Microstructural and tribological comparison of HVOF-sprayed and post-treated M-Mo-Cr-Si (M = Co, Ni) alloy coatings

High velocity oxygen-fuel (HVOF)-sprayed wear resistant Co-28%Mo-17%Cr-3%Si and Ni-32%Mo-15%Cr-3%Si coatings, both as-sprayed and after heat treatments at 600 degrees C for 1 h, have been studied. Particularly, their dry sliding wear behaviour has been compared by ball-on-disk tests against different counterbodies (100Cr6 steel and sintered alumina), and differences were discussed based on microstructural characteristics and micromechanical properties (Vickers microindentation and scratch test responses). As-sprayed coatings contain oxide stringers, are mostly amorphous and display rather low Vickers microhardness (about 7.4 GPa for the Co-based and 6.2 GPa for the Ni-based), toughness and elastic modulus. Heat-treated ones display sub-micrometric crystalline intermetallics, improving hardness (9.6 GPa and 7.4 GPa, respectively) and elastic modulus. Scratch tests indicate greater brittleness of the Ni-based alloy (higher tendency to cracking). Due to low hardness and toughness, both as-sprayed coatings undergo wear loss against steel and alumina counterparts. The more plastic Co-based alloy undergoes higher adhesive wear against steel and lower abrasive wear against alumina; the situation is reversed for the Ni-based alloy. After heat treatment, the wear loss against steel is very low for both coatings; abrasive wear still occurs against alumina. (c) 2007 Elsevier B.V. All rights reserved

Advanced open-celled structures from low-temperature sintering of a crystallization-resistant bioactive glass

Most materials for bone tissue engineering are in form of highly porous open-celled components (porosity > 70%) developed by means of an adequate coupling of formulations and manufacturing technologies. This paper is dedicated to porous components from BGMS10 bioactive glass, originally designed to undergo viscous flow sintering without crystallization, which is generally known to degrade the bioactivity of 45S5 bioglass. The adopted manufacturing technologies were specifically conceived to avoid any contamination and give excellent control on the microstructures by simple operations. More precisely, 'green' components were obtained by digital light processing and direct foaming of glass powders suspended in a photosensitive organic binder or in an aqueous solution, activated with an organic base, respectively. Owing to characteristic quite large sintering window of BGMS10 glass, sintering at 750 \ub0C caused the consolidation of the structures generated at room temperature, without any evidence of viscous collapse

Recent advances on innovative bioactive glass-hydroxyapatite composites for bone tissue applications: Processing, mechanical properties, and biological performance

New Hydroxyapatite-Bioactive Glass composites, xHA-(1-x)BG (x = 25, 50, and 75 wt %), are developed using HA and BGMS10 glass powders co-milled up to 2 h prior to Spark Plasma Sintering (SPS). Ball milling (BM) promoted the consolidation of HA-rich powders, whereas hindered the densification of 25HA-75BG samples. HA crystallite size is reduced from > 200 nm (unmilled) to 60 (x = 25 %) or 88 nm (x = 75 %) when using 2 h milled mixtures. Glass crystallization occurred in 75HA-25BG samples processed by SPS at 950 °C: a negligeable effect in the amount of the residual amorphous phase (12.3–13.3 wt %) is produced by BM, while changes are observed in the relative content of crystalline phases, with SiO2 increases from 8.5 to 13.1 wt %, whereas α- and β-CaSiO3 correspondingly decrease. Superior Young's modulus and Vickers hardness (130 GPa and 726, respectively) are obtained in HA rich products. Biological tests evidenced that the milling treatment does not determine negative consequences on cells viability

