Oxidation behaviour of SiC/SiC ceramic matrix composites in air

Oxidation of silicon melt infiltrated SiC/SiC ceramic matrix composites (CMC) was studied in air at 1200–1400 °C for 1, 5, 24 and 48 h. Weight gain and oxide layer thickness measurements revealed the oxidation follows parabolic reaction kinetics with increase in temperature and time. XRD showed the extent of oxide layer (SiO2) formation was greatest after 48 h at 1400 °C: an observation confirmed by X-ray photoelectron spectroscopy (XPS), energy dispersive spectroscopy (EDS) and transmission electron microscopy (TEM) analyses. Oxide layer thickness varied from 1 μm after 48 h at 1200 °C to 8 μm after 48 h at 1400 °C. Oxidation of SiC/SiC composites is both temperature and time dependent with an activation energy of 619 kJ mol−1. BN coatings around SiC fibres showed good resistance to oxidation even after 48 h at 1400 °C

Boehmite-bonded high-alumina refractories

High-alumina refractories (99+ % Al₂O₃) were produced by pressing a mixture of 70% tabular alumina and 30% reactive alumina and autoclaving in saturated steam at 1.4 MPa (200 psia)/194 °C to 3.4 MPa (500 psia)/242 °C for 12 to 96 h. Autoclaving converted the reactive alumina to boehmite which acted as the bond phase. At room temperature the MOR ranged up to 37 MPa depending upon boehmite content. The hot-MOR decreased steadily with increasing temperature, but was still 8 MPa at 1400 °C which exceeds that of comparable cement-bonded or conventionally fired high-alumina refractories. The estimated autoclaving costs are lower than conventional firing costs, but the overall economics of boehmite-bonded refractories are highly dependent upon the cost of the alumina used to form boehmite --Abstract, page 1

