The causes of holes and loss of physical integrity in long‐lasting insecticidal nets

Background: Long-lasting insecticidal nets (LLINs) are expected to last for at least 3 years, but whilst this may be achieved from an insecticidal perspective, physical protection is frequently compromised much earlier because of the rapid accumulation of holes during use. To understand why LLINs are so susceptible to loss of physical integrity, thousands of hole damage sites in LLINs retrieved from the feld in Africa and Asia were forensically studied to identify the persistent underlying causes. Methods: A total of 525 LLINs consisting of six diferent brands from fve diferent countries across Africa and Asia were collected from the feld after 1 to 3 years in use. More than 42,000 individual sites of hole damage were analysed based on the morphology and size of each individual hole, aided by optical microscopy (OM) and scanning electron microscopy (SEM). The fracture morphology enabled positive identifcation of the underlying mechanisms of the damage. Results: Across all LLINs and geographical settings, mechanical damage is the primary cause of holes and loss of physical integrity in LLINs (63.14% by frequency and 81.52% by area). Snagging is the single most frequent mechanical damage mechanism, whilst the largest sized holes in LLINs result from seam failure and tearing. Abrasion and hole enlargement are also responsible for a progressive loss in the physical integrity of nets. Collectively, these fve modes of mechanical damage can be expected to result from normal use of LLINs by households. Evidence of deliberate cutting, burn holes and rodent damage was observed to a lesser degree, which LLINs are not designed to withstand. Conclusions: Loss of physical integrity in LLINs is an inevitable consequence of using a vector control product that has an inherently low resistance to mechanical damage during normal use. To improve performance, new specifcations based on laboratory textile testing is needed, to assess the resistance of LLIN products to the primary causes of mechanical damage when in use, which are snagging, tearing, abrasion and hole enlargement. Seam construction also needs to meet a revised minimum standard to reduce the risk of a rapid loss of physical integrity during use

Development of a single resistance to damage metric for mosquito nets related to physical integrity in the field

Background In common with the majority of personal protective equipment and healthcare products, the ability for long-lasting insecticidal nets (LLINs) to remain in good physical condition during use is a key factor governing fitness for purpose and serviceability. The inherent ability of a product to resist physical deterioration should be known in advance of it being used to ensure it has maximum value to both the end-user and procurer. The objective of this study was to develop a single performance metric of resistance to damage (RD) that can be applied to any LLIN product prior to distribution. Methods Algorithms to calculate RD values were developed based on consideration of both human factors and laboratory testing data. Quantitative reference forces applied to LLINs by users during normal use were determined so that aspirational performance levels could be established. The ability of LLINs to resist mechanical damage was assessed based on a new suite of textile tests, reflecting actual mechanisms of physical deterioration during normal household use. These tests quantified the snag strength, bursting strength, abrasion resistance and resistance to hole enlargement. Sixteen different unused LLINs were included in the analysis. The calculated RD values for all LLINs and the corresponding physical integrity data for the same nets retrieved from the field (up to 3 years of use) were then compared. Results On a RD scale of 0 (lowest resistance) – 100 (highest resistance), only six of the sixteen LLINs achieved an RD value above 50. No current LLIN achieved the aspirational level of resistance to damage (RD = 100), suggesting that product innovation is urgently required to increase the RD of LLINs. LLINs with higher RD values were associated with lower hole damage (PHI) in the field when adjusted for normal use conditions. Conclusions The RD value of any LLIN product can be determined prior to distribution based on the developed algorithms and laboratory textile testing data. Generally, LLINs need to achieve higher RD values to improve their ability to resist hole formation during normal use. Innovation in LLIN product design focused on the textile material should be actively encouraged and is urgently needed to close the performance gap

Textile testing to assess the resistance to damage of long-lasting insecticidal nets for malaria control and prevention

Background LLINs are susceptible to forming holes within a short time in use, compromising their ability to provide long-term physical protection against insect-borne vectors of disease. Mechanical damage is known to be responsible for the majority of holes, with most being the result of snagging, tearing, hole enlargement, abrasion and seam failure, which can readily occur during normal household use. To enable an assessment of the ability of LLINs to resist such damage prior to distribution, a new suite of testing methods was developed to reflect the main damage mechanisms encountered during normal use of LLINs. Methods Four existing BS EN and ISO standards used by the textile industry were adapted to determine the ability of LLINs to resist the most common mechanisms of real-world damage experienced in the field. The new suite comprised tests for snag strength (BS 15,598:2008), bursting strength (ISO 13938-2:1999), hole enlargement resistance (BS 3423–38:1998), abrasion resistance (ISO 12947-1:1998) and new guidance around the seam construction of LLINs. Fourteen different LLINs were tested using the new suite of tests to evaluate their resistance to damage. Results The resistance to mechanical damage of LLINs is not the same, even when the bursting strength values are comparable. Differences in performance between LLINs are directly related to the fabric design specifications, including the knitted structure and constituent yarns. The differences in performance do not primarily relate to what polymer type the LLIN is made from. LLINs made with a Marquisette knitted structure produced the highest snag strength and lowest hole enlargement values. By contrast, LLINs made with a traverse knitted structure exhibited low snag strength values when compared at the same mesh count. Conclusions Prequalification of LLINs should consider not only insecticidal performance, but also inherent resistance to mechanical damage. This is critical to ensuring LLINs are fit for purpose prior to distribution, and are capable of remaining in good physical condition for longer. The new suite of test methods enables the performance of LLINs to be assessed and specified in advance of distribution and can be used to establish minimum performance standards. Implementation of these testing methods is therefore recommended

