Terahertz probing of anisotropic conductivity and morphology of CuMnAs epitaxial thin films
Antiferromagnetic CuMnAs thin films have attracted attention since the
discovery of the manipulation of their magnetic structure via electrical,
optical, and terahertz pulses of electric fields, enabling convenient
approaches to the switching between magnetoresistive states of the film for the
information storage. However, the magnetic structure and, thus, the efficiency
of the manipulation can be affected by the film morphology and growth defects.
In this study, we investigate the properties of CuMnAs thin films by probing
the defect-related uniaxial anisotropy of electric conductivity by contact-free
terahertz transmission spectroscopy. We show that the terahertz measurements
conveniently detect the conductivity anisotropy, that are consistent with
conventional DC Hall-bar measurements. Moreover, the terahertz technique allows
for considerably finer determination of anisotropy axes and it is less
sensitive to the local film degradation. Thanks to the averaging over a large
detection area, the THz probing also allows for an analysis of strongly
non-uniform thin films. Using scanning near-field terahertz and electron
microscopies, we relate the observed anisotropic conductivity of CuMnAs to the
elongation and orientation of growth defects, which influence the local
microscopic conductivity. We also demonstrate control over the morphology of
defects by using vicinal substrates.Comment: 33 pages, 16 figure
Quasi-phase-matched second harmonic generation of UV light using AlN waveguides
As an alternative to electrically injected diodes, UV light emission can be obtained via second harmonic generation (SHG). In weakly birefringent materials such as aluminum nitride (AlN), the phase matching of the driving and second harmonic waves can be achieved by the quasi-phase-matching (QPM) technique, where the polarity of the material is periodically changed commensurate with the coherence wavelength. QPM also allows the use of the highest nonlinear susceptibility, and therefore, higher conversion efficiencies are possible. In this work, the QPM SHG of UV light in AlN lateral polar structure-based waveguides is demonstrated. The peak intensity of the frequency doubled laser light was measured at 344nm and 472nm wavelengths, in agreement with dispersion-based theoretical predictions. These results confirm the potential of III-nitride-based lateral polar structures for quasi-phase-matched nonlinear optics and for frequency doubling media for UV light generation
Quasi-phase-matched second harmonic generation of UV light using AlN waveguides
As an alternative to electrically injected diodes, UV light emission can be obtained via second harmonic generation (SHG). In weakly birefringent materials such as aluminum nitride (AlN), the phase matching of the driving and second harmonic waves can be achieved by the quasi-phase-matching (QPM) technique, where the polarity of the material is periodically changed commensurate with the coherence wavelength. QPM also allows the use of the highest nonlinear susceptibility, and therefore, higher conversion efficiencies are possible. In this work, the QPM SHG of UV light in AlN lateral polar structure-based waveguides is demonstrated. The peak intensity of the frequency doubled laser light was measured at 344nm and 472nm wavelengths, in agreement with dispersion-based theoretical predictions. These results confirm the potential of III-nitride-based lateral polar structures for quasi-phase-matched nonlinear optics and for frequency doubling media for UV light generation
Second-Harmonic Generation of Blue Light in GaN Waveguides
Second-harmonic generation was studied in III-metal-polar GaN films grown on sapphire substrates by metalorganic chemical vapor deposition and formed into ridge waveguides. Broadband near-IR femtosecond pulses of an optical parametric amplifier system were injected by end-fire coupling and the nonlinear response was measured while tuning the central wavelength. A prominent peak was found at 450 nm for 1140 nm thick and 10 μm wide GaN waveguides. The measured second-harmonic peak was in agreement with the modal-dispersion phase matching condition calculated using the dispersion of the extraordinary refractive indices of GaN obtained by prism coupling
Second-harmonic generation of blue light in GaN waveguides
Second-harmonic generation was studied in III-metal-polar GaN films grown on sapphire substrates by metalorganic chemical vapor deposition and formed into ridge waveguides. Broadband near-IR femtosecond pulses of an optical parametric amplifier system were injected by end-fire coupling and the nonlinear response was measured while tuning the central wavelength. A prominent peak was found at 450 nm for 1140 nm thick and 10 µm wide GaN waveguides. The measured second-harmonic peak was in agreement with the modal-dispersion phase matching condition calculated using the dispersion of the extraordinary refractive indices of GaN obtained by prism coupling