Dentina afetada por cárie : avaliação e desenvolvimento de adesivo experimental

A Odontologia minimamente invasiva tornou-se possível em decorrência do atual avanço alcançado na Odontologia adesiva, e a remoção seletiva do tecido cariado passou a ser recomendada para dentes com lesões de cárie profunda. Tal preparo cavitário preserva a dentina afetada por cárie (DAC), camada mais interna da dentina cariada que é remineralizável. Entretanto, esse substrato apresenta propriedades mecânicas inferiores e diversos estudos relatam uma resistência de união reduzida. O objetivo do presente estudo foi revisar sistematicamente a literatura quanto a resistência da união dos sistemas adesivos à DAC quando comparada à dentina hígida (DH), assim como a influência das variáveis metodológicas dos estudos in vitro. Além disso, desenvolver e caracterizar uma resina adesiva com a incorporação de um fosfato de cálcio, assim como avaliar o potencial de induzir deposição mineral em dentes com DAC. As buscas foram realizadas nas bases de dados PubMed, Scopus, Web of Science e LILACS. Foram incluídos estudos laboratoriais que investigaram a resistência de união à microtração imediata e longitudinal de sistemas adesivos À DAC natural ou artificial, utilizando DH como controle. Oito artigos preencheram os critérios de inclusão, e uma metaregressão foi realizada para a associação das variáveis independentes do modelo com o desfecho de resistência de união. O modelo final com 5 variáveis explicou 75,6% da variabilidade entre os grupos. Todas as variáveis independentes apresentaram influência significativa no desfecho, e a DAC resultou em menor resistência de união. Sendo assim, uma resina adesiva com a incorporação de α-fosfato tricálcico (αTCP) foi desenvolvida e caracterizada. Para a formulação das resinas adesivas, 66,66% em peso de BisGMA, 33,33% em peso de HEMA e um sistema fotoiniciador foram misturados. O αTCP foi adicionado a 2% em peso, originando a resina adesiva teste. Uma resina sem adição de carga foi utilizada como controle. As resinas adesivas foram caracterizadas quanto à taxa de polimerização e grau de conversão, e degradação em solvente. Sessenta dentes permanentes extraídos com lesões de cárie profunda foram submetidos à remoção seletiva do tecido cariado e restaurados utilizando uma das duas resinas adesivas. As amostras foram avaliadas por meio de ensaios imediatos e longitudinais (no decorrer de 6 meses, armazenadas em SBF) de resistência de união à microtração, avaliação da deposição mineral por espectroscopia Raman e dureza Knoop. A dureza Knoop inicial da resina adesiva teste foi maior quando comparada à controle, e não houve diferença entre os grupos em relação ao percentual de variação da dureza Knoop após a imersão em solvente. O grupo teste apresentou maior taxa de polimerização e não houve diferença entres os grupos para o grau de conversão. Não houve diferença entre os grupos para a resistência de união imediata e longitudinal, e ambos os grupos mantiveram estável a resistência de união após 6 meses. A análise da interface em relação à deposição mineral mostrou que houve aumento do conteúdo mineral para os dois grupos. Em relação à dureza Knoop, houve um aumento nos valores após 3 meses, entretanto não houve diferença entre os grupos dentro das diferentes profundidades para cada tempo. Conclui-se que não houve diferença entre os grupos em relação à deposição mineral.The minimally invasive dentistry became possible due to the current advancement in adhesive dentistry, and the selective removal of carious tissue has been recommended for teeth with deep carious lesions. Such cavity preparation preserves the caries-affected dentin (CAD), the inner layer of carious dentin that is remineralizable. However, this substrate presents low mechanical properties and many studies reported reduced bond strength. The objective of this study was to systematically review the literature on the microtensile bond strength (μTBS) of adhesive systems to (CAD) when compared to sound dentin (SD), as well as on the influence of methodological variables of in vitro studies. Also, to develop and characterize an adhesive resin with the incorporation of a calcium phosphate, as well as evaluate the potential to induce mineral deposition in teeth presenting CAD. The electronic databases PubMed, Scopus, ISI Web of Science and LILACS were systematically searched. Were included in vitro studies that assessed the immediate and aged microtensile bond strength of adhesive systems to natural or artificially created CAD in comparison to SD. Eight studies met the inclusion criteria and were included in a linear meta-regression of microtensile bond strength. The fully adjusted model with 5 methodological variables explained 75.6% of the variability among groups. All methodological variables were associated with microtensile bond strength, and bond strength to CAD was lower than to SD. Thus, an adhesive resin with the incorporation of α-tricalcium phosphate (αTCP) was developed and characterized. To formulate the experimental adhesive resins, 66.66 wt% BisGMA, 33.33 wt% HEMA and a photo-initiator system were mixed. The αTCP at 2 wt% was added, yielding the test adhesive resin. An adhesive resin without filler was used as control. The adhesive resins were characterized regarding polymerization kinetics and degree of conversion, and softening in ethanol. Sixty extracted human posterior permanent teeth with deep carious lesions were submitted to selective removal of carious tissue and restored using one of the two adhesive resins. Samples were evaluated by immediate and longitudinal (6 months, storage in SBF) following tests: microtensile bond strength, mineral deposition by Raman spectroscopy and Knoop hardness. The test adhesive resin showed higher initial Knoop hardness than the control one, and there was no difference between the groups for the percentage of variation of Knoop hardness after solvent immersion. The test group showed increased polymerization rate, and there was no difference between groups for degree of conversion. There was no difference between the groups for immediate and longitudinal microtensile bond strength, and the microtensile bond strength of both groups remained stable after the 6 months. The interface analysis regarding mineral deposition showed an increasing in mineral content for both groups. For Knoop hardness, there was an increase after 3 months, however the groups where not significantly different considering depth and time. It could be concluded that there was no difference between control and test adhesive resin for mineral deposition

