Erection of a Stainless-Steel Tank for Storing a Phosphoric Acid

A storage tank for 93 % phosphoric acid was built in Luka Koper from 7 mm thick ground hot-rolled plates of 316L stainless steel. The capacity of the storage tank is of the 750 m3, diameter of 11 m and the height of 8,2 m. The shell plates were welded manually using the shielded metal-arc and gas-metal-arc processes. Before the erection, welding procedure tests according to EN 288-3 were carried out. During the construction several non-destructive examination methods were used, such as radiographic testing and visual and liquid penetrant examination. After the entire tank and roof structure were completed, a hydrostatic leak test was carried out. The surfaces of all the welds on the internal surface of the vessel were ground and the roughness was checked on site. The surfaces of the base material and the ground welds were passivated and tested for resistance to corrosion with electrochemical measurements

Pukotine na valjkastom ležaju

Bearings are among the most important components of electromotors, pumps, compressors and other processing equipment. After 30 years of work some non-destructive and metallographic examinations were carried out on a single-row cylindrical roller-bearing. A non-destructive liquid-penetrant testing revealed crack indications on an inner ring groove. When a sample of the roller-bearing outer ring was cut out for metallographic examination, new cracks were discovered that were not detected by the non-destructive testing. However, with the examination of the non-failed bearing it is possible to obtain useful information that can help us to decide how much of the remaining population of bearings with the same geometry and loading should be examined.Ležajevi su veoma značajne komponente elektromotora, crpki, kompresora i ostale procesne opreme. Na jednorednom valjkastom cilindričnom ležaju, koji je bio u pogonu 30 godina bile su izvedene kontrole bez razaranja i metalografska kontrola. Sa metodom tekućih pentranata su se otkrile indikacije pukotina u žlijebu unutrašnjeg prstena. Kada je bio iz vanjskog prstena uzet uzorak za metalografsko ispitivanje otkrivene su bile nove pukotine, koje nisu bile detektirane kontrolom bez razaranja. Sa ispitivanjem ležaja koji nije otkazao tako je moguće dobiti korisne informacije, koje nam mogu pomoći o odluci koliki će biti broj ispitanih ležajeva između ostale populacije s jednakom geometrijom i opterećenjem

Erection of a Stainless-Steel Tank for Storing a Phosphoric Acid

A storage tank for 93 % phosphoric acid was built in Luka Koper from 7 mm thick ground hot-rolled plates of 316L stainless steel. The capacity of the storage tank is of the 750 m3, diameter of 11 m and the height of 8,2 m. The shell plates were welded manually using the shielded metal-arc and gas-metal-arc processes. Before the erection, welding procedure tests according to EN 288-3 were carried out. During the construction several non-destructive examination methods were used, such as radiographic testing and visual and liquid penetrant examination. After the entire tank and roof structure were completed, a hydrostatic leak test was carried out. The surfaces of all the welds on the internal surface of the vessel were ground and the roughness was checked on site. The surfaces of the base material and the ground welds were passivated and tested for resistance to corrosion with electrochemical measurements

Utjecaj olova na toplo preoblikovanje austenitnog nehrđajućeg čelika s lijevanom strukturom

The impurities sulphur, phosphorus, lead, bismuth, tin and antimony affect the hot workability of stainless steels. In this study we show that lead segregate to phase and solidification-grain boundaries, where cracks appear during hot deformation. The workability was tested by the hot bending of laboratory steels.Nečistoće poput sumpora, fosfora, olova, bizmuta i antimona negativno utječu na toplo preoblikovanje nehrđajućih čelika. U ovaj je studiji pokazano, da olovo segregira na granicama zrna skrućivanja gdje se mogu pojaviti pukotine za vrijeme tople deformacije. Toplo preoblikovanje laboratorijski dobivenih čelika ispitano je metodom toplog savijanja

Utjecaj olova na toplo preoblikovanje austenitnog nehrđajućeg čelika s lijevanom strukturom

The impurities sulphur, phosphorus, lead, bismuth, tin and antimony affect the hot workability of stainless steels. In this study we show that lead segregate to phase and solidification-grain boundaries, where cracks appear during hot deformation. The workability was tested by the hot bending of laboratory steels.Nečistoće poput sumpora, fosfora, olova, bizmuta i antimona negativno utječu na toplo preoblikovanje nehrđajućih čelika. U ovaj je studiji pokazano, da olovo segregira na granicama zrna skrućivanja gdje se mogu pojaviti pukotine za vrijeme tople deformacije. Toplo preoblikovanje laboratorijski dobivenih čelika ispitano je metodom toplog savijanja

