Implications of pre-formed microcracking in relation to the theories of DEF mechanism

Abstract: Microcracks were induced in cementitious systems by freeze-thaw action and by alkali–silica reaction. These mechanisms often co-exist with delayed ettringite formation in concretes. Mortars and concretes were subjected to a heat treatment cycle consisting of a pre-set period of 4 h at 23 °C followed by accelerated curing at 95 °C. To isolate the mechanical effects of induced microcracking, heat-cured specimens were subjected to varied prescribed damage induced by freeze-thaw or alkali–silica reaction prior to the onset of delayed ettringite formation. It was found that inducement of pre-formed microcracks led to an earlier onset of expansion due to delayed ettringite formation. Initially, microcracks enhanced ultimate expansion until a certain relatively high extent of microcracking was reached. Thereafter, ultimate expansion decreased with any further increase in microcracking. This report gives support to the paste expansion theory

Dual effectiveness of lithium salt in controlling both delayed ettringite formation and ASR in concretes

Abstract: The influence of lithium nitrate on expansions due to delayed ettringite formation (DEF) and alkali-silica reaction (ASR) has been investigated. Effects of the lithium salt were examined in heat-cured mortars and concretes containing one or both damage mechanisms. The mortars and concretes made using reactive and/or non-reactive aggregates were subjected to heat treatment consisting of a hydration delay period of 4 hours at 23oC followed by steam-curing at 95oC and then stored in limewater. Results showed that the lithium salt admixture was able to reduce the occurrence of deleterious expansion due to delayed ettringite formation in addition to controlling alkali-silica reaction in cementitious systems containing one or both mechanisms. In concretes made using non-reactive limestone aggregates, incorporation of lithium nitrate in a proportion of 0.74 molar ratio of Li to (Na+K) was found to control delayed ettringite formation during the one-year period of this study. By analyzing the leaching properties of lithium and other alkalis from mortars during storage, it was found that a substantial amount of lithium was retained in the cementitious system in a slightly soluble form, and is expected to be responsible for reducing DEF