Model and prototype of an extensible repository for components of software

Várias ferramentas de desenvolvimento utilizam mecanismos para centralizar/gerenciar código compartilhado entre diferentes desenvolvedores ou equipes de desenvolvimento. Estes repositórios geralmente deixam muito a desejar em relação aos serviços que oferecem, não só aos desenvolvedores, mas também aos usuários de sistemas já desenvolvidos, que desejam ter atualizações e correções constantes em seus aplicativos. Surge então a necessidade de disponibilizar esses recursos em um ambiente de trabalho realmente cooperado. Este trabalho propõe a modelagem de um repositório de componentes de software, formado por uma área de armazenamento centralizada comum aos desenvolvedores, e com capacidade de gerenciar componentes e agregar serviços extras, administrando seu ciclo de vida de modo integrado. Para tal, várias tecnologias baseadas em Java foram integradas, tais como as seguintes API's: Enterprise Java Beans (EJB), Java Naming and Directory Interface (JNDI), Remote Method Invocation (RMI), Java Messaging Service (JMS), Java Transaction (JTA), Java Transaction Service (JTS) e Java Database Connection (JDBC).Para que o modelo aqui proposto possua um nível de funcionalidade adequado, são fornecidos vários serviços pelo repositório, atendendo assim às expectativas tanto de desenvolvedores, como dos usuários finais. Dentre outros, são providos os seguintes serviços: Serviço de Descrição, Serviço de Histórico, Serviço de Controle de Versões, Serviço de Teste OO, Serviço de Padrões de Projeto e Serviço de Invalidação de Componentes.Software development tools commonly use mechanisms for storing/managing code shared among different developers or development teams. These repositories generally are very poor in relation to the services they provide to developers and also to the users of already developed systems which need to make constant updates and corrections on their applications. There is a need to supply supporting services to software integration through a really cooperated development environment. This work considers the modeling of a software component repository comprising a common storage area to be accessed by developers, possessing capacity to manage components and to add extra services, and managing the development life cycle in an integrated mode. To accomplish this model, some technologies based on Java have been integrated, namely: Enterprise Java Beans (EJB), Java Naming and Directory Interface (JNDI), Remote Method Invocation (RMI), Java Messaging Service (JMS), Java Transaction (JTA), Java Transaction Service (JTS) and Java Database Connection (JDBC). For the model considered here to have an adjusted level of functionality, some repository services are supplied so assuring the expectations of developers and final users. Among the services provided, the following must be mentioned: Description Service, History Service, Version Control Service, OO Test Service, Design Patterns Service and Components Invalidation Service

Seleção de carteira através do modelo de Markowitz

Uma crescente quantidade de pessoas aplica seus recursos, em investimentos, na qual esperando agregar um maior valor, ou pelo menos protegê-lo dos riscos de perda do poder aquisitivo. Nos últimos tempos a número de opções de investimentos ampliou-se muito, sendo que o investimento no mercado de ações constitui-se uma dessas opções. Paralelamente, nos últimos anos houve uma ampliação nos estudos sobre o comportamento do mercado de capitais, com a finalidade de prever quais seriam as melhores opções de investimentos em ações. A fim de auxiliar este estudo observa-se uma ampliação de estudos quantitativos baseados na teoria econômica e financeira, a fim de elaborar modelos para tomada de decisão dos investidores. O trabalho demonstra como o processo de criação de uma carteira de ações pode ser elaborado, partindo da teoria de Markowitz, a com objetivo de minimizar o risco do conjunto de investimento, mediante um retorno esperado, utilizando a programação linear. Por fim, trabalho será concluído mostrando os resultados, de uma forma geral, as limitações dos cálculos feitos e como fazer para se chegar ao percentual de alocação ideal de um portfólio em renda variável. O trabalho ainda discutirá o número ótimo de ações que permite se obter carteiras diversificadas para a população de estudo (as ações mais negociadas no mercado acionário de São Paulo).An increasing amount of people applies its resources, in investments, the which wait to link a great value, or at least to protect it of the risks of loss of the purchasing power. In the last times the number of options of investments was extended very, being that the investment in the action market consists one of these options. Parallely, in the last years it had an enlargement in the studies on the behavior of the stock market, with the purpose to foresee, which would be the best options of investments in shares. In order to assist this study a magnifying of based quantitative studies in the economic and financial theory is observed, in order to elaborate models for taking of decision of the investors. The work demonstrates as the construction of a portfolio can be elaborated, from of the theory of Markowitz, with objective to minimize the risk of the set of investment, by means of a waited return, using the linear programming. These is a form the user can be helped by the softwares and to continue incriseasing hers apllies by these compensation. Finally, work will be concluded showing the results, of a general form, about limitations of the done calculations and as to make to arrive itself at the ideal percentage of allocation of a portfólio in changeable income. The work still will argue the excellent number of action that allows to get wallets diversified for the study population (the negotiated actions more in the shareholding market of São Paulo)

