Low energy proton radiation damage to (AlGa)As-GaAs solar cells

Twenty-seven 2 times 2 sq cm (AlGa)As-GaAs solar cells were fabricated and subjected to 50 keV, 100 keV, and 290 keV of proton irradiation along with eighteen high efficiency silicon solar cells. The results of the study further corroborate the advantages for space missions offered by GaAs cells over state of the art silicon cells. Thus, even though the GaAs cells showed greater degradation when irradiated by protons with energy less than 5 MeV, the solar cells were normally protected from these protons by the glass covers used in space arrays. The GaAs cells also offered superior end of life power capability compared with silicon. The change in the open circuit voltage, short circuit current, spectral response, and dark 1-5 characteristics after irradiation at each proton energy and fluence were found to be consistent with the explanation of the effect of the protons. Also dark 1-5 characteristics showed that a new recombination center dominates the current transport mechanism after irradiation

Electron Radiation Damage of (alga) As-gaas Solar Cells

Solar cells (2 cm by 2 cm (AlGa) As-GaAs cells) were fabricated and then subjected to irradiation at normal incidence by electrons. The influence of junction depth and n-type buffer layer doping level on the cell's resistance to radiation damage was investigated. The study shows that (1) a 0.3 micrometer deep junction results in lower damage to the cells than does a 0.5 micrometer junction, and (2) lowering the n buffer layer doping density does not improve the radiation resistance of the cell. Rather, lowering the doping density decreases the solar cell's open circuit voltage. Some preliminary thermal annealing experiments in vacuum were performed on the (AlGa)As-GaAs solar cells damaged by 1-MeV electron irradiation. The results show that cell performance can be expected to partially recover at 200 C with more rapid and complete recovery occurring at higher temperature. For a 0.5hr anneal at 400 C, 90% of the initial power is recovered. The characteristics of the (AlGa)As-GaAs cells both before and after irradiation are described

Magellanic Cloud stars with TiO bands in emission: binary post-RGB/AGB stars or young stellar objects?

Fourteen stars from a sample of Magellanic Cloud objects selected to have a mid-infrared flux excess have been found to also show TiO bands in emission. The mid-infrared dust emission and the TiO band emission indicate that these stars have large amounts of hot circumstellar dust and gas in close proximity to the central star. The luminosities of the sources are typically several thousand L_sun while the effective temperatures are 4000-8000 K. Such stars could be post-AGB stars of mass 0.4-0.8 M_sun or pre-main-sequence stars (young stellar objects) with masses of 7-19 M_sun. If the stars are pre-main-sequence stars, they are substantially cooler and younger than stars at the birth line where Galactic protostars are first supposed to become optically visible out of their molecular clouds. They should therefore be hidden in their present evolutionary state. The second explanation for these stars is that they are post-AGB or post-RGB stars that have recently undergone a binary interaction when the red giant of the binary system filled its Roche lobe. Being oxygen-rich, they have gone through this process before becoming carbon stars. Most of the stars vary slowly on timescales of 1000 days or more suggesting a changing circumstellar environment. Apart from the slow variations, most stars also show variability with periods of tens to hundreds of days. One star shows a period that is rapidly decreasing and we speculate that this star may have accreted a large blob of gas and dust onto a disk whose orbital radius is shrinking rapidly. Another star has Cepheid-like pulsations of rapidly increasing amplitude suggesting a rapid rate of evolution. Seven stars show quasi-periodic variability and one star has a light curve similar to that of an eclipsing binary.Comment: 15 pages, 2 tables, 8 figures, MNRAS, in pres

Optically visible post-AGB/RGB stars and young stellar objects in the Small Magellanic Cloud: candidate selection, spectral energy distributions and spectroscopic examination

We have carried out a search for optically visible post-AGB candidates in the Small Magellanic Cloud (SMC). We used mid-IR observations from the Spitzer Space Telescope to select optically visible candidates with a mid-IR excess. We obtained low-resolution optical spectra for 801 candidates. After removing contaminants and poor quality spectra, the final sample comprised of 63 post-AGB/RGB candidates of A - F spectral type. Using the spectra, we estimated the stellar parameters: effective temperature, surface gravity and [Fe/H]. We also estimated the reddening and deduced the luminosity using the stellar parameters combined with photometry. Based on a luminosity criterion, 42 of these 63 sources were classified as post-RGB candidates and the remaining as post-AGB candidates. From the spectral energy distributions we found that 6 of the 63 post-AGB/RGB candidates have a circumstellar shell suggesting that they are single stars, while 27 of them have a surrounding disc, suggesting that they are binaries. For the remaining candidates the nature of the circumstellar environment was unclear. Variability is displayed by 38 post-AGB/RGB candidates with common variability types being the Population II Cepheids (including RV-Tauri stars) and semi-regular variables. This study has also revealed a new s-process enriched RV Tauri star (J005107.19-734133.3). From the numbers of post-AGB/RGB stars in the SMC, we were able to estimate evolutionary rates that are in good agreement with the stellar evolution models with mass loss in the post-AGB phase and re-accretion in the post-RGB phase. This study also resulted in a new sample of 40 luminous young stellar objects (YSOs) of A - F spectral type. Additionally, we also identified a group of 63 objects whose spectra are dominated by emission lines and in some cases, a UV continuum. These objects are likely to be either hot post-AGB/RGBs or luminous YSOs.Comment: 67 pages, 26 figures, 20 tables, 3 appendices + online supporting information on CD

Medium energy proton radiation damage to (AlGa)As-GaAs solar cells

The performance of (AlGa)As-GaAs solar cells irradiated by medium energy 2, 5, and 10 MeV protons was evaluated. The Si cells without coverglass and a number of GaAs solar cells with 12 mil coverglass were irradiated simultaneously with bare GaAs cells. The cell degradation is directly related to the penetration of depth of protons with GaAs. The influence of periodic and continuous thermal annealing on the GaAs solar cells was investigated

Ocular Surface Squamous Neoplasia in Xeroderma Pigmentosum

Xeroderma pigmentosum (XP) is a rare genetic disorder associated with multiple oculocutaneous and neurological manifestations. It occurs due to deficiency of the enzymes responsible for repairing ultraviolet radiation-induced DNA damage. Persistence of un-repaired DNA results in somatic mutations, leading to neoplasia of the skin and ocular surface. As this condition is rare, only isolated case reports of XP with ocular surface squamous neoplasia (OSSN) are found in literature

GaAs solar cells for concentrator systems in space

Cells for operation in space up to more than 100 suns were made, and an AMO efficiency of 21% at 100 suns with these cells was obtained. The increased efficiency resulted not only from the higher open circuit voltage associated with the higher light intensity (higher short circuit current); it also benefitted from the increase in fill factor caused by the lower relative contribution of the generation recombination current to the forward bias current when the cell's operating current density is increased. The experimental cells exhibited an AMO efficiency close to 16% at 200 C. The prospect of exploiting this capability for the continuous annealing of radiation damage or for high temperature missions (e.g., near Sun missions) remains therefore open. Space systems with concentration ratios on the order of 100 suns are presently under development. The tradeoff between increased concentration ratio and increased loss due to the cell's series resistance remains attractive even for space applications at a solar concentrator ratio of 100 suns. In the design of contact configuration with low enough series resistance for such solar concentration ratios, the shallow junction depth needed for good radiation hardness and the thin AlGaAs layer thickness needed to avoid excessive optical absorption losses have to be retained