19 research outputs found
The effect of internal stresses on solar cell efficiency
Diffusion induced stresses in silicon are shown to result in large localized changes in the minority carrier mobility which in turn have a significant effect on cell output. Evidence is given that both compressive and tensile stresses can be generated in either the emitter or the base region. Tensile stresses appear to be much more effective in altering cell performance. While most stress related effects appear to degrade cell efficiency, this is not always the case. Evidence is presented showing that arsenic induced stresses can result in emitter characteristics comparable to those found in the MINP cell without requiring a high degree of surface passivation
The achievement of low contact resistance to indium phosphide: The roles of Ni, Au, Ge, and combinations thereof
We have investigated the electrical and metallurgical behavior of Ni, Au-Ni, and Au-Ge-Ni contacts on n-InP. We have found that very low values of contact resistivity rho(sub c) in the E-7 omega-sq cm range are obtained with Ni-only contacts. We show that the addition of Au to Ni contact metallization effects an additional order of magnitude reduction in rho(sub c). Ultra-low contact resistivities in the E-8 omega-sq cm range are obtained with both the Au-Ni and the Au-Ge-Ni systems, effectively eliminating the need for the presence of Ge in the Au-Ge-Ni system. The formation of various nickel phosphides at the metal-InP interface is shown to be responsible for the observed rho(sub c) values in the Ni and Au-Ni systems. We show, finally, that the order in which the constituents of Au-Ni and Au-Ge-Ni contacts are deposited has a significant bearing on the composition of the reaction products formed at the metal-InP interface and therefore on the contact resistivity at that interface
A very low resistance, non-sintered contact system for use on indium phosphide concentrator/shallow junction solar cells
An investigation is made into the possibility of providing low resistance contacts to shallow junction InP solar cells which do not require sintering and which do not cause device degradation even when subjected to extended annealing at elevated temperatures. We show that the addition of In to Au contacts in amounts that exceed the solid solubility limit lowers the as-fabricated (unsintered) contact resistivity (R sub c) to the 10(exp -5) ohm cm(exp 2) range. We next consider the contact system Au/Au2P3, which has been shown to exhibit as-fabricated R sub c values in the 10(exp -6) ohm cm(exp 2) range, but which fails quickly when heated. We show that the substitution of a refractory metal (W, Ta) for Au preserves the low R sub c values while preventing the destructive reactions that would normally take place in this system at high temperatures. We show, finally, that R sub c values in the 10(exp -7) ohm cm(exp 2) range can be achieved without sintering by combining the effects of In or Ga additions to Au contacts with the effects of introducing a thin Au2P3 layer at the metal-InP interface
Lateral spreading of Au contacts on InP
The contact spreading phenomenon observed when small area Au contacts on InP are annealed at temperatures above about 400 C was investigated. It was found that the rapid lateral expansion of the contact metallization which consumes large quantities of InP during growth is closely related to the third stage in the series of solid state reactions that occur between InP and Au, i.e., to the Au3In-to-Au9In4 transition. Detailed descriptions are presented of both the spreading process and the Au3In-to-Au9In4 transition along with arguments that the two processes are manifestations of the same basic phenomenon
Semiconductor structural damage attendant to contact formation in III-V solar cells
In order to keep the resistive losses in solar cells to a minimum, it is often necessary for the ohmic contacts to be heat treated to lower the metal-semiconductor contact resistivity to acceptable values. Sintering of the contacts, however can result in extensive mechanical damage of the semiconductor surface under the metallization. An investigation of the detailed mechanisms involved in the process of contact formation during heat treatment may control the structural damage incurred by the semiconductor surface to acceptable levels, while achieving the desired values of contact resistivity for the ohmic contacts. The reaction kinetics of sintered gold contacts to InP were determined. It was found that the Au-InP interaction involves three consecutive stages marked by distinct color changes observed on the surface of the Au, and that each stage is governed by a different mechanism. A detailed description of these mechanisms and options to control them are presented
An x ray photoelectron spectroscopy study of Au(x)In(y) alloys