Dentina afetada por cárie : avaliação e desenvolvimento de adesivo experimental

A Odontologia minimamente invasiva tornou-se possível em decorrência do atual avanço alcançado na Odontologia adesiva, e a remoção seletiva do tecido cariado passou a ser recomendada para dentes com lesões de cárie profunda. Tal preparo cavitário preserva a dentina afetada por cárie (DAC), camada mais interna da dentina cariada que é remineralizável. Entretanto, esse substrato apresenta propriedades mecânicas inferiores e diversos estudos relatam uma resistência de união reduzida. O objetivo do presente estudo foi revisar sistematicamente a literatura quanto a resistência da união dos sistemas adesivos à DAC quando comparada à dentina hígida (DH), assim como a influência das variáveis metodológicas dos estudos in vitro. Além disso, desenvolver e caracterizar uma resina adesiva com a incorporação de um fosfato de cálcio, assim como avaliar o potencial de induzir deposição mineral em dentes com DAC. As buscas foram realizadas nas bases de dados PubMed, Scopus, Web of Science e LILACS. Foram incluídos estudos laboratoriais que investigaram a resistência de união à microtração imediata e longitudinal de sistemas adesivos À DAC natural ou artificial, utilizando DH como controle. Oito artigos preencheram os critérios de inclusão, e uma metaregressão foi realizada para a associação das variáveis independentes do modelo com o desfecho de resistência de união. O modelo final com 5 variáveis explicou 75,6% da variabilidade entre os grupos. Todas as variáveis independentes apresentaram influência significativa no desfecho, e a DAC resultou em menor resistência de união. Sendo assim, uma resina adesiva com a incorporação de α-fosfato tricálcico (αTCP) foi desenvolvida e caracterizada. Para a formulação das resinas adesivas, 66,66% em peso de BisGMA, 33,33% em peso de HEMA e um sistema fotoiniciador foram misturados. O αTCP foi adicionado a 2% em peso, originando a resina adesiva teste. Uma resina sem adição de carga foi utilizada como controle. As resinas adesivas foram caracterizadas quanto à taxa de polimerização e grau de conversão, e degradação em solvente. Sessenta dentes permanentes extraídos com lesões de cárie profunda foram submetidos à remoção seletiva do tecido cariado e restaurados utilizando uma das duas resinas adesivas. As amostras foram avaliadas por meio de ensaios imediatos e longitudinais (no decorrer de 6 meses, armazenadas em SBF) de resistência de união à microtração, avaliação da deposição mineral por espectroscopia Raman e dureza Knoop. A dureza Knoop inicial da resina adesiva teste foi maior quando comparada à controle, e não houve diferença entre os grupos em relação ao percentual de variação da dureza Knoop após a imersão em solvente. O grupo teste apresentou maior taxa de polimerização e não houve diferença entres os grupos para o grau de conversão. Não houve diferença entre os grupos para a resistência de união imediata e longitudinal, e ambos os grupos mantiveram estável a resistência de união após 6 meses. A análise da interface em relação à deposição mineral mostrou que houve aumento do conteúdo mineral para os dois grupos. Em relação à dureza Knoop, houve um aumento nos valores após 3 meses, entretanto não houve diferença entre os grupos dentro das diferentes profundidades para cada tempo. Conclui-se que não houve diferença entre os grupos em relação à deposição mineral.The minimally invasive dentistry became possible due to the current advancement in adhesive dentistry, and the selective removal of carious tissue has been recommended for teeth with deep carious lesions. Such cavity preparation preserves the caries-affected dentin (CAD), the inner layer of carious dentin that is remineralizable. However, this substrate presents low mechanical properties and many studies reported reduced bond strength. The objective of this study was to systematically review the literature on the microtensile bond strength (μTBS) of adhesive systems to (CAD) when compared to sound dentin (SD), as well as on the influence of methodological variables of in vitro studies. Also, to develop and characterize an adhesive resin with the incorporation of a calcium phosphate, as well as evaluate the potential to induce mineral deposition in teeth presenting CAD. The electronic databases PubMed, Scopus, ISI Web of Science and LILACS were systematically searched. Were included in vitro studies that assessed the immediate and aged microtensile bond strength of adhesive systems to natural or artificially created CAD in comparison to SD. Eight studies met the inclusion criteria and were included in a linear meta-regression of microtensile bond strength. The fully adjusted model with 5 methodological variables explained 75.6% of the variability among groups. All methodological variables were associated with microtensile bond strength, and bond strength to CAD was lower than to SD. Thus, an adhesive resin with the incorporation of α-tricalcium phosphate (αTCP) was developed and characterized. To formulate the experimental adhesive resins, 66.66 wt% BisGMA, 33.33 wt% HEMA and a photo-initiator system were mixed. The αTCP at 2 wt% was added, yielding the test adhesive resin. An adhesive resin without filler was used as control. The adhesive resins were characterized regarding polymerization kinetics and degree of conversion, and softening in ethanol. Sixty extracted human posterior permanent teeth with deep carious lesions were submitted to selective removal of carious tissue and restored using one of the two adhesive resins. Samples were evaluated by immediate and longitudinal (6 months, storage in SBF) following tests: microtensile bond strength, mineral deposition by Raman spectroscopy and Knoop hardness. The test adhesive resin showed higher initial Knoop hardness than the control one, and there was no difference between the groups for the percentage of variation of Knoop hardness after solvent immersion. The test group showed increased polymerization rate, and there was no difference between groups for degree of conversion. There was no difference between the groups for immediate and longitudinal microtensile bond strength, and the microtensile bond strength of both groups remained stable after the 6 months. The interface analysis regarding mineral deposition showed an increasing in mineral content for both groups. For Knoop hardness, there was an increase after 3 months, however the groups where not significantly different considering depth and time. It could be concluded that there was no difference between control and test adhesive resin for mineral deposition

