties that impacts the characteristics of the nanocomposites composed thereof is largely unknown. Here, monodisperse PS nanoparticles (MPNPs) are synthesized via emulsion polymerization in five sizes (50, 150, 300, 350, and 450 nm). The size of the PS MPNPs is tailored by controlling the reaction time, temperature, and amount of surfactant and initiator. The correlation between the particle size and structural properties of the PS MPNPs is established by different thermomechanical and optical characterizations. The smaller particles (50 and 150 nm) show a lower glass transition (Tg) and thermal decomposition temperature and a lower Raman peak intensity. Yet, they trigger a higher IR absorption, thanks to a larger surface area. When incorporated in a polyvinyl alcohol (PVA) matrix, the smaller particles impart the resulting nanocomposite a higher tensile strength, and elastic and storage moduli. Whereas, they decline the elongation and loss factor. The very few examples of the MPNPs incorporated polymeric nanocomposites have been unstudied from this perspective. Thus, these tangible knowledge can profit scalable production of this kind of nanocomposite materials for different applications in a cost/energy efficient manner.Peer reviewe

Low molecular weight poly(lactic acid) microparticles for controlled release of the herbicide metazachlor: Preparation, morphology, and release kinetics

The preemergence chloroacetamide herbicide metazachlor was encapsulated in biodegradable low molecular weight poly(lactic acid) micro- and submicroparticles, and its release to the water environment was investigated. Three series of particles, S, M, and L, varying in their size (from 0.6 to 8 μm) and with various initial amounts of the active agent (5%, 10%, 20%, 30% w/w) were prepared by the oil-in-water solvent evaporation technique with gelatin as biodegradable surfactant. The encapsulation efficiencies reached were about 60% and appeared to be lower for smaller particles. Generally, it was found that the rate of herbicide release decreased with increasing size of particles. After 30 days the portions of the herbicide released for its highest loading (30% w/w) were 92%, 56%, and 34% for about 0.6, 0.8, and 8 μm particles, respectively. The release rates were also lower for lower herbicide loadings. Metazachlor release from larger particles tended to be a diffusion-controlled process, while for smaller particles the kinetics was strongly influenced by an initial burst release. © 2012 American Chemical Society