High-Speed Monitoring of Dust Particles in ITER ELMs Simulation Experiments with QSPA Kh-50

Dust generation under powerful plasma stream impacts has been studied in ITER ELM simulation experiments with QSPA Kh-50 plasma accelerator. Repetitive plasma exposures of tungsten have been performed by 0.25 ms plasma pulses and the heat load varied in the range (0.1÷1.1) MJm-2. Main characteristics of dust particles such as a number of ejected particles, their velocity, angular distribution and start time from the surface are investigated. Dust particles have not been observed under heat load below the cracking threshold. Quantity of dust particles rises with increasing heat load. Average velocities of dust particles are found to be strongly dependent on their start time from the surface after beginning of plasma-surface interaction. Maximal velocity achieved a few tens of meters per second

The experimental and theoretical investigations of damage development and distribution in double-forged tungsten under plasma irradiation-initiated extreme heat loads

The influence of extreme heat loads, as produced by a multiple pulses of non-homogeneous fl ow of slow plasma (0.1-1 keV) and fast ions (100 keV), on double-forged tungsten (DFW) was investigated. For generation of deuterium plasma and fast deuterons, plasma-focus devices PF-12 and PF-1000 are used. Depending on devices and conditions, the power flux density of plasma varied in a range of 107-1010 W/cm2 with pulse duration of 50-100 ns. Power flux density of fast ions was 1010-1012 W/cm2 at the pulse duration of 10-50 ns. To achieve the combined effect of different kind of plasmas, the samples were later irradiated with hydrogen plasma (105 W/cm2, 0.25 ms) by a QSPA Kh-50 plasma generator. Surface modification was analysed by scanning electron microscopy (SEM) and microroughness measurements. For estimation of damages in the bulk of material, an electrical conductivity method was used. Investigations showed that irradiation of DFW with multiple plasma pulses generated a mesh of micro- and macrocracks due to high heat load. A comparison with single forged tungsten (W) and tungsten doped with 1% lanthanum-oxide (WL10) reveals the better crack-resistance of DFW. Also, sizes of cells formed between the cracks on the DFW’s surface were larger than in cases of W or WL10. Measurements of electrical conductivity indicated a layer of decreased conductivity, which reached up to 500 μm. It depended mainly on values of power flux density of fast ions, but not on the number of pulses. Thus, it may be concluded that bulk defects (weakening bonds between grains and crystals, dislocations, point-defects) were generated due to mechanical shock wave, which was generated by the fast ions flux. Damages and erosion of materials under different combined radiation conditions have also been discussed

Plasma exposure of different tungsten grades with plasma accelerators under ITER-relevant conditions

This paper presents the results of tungsten irradiation experiments performed with three plasma facilities: the QSPA Kh-50 quasi-steady-state plasma accelerator, the PPA pulsed plasma gun and the magneto-plasma compressor. Targets made of different kinds of tungsten (sintered, rolled and deformed) were irradiated with powerful plasma streams at heat fluxes relevant to edge-localized modes in ITER. The irradiated targets were analyzed and two different meshes of cracks were identified. It has been shown that the major cracks do not depend on the tungsten grade. This has been attributed to ductile-to-brittle transition effects. Meshes of inter-granular micro-cracks were detected for energy loads above the melting threshold and these were probably caused by the re-solidification process. The blister-like and cellular-like structures were observed on sample surfaces exposed to helium and hydrogen plasmas