A predictive fatigue life model for anodized 7050 aluminium alloy

The objective of this study is to predict fatigue life of anodized 7050 aluminum alloy specimens. In the case of anodized 7050-T7451 alloy, fractographic observations of fatigue tested specimens showed that pickling pits were the predominant sites for crack nucleation and subsequent failure. It has been shown that fatigue failure was favored by the presence of multiple cracks. From these experimental results, a fatigue life predictive model has been developed including multi-site crack consideration, coalescence between neighboring cracks, a short crack growth stage and a long crack propagation stage. In this model, all pickling pits are considered as potential initial flaws from which short cracks could nucleate if stress conditions allow. This model is built from experimental topography measurements of pickled surfaces which allowed to detect the pits and to characterize their sizes (depth, length, width). From depth crack propagation point of view, the pickling pits are considered as stress concentrator during the only short crack growth stage. From surface crack propagation point of view, machining roughness is equally considered as stress concentrator and its influence is taken into account during the all propagation stage. The predictive model results have been compared to experimental fatigue data obtained for anodized 7050-T7451 specimens. Predictions and experimental results are in good agreement

Surface characterization and influence of anodizing process on fatigue life of Al 7050 alloy

The present study investigates the influence of anodizing process on fatigue life of aluminium alloy 7050-T7451 by performing axial fatigue tests at stress ratio ‘R’ of 0.1. Effects of pre-treatments like degreasing and pickling employed prior to anodizing on fatigue life were studied. The post-exposure surface observations were made by scanning electron microscope (SEM) to characterize the effect of each treatment before fatigue testing. The surface observations have revealed that degreasing did not change the surface topography while pickling solution resulted in the formation of pits at the surface. Energy dispersive spectroscopy (EDS) was used to identify those constituent particles which were responsible for the pits formation. These pits are of primary concern with respect to accelerated fatigue crack initiation and subsequent anodic coating formation. The fatigue test results have shown that pickling process was detrimental in reducing the fatigue life significantly while less decrease has been observed for anodized specimens. Analyses of fracture surfaces of pickled specimens have revealed that the process completely changed the crack initiation mechanisms as compared to non-treated specimens and the crack initiation started at the pits. For most of the anodized specimens, fatigue cracks still initiated at the pits with very few cracks initiated from anodic coating. The decrease in fatigue life for pickled and anodized specimens as compared to bare condition has been attributed to decrease in initiation period and multi-site crack initiations. Multi-site crack initiation has resulted in rougher fractured surfaces for the pickled and anodized specimens as compare to bare specimens tested at same stress levels

Load Frequency Control (LFC) Strategies in Renewable Energy‐Based Hybrid Power Systems:A Review

The hybrid power system is a combination of renewable energy power plants and conventional energy power plants. This integration causes power quality issues including poor settling times and higher transient contents. The main issue of such interconnection is the frequency variations caused in the hybrid power system. Load Frequency Controller (LFC) design ensures the reliable and efficient operation of the power system. The main function of LFC is to maintain the system frequency within safe limits, hence keeping power at a specific range. An LFC should be supported with modern and intelligent control structures for providing the adequate power to the system. This paper presents a comprehensive review of several LFC structures in a diverse configuration of a power system. First of all, an overview of a renewable energy-based power system is provided with a need for the development of LFC. The basic operation was studied in single-area, multi-area and multi-stage power system configurations. Types of controllers developed on different techniques studied with an overview of different control techniques were utilized. The comparative analysis of various controllers and strategies was performed graphically. The future scope of work provided lists the potential areas for conducting further research. Finally, the paper concludes by emphasizing the need for better LFC design in complex power system environments

Tuberculosis in renal transplant recipients in Isfahan University of Medical Sciences