A new bioactive glass/collagen hybrid composite for applications in dentistry

Bioactive glasses (BGs) are currently employed in a wide range of medical and dentistry applications by virtue of their bone-bonding ability. The incorporation of BGs into a collagen matrix may be used to combine the regenerative potential of these materials with the specific biological advantages of collagen. However, most of the collagen/BG composites reported in the literature are scaffolds and there is a lack of moldable putties or injectable systems. Here, granules of an innovative BG containing strontium and magnesium were mixed with collagen and PEG to obtain a putty (BGMS/C) suitable for dental applications. For the sake of comparison, granules of 45S5 Bioglass\uae, the gold standard among BGs, were used to prepare a 45S5/collagen putty. Both the composites were evaluated in vitro with respect to murine fibroblasts. The materials showed an excellent biocompatibility, making them interesting for possible applications in dentistry and reconstructive surgery. Moreover, BGMS/C seems to stimulate cell proliferation.Bioactive glasses (BGs) are currently employed in a wide range of medical and dentistry applications by virtue of their bone-bonding ability. The incorporation of BGs into a collagen matrix may be used to combine the regenerative potential of these materials with the specific biological advantages of collagen. However, most of the collagen/BG composites reported in the literature are scaffolds and there is a lack of moldable putties or injectable systems. Here, granules of an innovative BG containing strontium and magnesium were mixed with collagen and PEG to obtain a putty (BGMS/C) suitable for dental applications. For the sake of comparison, granules of 45S5 Bioglass\uae, the gold standard among BGs, were used to prepare a 45S5/collagen putty. Both the composites were evaluated in vitro with respect to murine fibroblasts. The materials showed an excellent biocompatibility, making them interesting for possible applications in dentistry and reconstructive surgery. Moreover, BGMS/C seems to stimulate cell proliferation

Human mesenchymal stem cell combined with a new strontium-enriched bioactive glass: An ex-vivo model for Bone Regeneration

A 3D cellular model that mimics the potential clinical application of a biomaterial is here applied for the first time to a bioactive glass, in order to assess its biological potential. A recently developed bioactive glass (BGMS10), whose composition contained strontium and magnesium, was produced in the form of granules and fully investigated in terms of biocompatibility in vitro. Apart from standard biological characterization (Simulated Body Fluid (SBF) testing and biocompatibility as per ISO10993), human bone marrow mesenchymal stromal/stem cells (BM-MSCs) were used to investigate the performance of the bioactive glass granules in an innovative 3D cellular model. The results showed that BGMS10 supported human BM-MSCs adhesion, colonization, and bone differentiation. Thus, bioactive glass granules seem to drive osteogenic differentiation and thus look particularly promising for orthopedic applications, bone tissue engineering and regenerative medicine

Short range investigation of sub-micron zirconia particles

The Perturbed Angular Correlations technique was used to determine the configurations around Zirconium ions and their thermal behavior in non-aggregated sub-micron zirconia spherical particles. Three residues containing- Zr surroundings were determined for the non-crystalline starting particles, which were identified under the assumption of a certain chemical reactions sequence during synthesis. While the one made up mainly by hydroxyl groups was common to both samples, the two involving mainly organic residues were particle size dependent. Upon crystallization, both samples stabilized in the t'- and t- tetragonal forms and the Xc-cubic form but their amounts and temperatures of appearance were different. On heating, the structure of the smaller particles became gradually monoclinic achieving total degradation upon the subsequent cooling to RT.Instituto de Física La Plat

Alginate-Sr/Mg Containing Bioactive Glass Scaffolds: The Characterization of a New 3D Composite for Bone Tissue Engineering

In bone regeneration, combining natural polymer-based scaffolds with Bioactive Glasses (BGs) is an attractive strategy to improve the mechanical properties of the structure, as well as its bioactivity and regenerative potential. Methods: For this purpose, a well-studied alginate/hydroxyapatite (Alg/HAp) porous scaffold was enhanced with an experimental bioglass (BGMS10), characterized by a high crystallization temperature and containing therapeutic ions such as strontium and magnesium. This resulted in an improved biological response compared to 45S5 Bioglass (R), the "gold" standard among BGs. Porous composite scaffolds were fabricated by freeze-drying technique and characterized by scanning electron microscopy and microanalysis, infrared spectroscopy, and microcomputed tomography. The mechanical properties and cytocompatibility of the new scaffold composition were also evaluated. The addition of bioglass to the Alg/HAp network resulted in a slightly lower porosity. However, despite the change in pore size, the MG-63 cells were able to better adhere and proliferate when cultured for one week on a BG scaffold compared to the control Alg/HAp scaffolds. Thus, our findings indicate that the combination of bioactive glass BGMS10 does not affect the structural and physicochemical properties of the Alg/HAp scaffold and confers bioactive properties to the structures, making the Alg/HAp-BGMS10 scaffold a promising candidate for future application in bone tissue regeneration

