Effects of alloying elements on defect structures in the incubation period for void swelling in austenitic stainless steels
Positron lifetime measurements were used to study the effects of alloying elements on the defect structure during the incubation period for void swelling in several fcc model alloys. Pure Ni, four model alloys (FeāCrāNi, FeāCrāNiāMoāMn, FeāCrāNiāMoāMnāSi and FeāCrāNiāMoāMnāSiāTi), and four commercial alloys (SUS316LSS, SUS316SS, SUS304SS and Ti added modified SUS316SS) were irradiated with electrons and neutrons. Even at 363 and 573 K to a dose of 0.2 dpa, an effect of alloying elements was observed. At 363 K irradiation, voids were formed only in Ni and FeāCrāNi. At 573 K irradiation, voids were formed in Ni and all model alloys, though the concentration depended on the alloying elements. In commercial alloys, precipitates were formed instead of vacancy clusters, which prevented void growth