One-step Laser-Induced Hydrogen Generation from Coal Powders in Water

This study presents a simple way of obtaining hydrogen gas (H2) from various ranks of coal, coke, and graphite using nanosecond laser pulses. Powder samples of coal and graphite with and without water were irradiated with 1064 nm and 532 nm pulses from an Nd: YAG laser for 45 minutes under air and argon atmospheres. It was observed that 532 nm laser pulses were more effective than 1064 nm pulses in gas generation and both were nonlinearly correlated with respect to the laser energy density. Mainly hydrogen (H2) and carbon monoxide (CO) were observed. The H2 to CO ratio shows that the highest efficiency rank was the anthracite coal, with an average ratio of 1.4 due to its high fixedcarbon content and relatively high hydrocarbon amount. Coal samples were characterized by scanning electron microscope (SEM), Fourier transform infrared (FTIR) spectroscopy, Thermogravimetric analyzer (TGA), and calorimeter. Graphite was used as a pure carbon source to study the possible reactions of gas yielded during irradiation process. The amount of H2 produced was negligible when graphite powder was exposed under the air and argon atmospheres. On the other hand, H2 was obtained from irradiation of graphite powder in the presence of water due to a possible carbon-water reaction. When coal powders were irradiated under air and argon atmosphere, the amount of produced H2 increased drastically compared to graphite due to the presence of hydrocarbons in coal. In addition, theoretical simulations by a standard finite difference method supported experimental observations

Laser Shock Wave Assisted Patterning on NiTi Shape Memory Alloy Surfaces

An advanced direct imprinting method with low cost, quick, and less environmental impact to create thermally controllable surface pattern using the laser pulses is reported. Patterned micro indents were generated on Ni50Ti50 shape memory alloys (SMA) using an Nd:YAG laser operating at 1064 nm combined with suitable transparent overlay, a sacrificial layer of graphite, and copper grid. Laser pulses at different energy densities which generates pressure pulses up to 10 GPa on the surface was focused through the confinement medium, ablating the copper grid to create plasma and transferring the grid pattern onto the NiTi surface. Scanning electron microscope (SEM) and optical microscope images of square pattern with different sizes were studied. One dimensional profile analysis shows that the depth of the patterned sample initially increase linearly with the laser energy until 125 mJ/pulse where the plasma further absorbs and reflects the laser beam. In addition, light the microscope image show that the surface of NiTi alloy was damaged due to the high power laser energy which removes the graphite layer

Recoverable Stress Induced Two-Way Shape Memory Effect on NiTi Surface Using Laser-Produced Shock Wave

The surfaces of Ni50Ti50 shape memory alloys (SMAs) were patterned by laser scribing. This method is more simplistic and efficient than traditional indentation techniques, and has also shown to be an effective method in patterning these materials. Different laser energy densities ranging from 5 mJ/pulse to 56 mJ/pulse were used to observe recovery on SMA surface. The temperature dependent heat profiles of the NiTi surfaces after laser scribing at 56 mJ/pulse show the partially-recovered indents, which indicate a shape memory effect (SME) Experimental data is in good agreement with theoretical simulation of laser induced shock wave propagation inside NiTi SMAs. Stress wave closely followed the rise time of the laser pulse to its peak values and initial decay. Further investigations are underway to improve the SME such that the indents are recovered to a greater extent

Formation of Two-Way Shape Memory Effect in NiTi Alloy Using Pulsed Laser Irradiation

Shape memory alloys (SMAs) are a unique class of smart materials and they were employed in various applications in engineering, biomedical, and aerospace technologies. Here, we report an advanced, efficient, and low-cost direct imprinting method with low environmental impact to create thermally controllable surface patterns. Patterned microindents were generated on Ni50Ti50 (at. %) SMAs using an Nd:YAG laser with 1064 nm wavelength at 10 Hz. Laser pulses at selected fluences were focused on the NiTi surface and generated pressure pulses of up to a few GPa. Optical microscope images showed that surface patterns with tailorable sizes can be obtained. The depth of the patterns increases with laser power and irradiation time. Upon heating, the depth profile of SMA surfaces changed where the maximum depth recovery ratio of 30 % was observed. Recovery ratio decreased and saturated at about 15 % when the amount of time and thus the indent depth was increased. Laser-induced shock wave propagation inside the material was simulated and showed a good agreement with the experimental results. The stress wave closely followed the rise time of the laser pulse to its peak value and initial decay. Rapid attenuation and dispersion of the stress wave were observed

Room-temperature superfluorescence in hybrid perovskites and its origins

International audienc