Thermal annealing and transformation of dimer F centers in neutron-irradiated Al2O3 single crystals

This work has been carried out within the framework of the EUROfusion Consortium and has received funding from the Euratom research and training programme 2014-2018 and 2019-2020 under grant agreement No 633053. The views and opinions expressed herein do not necessarily reflect those of the European Commission. In addition, the research leading to these results has received funding from the Estonian Research Council grant (PUT PRG619).The precise study of the thermal annealing of the F2-type dimer defects, being under discussion in the literature for a long time and responsible for the number of absorption bands below 4.5 eV, has been performed in corundum single crystals irradiated by fast neutrons with a fluence of 6.9 × 1018 n/cm2. The Gaussian components of the radiation-induced optical absorption with the maxima at 4.08, 3.45 and 2.75 eV have been considered as a measure of the F2, F2+and F22+centers, respectively. In contrast to the Fand F+ centers, the concentration of which continuously decreases at the sample heating up to 1100 K, the concentration of dimer defects with different charge states passes the increasing stages above 500 K starting from the F22+centers. The tentative mechanisms of such rise of the F22+centers as well as of the subsequent transformation/rise of dimer centers, F22+→F2+→F2at 650-800 K are considered. The possible sources of carriers needed for the recharging of dimer centers are also analysed on the basis of thermally stimulated luminescence measurements up to ~850 K.EUROfusion Consortium, Euratom research and training programme 2014-2018 and 2019-2020, grant agreement No 633053; Estonian Research Council grant (PUT PRG619); Institute of Solid State Physics, University of Latvia as the Center of Excellence has received funding from the European Union’s Horizon 2020 Framework Programme H2020-WIDESPREAD-01-2016-2017-TeamingPhase2 under grant agreement No. 739508, project CAMART

Accumulation of radiation defects and modification of micromechanical properties under MgO crystal irradiation with swift 132Xe ions

This work has been carried out within the framework of the EUROfusion Consortium and has received funding from the Euratom research and training programme 2014-2018 and 2019-2020 under grant agreement No. 633053. The views and opinions expressed herein do not necessarily reflect those of the European Commission. A.A. also acknowledges support via the project GF AP05134257 of Ministry of Education and Science of the Republic of Kazakhstan .Accumulation of F-type defects under irradiation of MgO crystals by 0.23-GeV 132Xe ions with fluence varying by three orders of magnitude has been investigated via the spectra of optical absorption and low-temperature cathodoluminescence. The number of single centers continuously increases with fluence without any marks of saturation. At the highest fluence, a mean volume concentration of 3.1 × 1019 and 3.35 × 1019 cm−3 is reached for F and F+ centers, respectively. The F+ emission strongly dominates in the cathodoluminescence of irradiated MgO and its enhancement with fluence is detected. However, the creation efficiency of the F2 aggregate centers is very low and fluence dependence has a complicated shape. Radiation-induced changes of micro-mechanical properties of the same samples have been analysed; the depth profiles of hardening correlate with the ion energy loss. A joint contribution of ionization and impact mechanisms in the formation of structural defects under MgO irradiation with Xe ions is considered.H2020 Euratom 2019-2020,633053,2014-2018,GF AP05134257; Ministry of Education and Science of the Republic of Kazakhstan GF AP05134257; Institute of Solid State Physics, University of Latvia as the Center of Excellence has received funding from the European Union’s Horizon 2020 Framework Programme H2020-WIDESPREAD-01-2016-2017-TeamingPhase2 under grant agreement No. 739508, project CAMART