The influence of toothbrushing and coffee staining on different composite surface coatings

The aim of our study is to evaluate the performance of surface sealants and conventional polishing after ageing procedures. Eighty circular composite restorations were performed on extracted human molars. After standardised roughening, the restorations were either sealed with one of three surface sealants (Lasting Touch (LT), BisCover LV (BC), G-Coat Plus (GP) or a dentin adhesive Heliobond (HB)) or were manually polished with silicon polishers (MP) (n = 16). The average roughness (Ra) and colourimetric parameters (CP) (L*a*b*) were evaluated. The specimens underwent an artificial ageing process by thermocycling, staining (coffee) and abrasive (toothbrushing) procedures. After each ageing step, Ra and CP measurements were repeated. A qualitative surface analysis was performed with SEM. The differences between the test groups regarding Ra and CP values were analysed with nonparametric ANOVA analysis (α = 0.05). The lowest Ra values were achieved with HB. BC and GP resulted in Ra values below 0.2μm (clinically relevant threshold), whereas LT and MP sometimes led to higher Ra values. LT showed a significantly higher discolouration after the first coffee staining, but this was normalised to the other groups after toothbrushing. The differences between the measurements and test groups for Ra and CP were statistically significant. However, the final colour difference showed no statistical difference among the five groups. SEM evaluation showed clear alterations after ageing in all coating groups. Surface sealants and dentin adhesives have the potential to reduce surface roughness but tend to debond over time. Surface sealants can only be recommended for polishing provisional restoration

Micromorphology and adhesive performance of Er:YAG laser-treated dentin of primary teeth

This study evaluated (1) the micromorphology by scanning electron microscopy (SEM) and (2) the adhesive performance by microtensile bond strength (μTBS) of diamond bur-treated dentin compared to Er:YAG laser-treated dentin of human primary teeth. (1) For qualitative SEM evaluation, dentin of 18second primary molars (n = 3/method) was treated with either diamond bur as a control (group 1a: 40μm diamond bur only (clinical situation); group 1b: grinding + 40μm diamond bur) or with Er:YAG laser (group 2a (clinical situation, manufacturer's settings): 200mJ/25Hz (5W) + 100mJ/35Hz (3.5W) laser only; group 2b (experimental setting "high"): grinding + 400mJ/20Hz (8W); group 2c (manufacturer's setting "finishing"): grinding + 100mJ/35Hz (3.5W); group 2d (experimental setting "low"): grinding + 50mJ/35Hz (1.75W)). (2) For evaluation of adhesive performance, 64second primary molars were divided into four groups and treated as described for group 1b and groups 2b/c/d (n = 16/method), and μTBS of Clearfil SE/Clearfil Majesty Esthetic to dentin was measured. The SEM micrographs were qualitatively analyzed. The μTBS values were compared with a Kruskal-Wallis test. The significance level was set at α = 0.05. SEM micrographs showed the typical micromorphologies with a smear layer for the diamond bur groups and open dentin tubules for all laser-treated groups. However, in group 2d, the laser beam had insufficiently irradiated the dentin area, rendering the underlying ground surface partly visible. There were no statistically significant differences between μTBS values of the four groups (p = 0.394). This suggests that Er:YAG laser treatment of dentin of primary molars provides bond strengths similar to those obtained following diamond bur treatmen

In vitro evaluation of surface roughness, adhesion of periodontal ligament fibroblasts, and Streptococcus gordonii following root instrumentation with Gracey curettes and subsequent polishing with diamond-coated curettes

Objectives: The objective of the study was to evaluate the efficacy of an additional usage of a diamond-coated curette on surface roughness, adhesion of periodontal ligament (PDL) fibroblasts, and of Streptococcus gordonii in vitro. Materials and methods: Test specimens were prepared from extracted teeth and exposed to instrumentation with conventional Gracey curettes with or without additional use of diamond-coated curettes. Surface roughness (Ra and Rz) was measured before and following treatment. In addition, the adhesion of PDL fibroblasts for 72h and adhesion of S. gordonii ATCC 10558 for 2h have been determined. Results: Instrumentation with conventional Gracey curettes reduced surface roughness (median Ra before: 0.36μm/after: 0.25μm; p < 0.001; median Rz before: 2.34μm/after: 1.61μm; p < 0.001). The subsequent instrumentation with the diamond-coated curettes resulted in a median Ra of 0.31μm/Rz of 2.06μm (no significance in comparison to controls). The number of attached PDL fibroblasts did not change following scaling with Gracey curettes. The additional instrumentation with the diamond-coated curettes resulted in a two-fold increase in the number of attached PDL fibroblasts but not in the numbers of adhered bacteria. Conclusions: Treatment of root surfaces with conventional Gracey curettes followed by subsequent polishing with diamond-coated curettes may result in a root surface which provides favorable conditions for the attachment of PDL fibroblasts without enhancing microbial adhesion. Clinical relevance: The improved attachment of PDL fibroblasts and the limited microbial adhesion on root surfaces treated with scaling with conventional Gracey curettes followed by subsequent polishing with diamond-coated curettes may favor periodontal wound healin