Fabrication and Characterization of Quinary High Entropy-Ultra-High Temperature Diborides” Ceramics

Due to their inherently chemical complexity and their refractory nature, the obtainment of highly dense and single-phase High Entropy (HE) diborides represents a very hard target to achieve. In this framework, homogeneous (Hf0.2Nb0.2Ta0.2Mo0.2Ti0.2)B2, (Hf0.2Zr0.2Ta0.2Mo0.2Ti0.2)B2, and (Hf0.2Zr0.2Nb0.2Mo0.2Ti0.2)B2 ceramics with high relative densities (97.4, 96.5 and 98.2 %, respectively) are successfully produced by Spark Plasma Sintering (SPS) using powders prepared by Self-propagating High-temperature Synthesis (SHS). Although the latter technique does not lead to the complete conversion of initial precursors into the prescribed HE phases, such goal is fully reached after SPS (1950°C/20min/20 MPa). The three HE products show similar, even better in some cases, mechanical properties compared to ceramics with the same nominal composition attained using alternative processing methods. Superior Vickers hardness and elastic modulus values are found for the (Hf0.2Nb0.2Ta0.2Mo0.2Ti0.2)B2 and (Hf0.2Zr0.2Ta0.2Mo0.2Ti0.2)B2 systems, i.e. 28.1 GPa/538.5 GPa and 28.08 GPa/498.1 GPa, respectively, in spite of the correspondingly higher residual po-rosities (1.2 and 2.2 vol.%, respectively). In contrast, the third ceramic, not containing Tantalum, displays lower values of these two properties (25.1 GPa/404.5 GPa). However, the corresponding fracture toughness (8.84 MPa m1/2) is relatively higher. This fact can be likely ascribed to the smaller residual porosity (0.3 vol.%) of the sintered material

Inclusion of Magnesium- and Strontium-Enriched Bioactive Glass into Electrospun PCL Scaffolds for Tissue Regeneration

Bioactive glass (BG) is a promising material known for its osteogenic, osteoinductive, antimicrobial, and angiogenic properties. For this reason, melt-quench-derived BG powders embedded into composite electrospun poly(epsilon-caprolactone) (PCL) mats represent an interesting option for the fabrication of bioactive scaffolds. However, incorporating BG into nano-/micro-fibers remains challenging. Our research focused on integrating two BG compositions into the mat structure: 45S5 and 45S5_MS (the former being a well-known, commercially available BG composition, and the latter a magnesium- and strontium-enriched composition based on 45S5). Both BG types were added at concentrations of 10 wt.% and 20 wt.%. A careful grinding process enabled effective dispersion of BG into a PCL solution, resulting in fibers ranging from 500 nm to 2 mu m in diameter. The mats' mechanical properties were not hindered by the inclusion of BG powder within the fibrous structure. Furthermore, our results indicate that BG powders were successfully incorporated into the scaffolds, not only preserving their properties but potentially enhancing their biological performance compared to unloaded PCL electrospun scaffolds. Our findings indicate proper cell differentiation and proliferation, supporting the potential of these devices for tissue regeneration applications

Short range investigation of sub-micron zirconia particles

The Perturbed Angular Correlations technique was used to determine the configurations around Zirconium ions and their thermal behavior in non-aggregated sub-micron zirconia spherical particles. Three residues containing- Zr surroundings were determined for the non-crystalline starting particles, which were identified under the assumption of a certain chemical reactions sequence during synthesis. While the one made up mainly by hydroxyl groups was common to both samples, the two involving mainly organic residues were particle size dependent. Upon crystallization, both samples stabilized in the t'- and t- tetragonal forms and the Xc-cubic form but their amounts and temperatures of appearance were different. On heating, the structure of the smaller particles became gradually monoclinic achieving total degradation upon the subsequent cooling to RT.Instituto de Física La Plat