Thermal Conductivity of High Performance Concrete in Wide Temperature and Moisture Ranges

The thermal conductivity of two types of high performance concrete was measured in the temperature range from 100 °C to 800 °C and in the moisture range from dry material to saturation water content. A transient measuring method based on analysis of the measured temperature fields was chosen for the high temperature measurements, and a commercial hot wire device was employed in room temperature measurements of the effect of moisture on thermal conductivity. The measured results reveal that both temperature and moisture exhibit significant effects on the values of thermal conductivity, and these effects are quite comparable from the point of view of the magnitude of the observed variations

Temperature and Moisture Dependence of the Specific Heat of High Performance Concrete

The specific heat of two types of high performance concrete was measured in the temperature range from 20 °C to 1000 °C and in the moisture range from dry material to saturation water content. A nonadiabatic method was chosen instead of classical adiabatic treatments in order to meet the requirements following from the large representative elementary volume of the materials. The measured results reveal a significant temperature effect on the specific heat value. The influence of moisture is less important than the influence of temperature, but is also not negligible

Thermal and Hygric Expansion of High Performance Concrete

The linear thermal expansion coefficient of two types of high performance concrete was measured in the temperature range from 20 °C to 1000 °C, and the linear hygric expansion coefficient was determined in the moisture range from dry material to saturation water content. Comparative methods were applied for measurements of both coefficients. The experimental results show that both the effect of temperature on the values of linear thermal expansion coefficients and the effect of moisture on the values of linear hygric expansion coefficients are very significant and cannot be neglected in practical applications

Alternative Policies for the Control of Air Pollution in Poland

Like other Central European countries, Poland faces the twin challenges of improving environmental quality while also promoting economic development. This study examines the cost of achieving alternative emission standards and the savings in abatement cost that might be achieved with policies that rely on economic incentives rather than with rigid " command and control " measures. The focus is primarily on three pollutants arising from energy combustion - particulate matter, nitrogen oxides, and sulfur dioxide - although carbon dioxide emissions also are tracked. A central element of the analysis is a dynamic model of least-cost energy supply in Poland that allows examination at a national level of effects of different pollution standards and policies

Changes in certain nitrogen fractions and nitrate reductase activity in crowns of three varieties of winter wheat during cold hardening and dehardening

Call number: LD2668 .T4 1963 T65Master of Scienc

Structural stability of Fe5Si3 and Ni2Si studied by high-pressure x-ray diffraction and ab initio total-energy calculations

We performed high-pressure angle dispersive x-ray diffraction measurements on Fe5Si3 and Ni2Si up to 75 GPa. Both materials were synthesized in bulk quantities via a solid-state reaction. In the pressure range covered by the experiments, no evidence of the occurrence of phase transitions was observed. On top of that, Fe5Si3 was found to compress isotropically, whereas an anisotropic compression was observed in Ni2Si. The linear incompressibility of Ni2Si along the c-axis is similar in magnitude to the linear incompressibility of diamond. This fact is related to the higher valence-electron charge density of Ni2Si along the c-axis. The observed anisotropic compression of Ni2Si is also related to the layered structure of Ni2Si where hexagonal layers of Ni2+ cations alternate with graphite-like layers formed by (NiSi)2- entities. The experimental results are supported by ab initio total-energy calculations carried out using density functional theory and the pseudopotential method. For Fe5Si3, the calculations also predicted a phase transition at 283 GPa from the hexagonal P63/mcm phase to the cubic structure adopted by Fe and Si in the garnet Fe5Si3O12. The room-temperature equations of state for Fe5Si3 and Ni2Si are also reported and a possible correlation between the bulk modulus of iron silicides and the coordination number of their minority element is discussed. Finally, we report novel descriptions of these structures, in particular of the predicted high-pressure phase of Fe5Si3 (the cation subarray in the garnet Fe5Si3O12), which can be derived from spinel Fe2SiO4 (Fe6Si3O12).Comment: 44 pages, 13 figures, 3 Table

Differential transactivation of sphingosine-1-phosphate receptors modulates NGF-induced neurite extension

The process of neurite extension after activation of the TrkA tyrosine kinase receptor by nerve growth factor (NGF) involves complex signaling pathways. Stimulation of sphingosine kinase 1 (SphK1), the enzyme that phosphorylates sphingosine to form sphingosine-1-phosphate (S1P), is part of the functional TrkA signaling repertoire. In this paper, we report that in PC12 cells and dorsal root ganglion neurons, NGF translocates SphK1 to the plasma membrane and differentially activates the S1P receptors S1P1 and S1P2 in a SphK1-dependent manner, as determined with specific inhibitors and small interfering RNA targeted to SphK1. NGF-induced neurite extension was suppressed by down-regulation of S1P1 expression with antisense RNA. Conversely, when overexpressed in PC12 cells, transactivation of S1P1 by NGF markedly enhanced neurite extension and stimulation of the small GTPase Rac, important for the cytoskeletal changes required for neurite extension. Concomitantly, differentiation down-regulated expression of S1P2 whose activation would stimulate Rho and inhibit neurite extension. Thus, differential transactivation of S1P receptors by NGF regulates antagonistic signaling pathways that modulate neurite extension

Effect of Nickel Administration in vivo on the Testicular Structure in Male Mice

The aim of this study was to describe the effects of nickel (NiCl2) on murine testicular structure. Experimental animals were injected intraperitoneally with a single dose of 20 mg NiCl2 per kg of body mass (group A, n = 5) and 40 mg NiCl2 per kg b. m. (group B, n = 5). The group without injection (n = 5) was the control (C). Animals were killed 48 hours after administration of nickel. The body mass of animals, the mass of testes and the testes : body mass ratio were not significantly affected. In both experimental groups a significant (p p p < 0.05 - 0.001) after nickel administration. Evaluation of the lumen diameter in the seminiferous tubule showed a significant increase in both experimental groups. The data of the perimeter of seminiferous tubules corresponded with those of the seminiferous tubule diameter. TUNEL assay detected a higher frequency of localized apoptosis in the interstitium of nickel-administered animals compared to control group. Our findings clearly suggest a negative effect of nickel on the structure as well as on the function of the seminferous epithelium at the site of spermatozoa production