Seleção de carteira através do modelo de Markowitz

Uma crescente quantidade de pessoas aplica seus recursos, em investimentos, na qual esperando agregar um maior valor, ou pelo menos protegê-lo dos riscos de perda do poder aquisitivo. Nos últimos tempos a número de opções de investimentos ampliou-se muito, sendo que o investimento no mercado de ações constitui-se uma dessas opções. Paralelamente, nos últimos anos houve uma ampliação nos estudos sobre o comportamento do mercado de capitais, com a finalidade de prever quais seriam as melhores opções de investimentos em ações. A fim de auxiliar este estudo observa-se uma ampliação de estudos quantitativos baseados na teoria econômica e financeira, a fim de elaborar modelos para tomada de decisão dos investidores. O trabalho demonstra como o processo de criação de uma carteira de ações pode ser elaborado, partindo da teoria de Markowitz, a com objetivo de minimizar o risco do conjunto de investimento, mediante um retorno esperado, utilizando a programação linear. Por fim, trabalho será concluído mostrando os resultados, de uma forma geral, as limitações dos cálculos feitos e como fazer para se chegar ao percentual de alocação ideal de um portfólio em renda variável. O trabalho ainda discutirá o número ótimo de ações que permite se obter carteiras diversificadas para a população de estudo (as ações mais negociadas no mercado acionário de São Paulo).An increasing amount of people applies its resources, in investments, the which wait to link a great value, or at least to protect it of the risks of loss of the purchasing power. In the last times the number of options of investments was extended very, being that the investment in the action market consists one of these options. Parallely, in the last years it had an enlargement in the studies on the behavior of the stock market, with the purpose to foresee, which would be the best options of investments in shares. In order to assist this study a magnifying of based quantitative studies in the economic and financial theory is observed, in order to elaborate models for taking of decision of the investors. The work demonstrates as the construction of a portfolio can be elaborated, from of the theory of Markowitz, with objective to minimize the risk of the set of investment, by means of a waited return, using the linear programming. These is a form the user can be helped by the softwares and to continue incriseasing hers apllies by these compensation. Finally, work will be concluded showing the results, of a general form, about limitations of the done calculations and as to make to arrive itself at the ideal percentage of allocation of a portfólio in changeable income. The work still will argue the excellent number of action that allows to get wallets diversified for the study population (the negotiated actions more in the shareholding market of São Paulo)

Boehmite-Bonded High Alumina Refractories

The objective of the present study was to investigate the feasibility of producing boehmite-bonded, high alumina refractories. The optimum autoclaving conditions, saturated steam pressure, and exposure time were determined within assumed technological and economical limits. The mechanical and thermal properties of these high alumina refractories containing no bond agent other than boehmite were measured and related to the autoclaving conditions