Four gold-indium alloys were studied by x ray photoelectron spectroscopy. The binding energies and intensity ratios of the Au 4f7/2 and In 3d5/2 core levels were determined for the bulk alloy compositions of Au(10 percent In), Au3In, AuIn, and AuIn2. These values were determined for the native oxides on the materials, for the surfaces prepared by ion bombardment to remove the oxide and for surfaces scraped in-situ with a ceramic tool to expose the bulk composition. These results furnish calibration values that allow determination of the composition of thin films of this alloy system. In addition the binding energies add to the data base for understanding the effect of alloying on core level binding energies. As an illustration, these results are used to determine the composition of a series of alloy films formed by incongruent evaporation of an alloy charge
Low resistance contacts for shallow junction semiconductors
A method of enhancing the specific contact resistivity in InP semiconductor devices and improved devices produced thereby are disclosed. Low resistivity values are obtained by using gold ohmic contacts that contain small amounts of gallium or indium and by depositing a thin gold phosphide interlayer between the surface of the InP device and the ohmic contact. When both the thin interlayer and the gold-gallium or gold-indium contact metallizations are used, ultra low specific contact resistivities are achieved. Thermal stability with good contact resistivity is achieved by depositing a layer of refractory metal over the gold phosphide interlayer
The Influence of Interstitial Ga and Interfacial Au (sub 2)P (sub 3) on the Electrical and Metallurgical Behavior of Au-Contacted III-V Semiconductors
The introduction of a very small amount of Ga into Au contact metallization on InP is shown to have a significant effect on both the metallurgical and electrical behavior of that contact system. Ga atoms in the interstices of the Au lattice are shown to be effective in preventing the solid state reactions that normally take place between Au and InP during contact sintering. In addition to suppressing the metallurgical interaction, the presence of small amounts of Ga is shown to cause an order of magnitude reduction in the specific contact resistivity. Evidence is presented that the reactions of GaP and GaAs with Au contacts are also drastically affected by the presence of Ga. The sintering behavior of the Au-GaP and the Au-GaAs systems (as contrasted with that of the Au-InP system) is explained as due to the presence of interstitial Ga in the contact metallization. Finally the large, two-to-three order of magnitude drop in the contact resistance that occurs in the Au-InP system upon sintering at 400 degrees Centigrade is shown to be a result of the formation of an Au (sub 2) P (sub 3) layer at the metal-semiconductor interface. Contact resistivities in the 10 (sup -6) ohm square centimeter range are obtained for as-deposited Au on InP when a thin (20 Angstrom) layer of Au (sub 2) P (sub 3) is introduced between the InP and the Au contacts
Effects of solar cell environment on contact integrity
The III-V semiconductors react extremely rapidly with most commonly used contact metallizations. This precludes the use of elevated temperatures in the contact formation process for solar cells and other shallow junction devices. These devices must rely upon contact metallizations that are sufficiently conductive in their 'as-fabricated' state. However, while there are a number of non-sintered metallizations that have acceptable characteristics, the lack of a sintering step makes them vulnerable to a variety of environmentally induced degradation processes. The degrading effects resulting from the exposure of unsintered devices to a humid environment and to a vacuum (space) environment are described. It is shown, further, that these effects are magnified by the presence of mechanical damage in the contact metallization. The means to avoid or prevent these degrading interactions are presented
Au/Zn Contacts to rho-InP: Electrical and Metallurgical Characteristics and the Relationship Between Them
The metallurgical and electrical behavior of Au/Zn contacting metallization on p-type InP was investigated as a function of the Zn content in the metallization. It was found that ohmic behavior can be achieved with Zn concentrations as small as 0.05 atomic percent Zn. For Zn concentrations between 0.1 and 36 at. percent, the contact resistivity rho(sub c) was found to be independent of the Zn content. For low Zn concentrations the realization of ohmic behavior was found to require the growth of the compound Au2P3 at the metal-InP interface. The magnitude of rho(sub c) is shown to be very sensitive to the growth rate of the interfacial Au2P3 layer. The possibility of exploiting this sensitivity to provide low resistance contacts while avoiding the semiconductor structural damage that is normally attendant to contact formation is discussed