Correlation of textile ‘resistance to damage’ scores with actual physical survival of long-lasting insecticidal nets in the field

Background Attempts have been made to link procurement of long-lasting insecticidal nets (LLIN) not only to the price but also the expected performance of the product. However, to date it has not been possible to identify a specific textile characteristic that predicts physical durability in the field. The recently developed resistance to damage (RD) score could provide such a metric. This study uses pooled data from durability monitoring to explore the usefulness of the RD methodology. Methods Data from standardized, 3-year, prospective LLIN durability monitoring for six LLIN brands in 10 locations and four countries involving 4672 campaign LLIN were linked to the RD scores of the respective LLIN brands. The RD score is a single quantitative metric based on a suite of standardized textile tests which in turn build on the mechanisms of damage to a mosquito net. Potential RD values range from 0 to 100 where 100 represents optimal resistance to expected day-to-day stress during reasonable net use. Survival analysis was set so that risk of failure only started when nets were first hung. Cox regression was applied to explore RD effects on physical survival adjusting for known net use environment variables. Results In a bivariate analysis RD scores showed a linear relationship with physical integrity suggesting that the proportion of LLIN with moderate damage decreased by 3%-points for each 10-point increase of the RD score (p = 0.02, R2 = 0.65). Full adjustment for net care and handling behaviours as well as other relevant determinants and the country of study showed that increasing RD score by 10 points resulted in a 36% reduction of risk of failure to survive in serviceable condition (p < 0.0001). LLINs with RD scores above 50 had an additional useful life of 7 months. Conclusions This study provides proof of principle that the RD metric can predict physical durability of LLIN products in the field and could be used to assess new products and guide manufacturers in creating improved products. However, additional validation from other field data, particularly for next generation LLIN, will be required before the RD score can be included in procurement decisions for LLINs

The oxidation of cyst(e)ine by mast-cell tumour P815 in culture

1. Mast-cell tumour P815 cells oxidize [(35)S]cyst(e)ine to (35)SO(4)(2−). 2. Addition of cysteinesulphinate or sulphite decreases the formation of (35)SO(4)(2−); at the same time [(35)S]cysteinesulphinate or (35)SO(3)(2−) accumulates. 3. Extracts of P815 cells form sulphite from cysteinesulphinate and 2-oxoglutarate. The K(m) for cysteinesulphinate is 6·35mm and that for 2-oxoglutarate is 0·165mm. 4. Extracts oxidize sulphite to sulphate. 5. No formation of hydrogen sulphide from cyst(e)ine was detectable. 6. It is concluded that P815 cells oxidize cyst(e)ine to sulphate solely via cysteinesulphinate and sulphite. 7. The concentration of the enzymes catalysing this sequence is unaltered by several variations in the conditions of growth

Physical durability: are bed nets getting any stronger?

Background For at least a decade, concerns have been raised about the physical durability of insecticide-treated nets (ITNs) and their ability to remain in good condition for at least three years. To discover if the resistance to damage (RD) of ITNs has improved or not, the RD scores of ITNs sampled in 2013 and 2020 were compared. Methods The RD scores and disaggregated textile performance data for nine ITNs recommended by the WHO pesticide evaluation scheme (WHOPES) measured in 2013 were compared with WHO-prequalified ITNs sampled in 2020. This included assessment of newer ITNs not available in 2013, to determine the extent to which product development has led to performance improvements across all available ITNs in the intervening years. Results The resistance to damage of ITNs has not generally improved from 2013 to 2020, and in some cases performance is worse. The average RD score of comparable ITNs brands decreased from 40 in 2013 to 36 in 2020. Of the nets available in 2020, only two of the twenty-four ITN products tested achieved an RD score of > 50, while six ITNs had very low RD scores of < 30, highlighting a serious inherent, and literal weakness in many WHO-prequalified ITNs. Conclusions The long-term physical durability of ITN products cannot be expected to improve while their resistance to damage remains so low, and major upgrades to the performance standards of textile materials used to make ITNs, as well as incentives to develop stronger ones are urgently required