The effect of a tin-containing fluoride mouth rinse on the bond between resin composite and erosively demineralised dentin

Objectives: To evaluate the effect of a tin-containing fluoride (Sn/F) mouth rinse on microtensile bond strength (μTBS) between resin composite and erosively demineralised dentin. Materials and methods: Dentin of 120 human molars was erosively demineralised using a 10-day cyclic de- and remineralisation model. For 40 molars, the model comprised erosive demineralisation only; for another 40, the model included treatment with a NaF solution; and for yet another 40, the model included treatment with a Sn/F mouth rinse. In half of these molars (n = 20), the demineralised organic matrix was continuously removed by collagenase. Silicon carbide paper-ground, non-erosively demineralised molars served as control (n = 20). Subsequently, μTBS of Clearfil SE/Filtek Z250 to the dentin was measured, and failure mode was determined. Additionally, surfaces were evaluated using SEM and EDX. Results: Compared to the non-erosively demineralised control, erosive demineralisation resulted in significantly lower μTBS regardless of the removal of demineralised organic matrix. Treatment with NaF increased μTBS, but the level of μTBS obtained by the non-erosively demineralised control was only reached when the demineralised organic matrix had been removed. The Sn/F mouth rinse together with removal of demineralised organic matrix led to significantly higher µTBS than did the non-erosively demineralised control. The Sn/F mouth rinse yielded higher μTBS than did the NaF solution. Conclusions: Treatment of erosively demineralised dentin with a NaF solution or a Sn/F mouth rinse increased the bond strength of resin composite. Clinical relevance: Bond strength of resin composite to eroded dentin was not negatively influenced by treatment with a tin-containing fluoride mouth rins

Towards a Swiss National Research Infrastructure

In this position paper we describe the current status and plans for a Swiss National Research Infrastructure. Swiss academic and research institutions are very autonomous. While being loosely coupled, they do not rely on any centralized management entities. Therefore, a coordinated national research infrastructure can only be established by federating the various resources available locally at the individual institutions. The Swiss Multi-Science Computing Grid and the Swiss Academic Compute Cloud projects serve already a large number of diverse user communities. These projects also allow us to test the operational setup of such a heterogeneous federated infrastructure

Enamel loss and adhesive remnants following bracket removal and various clean-up procedures in vitro

This study evaluated the enamel loss and composite remnants after debonding and clean-up. The tested null hypothesis is that there are no differences between different polishing systems regarding removing composite remnants without damaging the tooth surface. Brackets were bonded to 75 extracted human molars and removed after a storage period of 100 hours. The adhesive remnant index (ARI) was evaluated. The clean-up was carried out with five different procedures: 1. carbide bur; 2. carbide bur and Brownie and Greenie silicone polishers; 3. carbide bur and Astropol polishers; 4. carbide bur and Renew polishers; and 5. carbide bur, Brownie, Greenie and PoGo polishers. Silicone impressions were made at baseline (T0) and after debonding (T1) and polishing (T2) to produce plaster replicas. The replicas were analysed with a three-dimensional laser scanner and measured with analytical software. Statistical analysis was performed with the Kruskal-Wallis test and pairwise Wilcoxon tests with Bonferroni-Holm adjustment (α = 0.05). Enamel breakouts after debonding were detectable in 27 per cent of all cases, with a mean volume loss of 0.02 mm3 (±0.03 mm3) and depth of 44.9 μm (±48.3 μm). The overall ARI scores was 3 with a few scores of 1 and 2. The composite remnants after debonding had a mean volume of 2.48 mm3 (±0.92 mm3). Mean volume loss due to polishing was 0.05 mm3 (±0.26 mm3) and the composite remnants had a mean volume of 0.22 mm3 (±0.32 mm3). There were no statistically significant differences in volumetric changes after polishing (P = 0.054) between the different clean-up methods. However, sufficient clean-up without enamel loss was difficult to achiev

Light curing through glass ceramics with a second- and a third-generation LED curing unit: effect of curing mode on the degree of conversion of dual-curing resin cements