سابقه و هدف : عفـونت با مایکـوباکتـریـوم توبرکولوزیس یکـی از علل مهم بیمارگنـی و مرگ و میـر در دریافتکنندگان پیوند کلیه میباشد. شیوع توبرکولوزیس در این افراد به مراتب بیشتر از افراد عادي میباشد و در کشورهاي در حال توسعهو مناطق آندمیک از نظر B.T ،باز هم شیوع آن بیشتراست. مواد و روشها: در این مطالعه که از نوع مرور پرونده بود، 700 بیمار دریافتکننده پیوند کلیه بررسی شدند و 10 مورد ابتلاي قطعی به توبرکولوزیس، از نظر اطلاعات دموگرافیک، فاصله بین پیوند کلیه تا تشخیص سل، محل درگیري، پیآمد(Outcome ،(بقا(Survival (گرافت مورد مطالعه قرار گرفتند. یافتهها: شیوع توبرکولوزیس پس از پیوند کلیه در این مطالعه 4/1 درصد بود. میانگین سن بیماران 9/37 سال و متوسط فاصله بین پیوند کلیه تا تشخیص B.T 7/15 ماه بود. شایعترین نوع درگیري، B.T برونکوپولمونري(60 درصد) و پس از آن B.T منتشر(20 درصد) و B.T مفصل هیپ(20 درصد) بود. استنتاج: شیوع B.T در بیماران پیوند کلیه بیشتر از افراد عادي است. تظاهرات آن غیرمعمول است و اثر زیادي روي سلامت فرد و عضو پیوندي دارد، در نظر داشتن بیماري و دقت و توجه کافی در پیگیري درازمدت این بیماران باعث تشخیص ودرمان صحیح و بهموقع و کاهش عوارض بیماري خواهد شد

Influence de la rugosité et des traitements d’anodisation sur la tenue en fatigue des alliages d’aluminium aéronautiques 2214 et 7050

The fatigue of materials and structures is a phenomenon in which surface condition plays an important role; specially in initiating the micro-cracks. Moreover, the structural components are also subjected to aggressive environments and hence are susceptible to corrosion phenomenon. Therefore, it is necessary to protect them against the corrosion phenomenon. For aluminium alloys used in aeronautical applications, anodization is widely used surface treatment to increase the corrosion resistance. Despite the benefits obtained in terms of enhanced corrosion resistance, the anodizing process has a damaging effect on the fatigue performance of the base material. One of the reasons for this decrease in fatigue life is associated to the degradation of surface condition during the anodizing process. In this work, we have studied the influence of machining and anodization on fatigue behaviour of aluminium alloys 2214 and 7050. We showed experimentally that for 2214 alloy the process of anodization-sealing reduced the fatigue life considerably while for 7050 alloy the process of pickling is the major cause in decreasing the fatigue life. We have also developed life prediction model for anodized alloys. The model is based on determination of concentration of stress ‘Kt’ generated by the surface condition. The developed model integrates the aspects of multi-site initiation, coalescence and regime of short crack propagation

A comparison of motivational self-regulation and high-risk behaviors in students suffering from attention deficit/hyperactivity disorder (ADHD) and normal students

زمینه و هدف: اختلال نقص توجه/ بیش فعالی یکی از اختلالاتی می‌باشد که توجه بسیاری از روان شناسان، روان پزشکان و پژوهشگران را به خود جلب کرده است. ازجمله عواملی که می‌تواند در تداوم این اختلال دخیل باشد، تنظیم نامناسب انگیزه‌ها و رفتارهای پرخطر است؛ لذا هدف پژوهش حاضر، مقایسه خودتنظیمی انگیزشی و رفتارهای پرخطر در دانش آموزان مبتلا به اختلال نقص توجه/ بیش فعالی و دانش آموزان عادی است. روش بررسی: این پژوهش توصیفی از نوع توصیفی- تحلیلی است. جامعه آماری پژوهش حاضر را کلیه دانش‌آموزان پسر مبتلا اختلال نقص توجه/ بیش فعالی و دانش آموزان عادی کلاس سوم دبیرستان تشکیل دادند که در سال تحصیلی 94-93 در شهر اردبیل مشغول به تحصیل بودند. نمونه پژوهش به حجم 80 نفر (شامل 40 دانش آموز عادی و 40 دانش آموز مبتلا به اختلال نقص توجه/ بیش فعالی) بودند که به‌صورت نمونه گیری خوشه‌ای چندمرحله‌ای انتخاب شدند، برای جمع‌آوری داده ها از مقیاس خودتنظیمی انگیزشی، مقیاس خطرپذیری نوجوانان ایرانی، مقیاس تشخیصی کوتاه اختلال نقص توجه/ بیش فعالی بزرگسالان کانرز و مصاحبه تشخیصی بر اساس DSM-5 استفاده شد. یافته ها: نتایج تحلیل واریانس چند متغیری (MANOVA) نشان داد که میانگین نمرات خودتنظیمی انگیزشی (در تمامی مؤلفه‌ها) دانش آموزان مبتلا به اختلال نقص توجه/ بیش فعالی به‌طور معنی داری از دانش آموزان عادی کمتر است (001/0>P)؛ همچنین نتایج نشان داد که میانگین نمرات رفتارهای پرخطر (در تمامی مؤلفه‌ها) دانش آموزان مبتلا به اختلال نقص توجه/ بیش فعالی به‌طور معنی داری از میانگین نمرات دانش آموزان عادی بیشتر است (001/0>P). نتیجه گیری: نتایج به‌دست‌آمده از این یافته‌ها نشانگر اهمیت راهبردهای خودتنظیمی انگیزشی و تنظیم و تعدیل این انگیزه‌ها در جهت پیشرفت تحصیلی و کاهش رفتارهای پرخاشگرانه، بی‌توجهی، حواس پرتی و درنهایت پیشگیری و کاهش رفتارهای پرخطر در دانش آموزان مبتلا به اختلال نقص توجه/ بیش فعالی است

