39 research outputs found
Modelling the damage evolution in notched omega stiffened composite panels under compression
In this paper, the compressive behaviour of an omega stiffened composite panel with a large notch damage has been investigated. The influence of intra-laminar and inter-laminar damage onset and evolution on the compressive behaviour of a stiffened panel, characterised by a cut-out located in the middle bay and oriented at 45° with respect to the load direction, has been studied. A numerical model, taking into account delamination and fibre-matrix damage evolution, respectively, by means of cohesive elements and Hashin's failure criteria together with material degradation rules, has been adopted. By comparing the performed numerical analyses, taking into account intra-laminar and inter-laminar damages, the effects of the interaction between delaminations and fibre-matrix damage in the large notch area on the global compressive behaviour of the omega stiffened composite panel have been assessed and critically discussed
Application of an additive manufactured hybrid metal/composite shock absorber panel to a military seat ejection system
In this work, a preliminary numerical assessment on the application of an additive manufactured hybrid metal/composite shock absorber panels to a military seat ejection system, has been carried out. The innovative character of the shock absorber concept investigated is that the absorbing system has a thickness of only 6 mm and is composed of a pyramidâshaped lattice core that, due to its small size, can only be achieved by additive manufacturing. The mechanical behaviour of these shock absorber panels has been examined by measuring their ability to absorb and dissipate the energy generated during the ejection phase into plastic deformations, thus reducing the loads acting on pilots. In this paper the effectiveness of a system composed of five hybrid shock absorbers, with very thin thickness in order to be easily integrated between the seat and the aircraft floor, has been numerically studied by assessing their ability to absorb the energy generated during the primary ejection phase. To accomplish this, a numerical simulation of the explosion has been performed and the energy absorbed by the shockâabsorbing mechanism has been assessed. The performed analysis demonstrated that the panels can absorb more than 60% of the energy generated during the explosion event while increasing the total mass of the pilotâseat system by just 0.8%
Cross-influence between intra-laminar damages and fibre bridging at the skin-stringer interface in stiffened composite panels under compression
In this paper, the skin-stringer separation phenomenon that occurs in stiffened composite panels under compression is numerically studied. Since the mode I fracture toughness and, consequently, the skin-stringer separation can be influenced by the fibre bridging phenomenon at the skin-stringer interface, in this study, comparisons among three different material systems with different fibre bridging sensitivities have been carried out. Indeed, a reference material system has been compared, in terms of toughness performance, against two materials with different degrees of sensitivity to fibre bridging. A robust numerical procedure for the delamination assessment has been used to mimic the skin-stringer separation. When analysing the global compressive behaviour of the stiffened panel, intra-laminar damages have been considered in conjunction with skin-stringer debonding to evaluate the effect of the fibre and matrix breakage on the separation between the skin and the stringer for the three analysed material systems. The latter are characterised by different toughness characteristics and fibre bridging sensitivities, resulting in a different material toughness
A robust numerical methodology for fatigue damage evolution simulation in composites
Composite materials, like metals, are subject to fatigue effects, representing one of the main causes for component collapse in carbon fiberâreinforced polymers. Indeed, when subject to low stress cyclic loading, carbon fiberâreinforced polymers exhibit gradual degradation of the mechanical properties. The numerical simulation of this phenomenon, which can strongly reduce time and costs to market, can be extremely expensive in terms of computational effort since a very high number of static analyses need to be run to take into account the real damage propagation due the fatigue effects. In this paper, a novel cycle jump strategy, named Smart Cycle strategy, is introduced in the numerical model to avoid the simulation of every single cycle and save computational resources. This cycle jump strategy can be seen as an enhancement of the empirical model proposed by Shokrieh and Lessard for the evaluation of the fatigueâinduced strength and stiffness degradation. Indeed, the Smart Cycle allows quickly obtaining a preliminary assessment of the fatigue behavior of composite structures. It is based on the hypothesis that the stress redistribution, due to the fatigueâinduced gradual degradation of the material properties, can be neglected until sudden fiber and/or matrix damage is verified at element/lamina level. The numerical procedure has been implemented in the commercial finite element code ANSYS MECHANICAL, by means of Ansys Parametric Design Languages (APDL). Briefly, the Smart Cycle routine is able to predict cycles where fatigue failure criteria are likely to be satisfied and to limit the numerical simulation to these cycles where a consistent damage propagation in terms of fiber and matrix breakage is expected. The proposed numerical strategy was preliminarily validated, in the frame of this research study, on 30° fiberâoriented unidirectional coupons subjected to tensileâ tensile fatigue loading conditions. The numerical results were compared with literature experimental data in terms of number of cycles at failure for different percentage of the static strength. Lastly, in order to assess its potential in terms of computational time saving on more complex structures and different loading conditions, the proposed numerical approach was used to investigate the fatigue behavior of a crossâply openâhole composite panel under tensionâtension fatigue loading conditions
Numerical-experimental investigation into the tensile behavior of a hybrid metallic-CFRP stiffened aeronautical panel
In this work, the tensile behavior of a hybrid metallic-composite stiffened panel is investigated. The analyzed structure consists of an omega-reinforced composite fiber-reinforced plastic (CFRP) panel joined with a Z-reinforced aluminum plate by fasteners. The introduced numerical model, able to simulate geometrical and material non-linearities, has been preliminary validated by means of comparisons with experimental test results, in terms of strain distributions in both composite and metallic sub-components. Subsequently, the inter-laminar damage behavior of the investigated hybrid structure has been studied numerically by assessing the influence of key structural subcomponents on the damage evolution of an artificial initial debonding between the composite skin and stringers
Large Notch Damage Evolution in Omega Stiffened Composite Panels
The aim of this work is the study of the influence of a large notch damage in a stiffened aeronautical panel. In particular, the damage onset and evolution due to a cut-out located in the bay of an omega stiffened composite panel subjected to a compressive load is investigated. Three different cut-outs are considered: parallel, normal, and 45° oriented respect to the load. The effects of such configurations are compared in terms of fibre and matrix failures, in order to better understand which configuration is the most sensitive to these type of damages
Acidente por injeção medicamentosa no mĂșsculo deltoide: lesĂ”es locais e Ă distĂąncia, revisĂŁo de 32 casos
Nicolau syndrome due to a traumatic finger injury with a needle : a case report with an exclusive photographic documentation
Characterization of the Impact Induced Damage in Composites by Cross-Comparison among Experimental Non Destructive Evaluation Techniques and Numerical Simulations
Composite fibre-reinforced materials, under low velocity impacts, can experience simultaneous interacting failure phenomena, such as intra-laminar damage, fibre breakage and matrix cracking, and inter-laminar damage such as delaminations. These failure mechanisms are usually the subject of extensive investigations because they can cause a significant reduction in strength of composites structures leading to premature failure. In the present work, composite plates under low velocity impact are investigated. Experimental data, such as experimental curves and images from non-destructive inspections, are used to characterise the low velocity impacts-induced damage in conjunction with a non-linear explicit Finite element numerical model. The adopted numerical model, implemented in the FE code (Abaqus/Explicit) by a user-defined material subroutine (VUMAT), has been demonstrated to be very effective in predicting the damage onset and evolution and, in general, able to correctly integrate the experimental data by providing useful information about the impact damage localisation and evolution