Objectives: The aim of this study was to measure the degree of conversion (DC) of five dual-curing resin cements after different curing modes with a second- and a third-generation light-emitting diode (LED) curing unit. Additionally, irradiance of both light curing units was measured at increasing distances and through discs of two glass ceramics for computer-aided design/manufacturing (CAD/CAM). Materials and methods: Irradiance and spectra of the Elipar FreeLight 2 (Standard Mode (SM)) and of the VALO light curing unit (High Power Mode (HPM) and Xtra Power Mode (XPM)) were measured with a MARC radiometer. Irradiance was measured at increasing distances (control) and through discs (1.5 to 6mm thickness) of IPS Empress CAD and IPS e.max CAD. DC of Panavia F2.0, RelyX Unicem 2 Automix, SpeedCEM, BisCem, and BeautiCem SA was measured with an attenuated total reflectance-Fourier transform infrared spectrometer when self-cured (negative control) or light cured in SM for 40s, HPM for 32s, or XPM for 18s. Light curing was performed directly (positive control) or through discs of either 1.5- or 3-mm thickness of IPS Empress CAD or IPS e.max CAD. DC was analysed with Kruskal-Wallis tests followed by pairwise Wilcoxon rank sum tests (α = 0.05). Results: Maximum irradiances were 1,545mW/cm2 (SM), 2,179mW/cm2 (HPM), and 4,156mW/cm2 (XPM), and all irradiances decreased by >80% through discs of 1.5mm, ≥95% through 3mm, and up to >99% through 6mm. Generally, self-curing resulted in the lowest DC. For some cements, direct light curing did not result in higher DC compared to when light cured through ceramic discs. For other cements, light curing through ceramic discs of 3 mm generally reduced DC. Conclusions: Light curing was favourable for dual-curing cements. Some cements were more susceptible to variations in curing mode than others. Clinical relevance: When light curing a given cement, the higher irradiances of the third-generation LED curing unit resulted in similar DC compared to the second-generation one, though at shorter light curing time

Light curing through glass ceramics: effect of curing mode on micromechanical properties of dual-curing resin cements

Objectives: The aim of this study was to investigate micromechanical properties of five dual-curing resin cements after different curing modes including light curing through glass ceramic materials. Materials and methods: Vickers hardness (VH) and indentation modulus (Y HU) of Panavia F2.0, RelyX Unicem 2 Automix, SpeedCEM, BisCem, and BeautiCem SA were measured after 1week of storage (37°C, 100% humidity). The resin cements were tested following self-curing or light curing with the second-generation light-emitting diode (LED) curing unit Elipar FreeLight 2 in Standard Mode (1,545mW/cm2) or with the third-generation LED curing unit VALO in High Power Mode (1,869mW/cm2) or in XtraPower Mode (3,505mW/cm2). Light curing was performed directly or through glass ceramic discs of 1.5 or 3mm thickness of IPS Empress CAD or IPS e.max CAD. VH and Y HU were analysed with Kruskal-Wallis tests followed by pairwise Wilcoxon rank sum tests (α = 0.05). Results: RelyX Unicem 2 Automix resulted in the highest VH and Y HU followed by BeautiCem SA, BisCem, SpeedCEM, and finally Panavia F2.0. Self-curing of RelyX Unicem 2 Automix and SpeedCEM lowered VH and Y HU compared to light curing whereas self-curing of Panavia F2.0, BisCem, and BeautiCem SA led to similar or significantly higher VH and Y HU compared to light curing. Generally, direct light curing resulted in similar or lower VH and Y HU compared to light curing through 1.5-mm-thick ceramic discs. Light curing through 3-mm-thick discs of IPS e.max CAD generally reduced VH and Y HU for all resin cements except SpeedCEM, which was the least affected by light curing through ceramic discs. Conclusions: The resin cements responded heterogeneously to changes in curing mode. The applied irradiances and light curing times adequately cured the resin cements even through 1.5-mm-thick ceramic discs. Clinical relevance: When light curing resin cements through thick glass ceramic restorations, clinicians should consider to prolong the light curing times even with LED curing units providing high irradiances

The influence of toothbrushing and coffee staining on different composite surface coatings

The aim of our study is to evaluate the performance of surface sealants and conventional polishing after ageing procedures. Eighty circular composite restorations were performed on extracted human molars. After standardised roughening, the restorations were either sealed with one of three surface sealants (Lasting Touch (LT), BisCover LV (BC), G-Coat Plus (GP) or a dentin adhesive Heliobond (HB)) or were manually polished with silicon polishers (MP) (n = 16). The average roughness (Ra) and colourimetric parameters (CP) (L*a*b*) were evaluated. The specimens underwent an artificial ageing process by thermocycling, staining (coffee) and abrasive (toothbrushing) procedures. After each ageing step, Ra and CP measurements were repeated. A qualitative surface analysis was performed with SEM. The differences between the test groups regarding Ra and CP values were analysed with nonparametric ANOVA analysis (α = 0.05). The lowest Ra values were achieved with HB. BC and GP resulted in Ra values below 0.2 μm (clinically relevant threshold), whereas LT and MP sometimes led to higher Ra values. LT showed a significantly higher discolouration after the first coffee staining, but this was normalised to the other groups after toothbrushing. The differences between the measurements and test groups for Ra and CP were statistically significant. However, the final colour difference showed no statistical difference among the five groups. SEM evaluation showed clear alterations after ageing in all coating groups. Surface sealants and dentin adhesives have the potential to reduce surface roughness but tend to debond over time. Surface sealants can only be recommended for polishing provisional restorations