Influence du décapage sur la tenue en fatigue de l'alliage Al7010-T7451 traité par oxydation anodique chromique

L’oxydation anodique chromique (OAC) est un procédé de traitement des alliages d’aluminium pour améliorer leur tenue à la corrosion. L’influence de ce traitement sur la durée de vie de l’alliage 7010-T7451 est étudiée à partir d’essais de fatigue en flexion rotative. Une réduction de la durée de vie par rapport à l’état usiné est observée. Il est montré que cette diminution de la durée de vie est imputable en grande partie à la dégradation de la rugosité de la surface occasionnée par la phase de décapage. Il est également montré que la correction des résultats de fatigue par le coefficient de concentration de contrainte local, déterminé par la méthode des éléments finis à partir du relevé du profil de rugosité, permet de rationaliser les courbes de fatigue de cet alliage : l’ensemble des résultats d’essais obtenus sur des éprouvettes n’ayant rien subi après l’usinage ou n’ayant subi que les phases de dégraissage et de décapage s’alignent sur une même courbe de fatigue maîtresse. Il est également montré que, traités par cette méthode du Ktlocal, les résultats de la durée de vie obtenus sur des éprouvettes décapées puis anodisées s’alignent sur une deuxième courbe décalée par rapport à cette courbe maîtresse

Modélisation de la multi-fissuration d’un alliage d’aluminium 7010 traité par oxydation anodique chromique

L’oxydation anodique chromique (OAC) est un procédé de traitement des alliages d’aluminium pour améliorer leur tenue à la corrosion mais il entraîne une très forte réduction de la durée de vie par rapport à l’état usiné. Cette diminution de la durée de vie est largement imputable à la dégradation de la rugosité de la surface occasionnée par la phase de décapage. La présente étude est consacrée à la modélisation de la fissuration à partir des piqûres de décapage observées à la surface d’échantillon en alliage 7010 traités puis testés en flexion rotative. Ces piqûres de décapage sont caractérisées par mesures topographiques. Ces topographies servent à élaborer des modèles éléments finis qui permettent de déterminer la contrainte locale maximale au droit de ces piqûres. Dans le modèle de calcul en fatigue, ces piqûres sont considérées comme des microfissures qui, en se propageant aussi bien en surface qu’en profondeur, peuvent coalescer avant de poursuivre leur propagation. Le calcul en fatigue est stoppé à la fin du stade II de la propagation

Myotonic dystrophy in a Pakistani family: a case series and literature review

Myotonic dystrophy also known as (Steinert\u27s disease) is a clinically and genetically heterogeneous multisystem disorder with a prevalence of 1 in 8000 in the general population. It is inherited as an autosomal dominant trait. It is characterized by myotonia, myopathy of voluntary and involuntary muscles, frontal baldness in men, cardiac conduction abnormalities, cataracts, intellectual deterioration and endocrinopathies. Affected men may have gonadal atrophy and infertility. On the other hand women are generally fertile. We report a case series of three individuals belonging to the same family presenting with characteristic features of myotonic dystrophy. The presentation of these cases depicts that this disease can lead to disability, loss of independence and social isolation especially in the elderly. They warrant adequate work up for diagnosis which may sometimes be extensive. Proper genetic counseling of the family is required regarding nature of the disease and with risks and prognosis

Awareness of stroke among general Practitioners

Stroke is the 2nd leading cause of death and 3rd leading cause of disability after cancer and ischemic heart disease. The recognition of acute stroke symptoms and knowledge about timely and prompt referral of a patient for possible thrombolysis is a need of time for which general practitioners (as they have to be the first responders many a times across Pakistan) need to be equipped with the advance knowledge about stroke treatment