Preparation and performance of plasma/polymer composite coatings on magnesium alloy

A triplex plasma (NiCoCrAlHfYSi/Al2O3·13%TiO2)/polycaprolactone composite coating was successfully deposited on a Mg-1.2Ca alloy by a combination of atmospheric plasma spraying and dip-coating techniques. The NiCoCrAlHfYSi (MCrAlHYS) coating, as the first layer, contained a large number of voids, globular porosities, and micro-cracks with a thickness of 40-50 μm, while the Al2O3·13%TiO2 coating, as the second layer, presented a unique bimodal microstructure with a thickness of 70-80 μm. The top layer was a hydrophobic polymer, which effectively sealed the porosities of plasma layers. The results of micro-hardness and bonding strength tests showed that the plasma coating presented excellent hardness (870 HV) and good bonding strength (14.8 MPa). However, the plasma/polymer coatings interface exhibited low bonding strength (8.6 MPa). The polymer coating formed thick layer (100-110 μm) that homogeneously covered the surface of the plasma layers. Contact angle measurement showed that polymer coating over plasma layers significantly decreased surface wettability. The corrosion current density (icorr) of an uncoated sample (262.7 µA/cm2) decreased to 76.9 µA/cm2 after plasma coatings were applied. However, it was found that the icorr decreased significantly to 0.002 µA/cm2 after polymer sealing of the porous plasma layers

Immobilization of Eu and Ho from synthetic acid mine drainage by precipitation with Fe and Al (hydr)oxides

Use of lime to mitigate acid mine drainage is, in general, accompanied by precipitation of iron (Fe) and aluminium (Al) (hydr)oxides which may increase the removal of trace elements from water. This work aimed to evaluate the precipitation of Fe/Al (hydr)oxides to remove rare earth elements (REE) from contaminated water and the stability of precipitates. Two sets of 60-day syntheses were carried out using different Fe/Al/REE molar ratios, for europium (Eu) and holmium (Ho). The pH was periodically adjusted to 9.0, and the stability of the resulting precipitates was evaluated by water-soluble and BCR extractable phases, namely (1) acid soluble, extracted by 0.11\ua0mol\ua0L acetic acid; (2) reducible, extracted with 0.5\ua0mol\ua0L hydroxylamine hydrochloride; and (3) oxidisable, extracted with 8.8\ua0mol\ua0L hydrogen peroxide efficiencies of the water treatments for both Eu and Ho that were higher than 99.9% irrespective to the Fe/Al/REE molar ratios. Water-soluble phases of Eu and Ho were lower than 0.01% of the total contents in the precipitates. Recoveries from precipitates by Bureau Communautaire de Référence (BCR) sequential extractions increased with increasing concentrations of Eu and Ho. Acetic acid extracted higher amounts of REE, but Eu recovery was superior to Ho. Lepidocrocite was formed as Eu concentration increased which decreased its stability in the precipitates