Excitation power and temperature dependence of excitons in CuInSe2

Excitonic recombination processes in high quality CuInSe2 single crystals have been studied by photoluminescence (PL) and reflectance spectroscopy as a function of excitation powers and temperature. Excitation power dependent measurements confirm the identification of well-resolved A and B free excitons in the PL spectra and analysis of the temperature quenching of these lines provides values for activation energies. These are found to vary from sample to sample, with values of 12.5 and 18.4meV for the A and B excitons, respectively, in the one showing the highest quality spectra. Analysis of the temperature and power dependent PL spectra from the bound excitonic lines, labelled M1, M2, and M3 appearing in multiplets points to a likely assignment of the hole involved in each case. The M1 excitons appear to involve a conduction band electron and a hole from the B valence band hole. In contrast, an A valence band hole appears to be involved for the M2 and M3 excitons. In addition, the M1 exciton multiplet seems to be due to the radiative recombination of excitons bound to shallow hydrogenic defects, whereas the excitons involved in M2 and M3 are bound to more complex defects. In contrast to the M1 exciton multiplet, the excitonic lines of M2 and M3 saturate at high excitation powers suggesting that the concentration of the defects involved is low. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4709448

Diamagnetic shift of the A free exciton in CuGaSe2 single crystals

Single crystals of CuGaSe2 were studied using magnetophotoluminescence inmagnetic fields up to 20 T at 4.2 K. The rate of the diamagnetic shift in the A free exciton peak was determined to be 9.82 x 10(-6) eV/T-2. This rate was used to calculate the reduced mass as 0.115m(0), the binding energy as 12.9 meV, the Bohr radius as 5.1 nm and an effective hole mass of 0.64m(0) (m(0) is the free electron mass) of the free A exciton using a low-field perturbation approach and the hydrogenic model

Excited states of the free excitons in CuInSe2 single crystals

High-quality CuInSe2 single crystals were studied using polarization resolved photoluminescence (PL) and magnetophotoluminescence (MPL). The emission lines related to the first (n=2) excited states for the A and B free excitons were observed in the PL and MPL spectra at 1.0481 meV and 1.0516 meV, respectively. The spectral positions of these lines were used to estimate accurate values for the A and B exciton binding energies (8.5 meV and 8.4 meV, respectively), Bohr radii (7.5 nm), band gaps (E-g(A)=1.050 eV and E-g(B)=1.054 eV), and the static dielectric constant (11.3) assuming the hydrogenic model

Inference of the Russian drug community from one of the largest social networks in the Russian Federation

The criminal nature of narcotics complicates the direct assessment of a drug community, while having a good understanding of the type of people drawn or currently using drugs is vital for finding effective intervening strategies. Especially for the Russian Federation this is of immediate concern given the dramatic increase it has seen in drug abuse since the fall of the Soviet Union in the early nineties. Using unique data from the Russian social network 'LiveJournal' with over 39 million registered users worldwide, we were able for the first time to identify the on-line drug community by context sensitive text mining of the users' blogs using a dictionary of known drug-related official and 'slang' terminology. By comparing the interests of the users that most actively spread information on narcotics over the network with the interests of the individuals outside the on-line drug community, we found that the 'average' drug user in the Russian Federation is generally mostly interested in topics such as Russian rock, non-traditional medicine, UFOs, Buddhism, yoga and the occult. We identify three distinct scale-free sub-networks of users which can be uniquely classified as being either 'infectious', 'susceptible' or 'immune'.Comment: 12 pages, 11 figure

Characterization of carbon contamination under ion and hot atom bombardment in a tin-plasma extreme ultraviolet light source

Molecular contamination of a grazing incidence collector for extreme ultraviolet (EUV) lithography was experimentally studied. A carbon film was found to have grown under irradiation from a pulsed tin plasma discharge. Our studies show that the film is chemically inert and has characteristics that are typical for a hydrogenated amorphous carbon film. It was experimentally observed that the film consists of carbon (~70 at. %), oxygen (~20 at. %) and hydrogen (bound to oxygen and carbon), along with a few at. % of tin. Most of the oxygen and hydrogen are most likely present as OH groups, chemically bound to carbon, indicating an important role for adsorbed water during the film formation process. It was observed that the film is predominantly sp3 hybridized carbon, as is typical for diamond-like carbon. The Raman spectra of the film, under 514 and 264 nm excitation, are typical for hydrogenated diamond-like carbon. Additionally, the lower etch rate and higher energy threshold in chemical ion sputtering in H2 plasma, compared to magnetron-sputtered carbon films, suggests that the film exhibits diamond-like carbon properties.Comment: 18 pages, 10 figure

Statistics of a noise-driven Manakov soliton

We investigate the statistics of a vector Manakov soliton in the presence of additive Gaussian white noise. The adiabatic perturbation theory for Manakov soliton yields a stochastic Langevin system which we analyze via the corresponding Fokker-Planck equation for the probability density function (PDF) for the soliton parameters. We obtain marginal PDFs for the soliton frequency and amplitude as well as soliton amplitude and polarization angle. We also derive formulae for the variances of all soliton parameters and analyze their dependence on the initial values of polarization angle and phase.Comment: Submitted to J.Phys.A: Mathematical and Genera

College of Arts and Sciences at Governors State University Announces Winter 2008 Dean’s List

The College of Arts and Sciences at Governors State University recently recognized undergraduate students who earned a 3.7 grade point average or higher during the Winter 2008 trimester

A photoluminescence study of CuInSe2 single crystals ion implanted with 5 keV hydrogen

CuInSe2 single crystals ion implanted with 5 keV hydrogen at doses from 3 × 1014 to 1016 cm-2 are studied by photoluminescence (PL). The PL spectra before and after implantation reveal two bands, a main dominant band centred at 0.96 eV and a lower intensity band centred at 0.93 eV. Detailed analysis of the shape of these bands, their temperature and excitation intensity dependencies allow the recombination mechanisms to be identified as band-to-tail (BT) and band-to-impurity (BI), respectively. The implantation causes gradual red shifts of the bands increasing linearly with the dose. The average depth of potential fluctuations is also estimated to increase with the dose and saturates for doses above 1015 cm-2. A model is proposed which associates the potential fluctuations with the antisite defects copper on indium site and indium on copper site. The saturation is explained by full randomization of copper and indium atoms on the cation sub-lattice

Ion channeling in CuInSe2 single crystals

CuInSe2 single crystals are studied by the Rutherford Backscattering of 2 MeV helium ions involving axial channeling along the 〈2 2 1〉 direction of the chalcopyrite lattice. Experimental values of the critical angle and normalized minimum yield are measured and compared with theory. The concentration of point defects separately in the Cu, In, and Se sublattices, determined from the comparison of experimental and theoretical minimum yields, are estimated as 4.7 × 1020, 1.0 × 1020, and 5.7 × 1020 cm-3, respectively. © 2013 Elsevier B.V. All rights reserved

Use of L-arginine immobilised on activated carbon for pharmacological correction of endothelial disfunction

For the first time a complex of L-arginine sodium salt of sulfate of cellulose acetate on activated carbon. To investigate the processes of sorption-desorption of L-arginine in a model environmen