Proces Charpy prijeloma u duktilnom području

The fracturing of structural steels in Charpy ductile range is investigated. The dependences load versus deflection and time were recorded and the consumption of energy for different fracturing events, as f.i. plastic deflection and crack propagation was assessed. The micromorphology of the crack surface and lips is examined and the succesions of decohesion mechanims is deduced. The aproximate change of fracturing temperature due to adiabatic dissipation of deformation energy as heat is deduced, also.Proces Charpy prijeloma u duktilnom području. Izražen je proces Charpy prijeloma u duktilnom području. Određene su ovisnosti sila-savijanja i sila-vrijeme te potrošnja energije za različite faze prijeloma, npr. plastično savijanje i propagacija pukotine. Ispitna je mikromorfologija površine prijeloma i određen je redosljed mehanizama dekohezije. Izračunata je promjena temperature prijeloma glede adiabatske pretvorbe deformacijske energije u toplinu

Crescimento vegetativo e produção em função da razão área foliar/fruto em diferentes posições da copa do cafeeiro.

Neste trabalho, nas safras 2006-2007 e 2007-2008, foi avaliado o crescimento dos ramos em plantas de café cultivadas em renques orientados na posição norte-sul em ramos plagiotrópicos com três razões área foliar/fruto (RAF) nas posições leste inferior (LI), leste superior (LS), oeste inferior (OI) e oeste superior (OS) da copa das plantas . Adicionalmente, em cada posição e em cada face de orientação, foi avaliada a produção de frutos nas safras 2006-2007, 2007-2008 e 2008-2009. Pode-se observar a competição entre o crescimento vegetativo e reprodutivo, tendo em vista que os ramos com menor RAF apresentaram menor crescimento na safra 2006-2007. A produção de frutos não apresentou o padrão de bienalidade do cafeeiro nas faces de posição na copa, e maiores produções nas safras 2006-2007 e 2008-2009. Verificou-se maior produção na face leste, o que pode estar associado a maior disponibilidade de luz naquela posição

Relação da morte de ramos com a razão área foliar por fruto, crescimento vegetativo e produção em diferentes posições da copa do cafeeiro.

Neste trabalho, o objetivo foi avaliar a correlação entre a ?morte de ramos? e a razão área foliar por fruto, taxa de crescimento e produção de frutos em ramos de Coffea arabica L. cv. Catuaí Vermelho ? IAC 99, cultivado a campo. Para isso foram selecionadas 30 plantas de café cultivadas em renques orientados na posição norte-sul, e nelas selecionados 24 ramos com três razões de área foliar por fruto nas posições leste inferior, leste superior, oeste inferior e oeste superior da copa das plantas. O ensaio foi realizado na safra 2006-2007. Em cada posição foi realizado o acompanhamento do crescimento de ramos, da produção de frutos nos ramos e do número de ramos mortos. Foram estimadas as correlações entre a ?morte de ramos? e as variáveis: área foliar por fruto, taxa de crescimento dos ramos, produção total de frutos, produção de frutos normais e produção de frutos-bóia. Observou-se que, à medida que aumenta a razão da área foliar por fruto, ocorre aumento da taxa de crescimento de ramos, redução da produção de frutos-bóias e redução do número de ramos mortos

A915.34.01.08- melon line resistant to leafminer (Liriomyza sativae).

Made available in DSpace on 2018-10-25T00:54:37Z (GMT). No. of bitstreams: 1 ART18066.pdf: 707023 bytes, checksum: 7c8b614201c4591beeab4d7e53d52810 (MD5) Previous issue date: 2018-10-23bitstream/item/185054/1/ART18066.pd

Atividade de enzimas do metabolismo do carbono em função da razão área foliar/frutos em diferentes posições da copa do cafeeiro.

Neste trabalho, em março de 2007 foram coletados tecidos foliares em ramos plagiotrópicos com três razões área foliar/fruto (RAF) de plantas de café cultivadas em renques orientados norte-sul nas posições leste inferior, leste superior, oeste inferior e oeste superior da copa das plantas, enquanto em 2008 foram coletados tecidos foliares em ramos plagiotrópicos em apenas uma RAF. Foi determinada a atividade das enzimas da sintase da sacarose-fosfato-SPS, pirofosforilase da ADP-glicose-AGPase, invertase ácida e sintase da sacarose-Susy. Adicionalmente, não foi observado um padrão claro de resposta das atividades das enzimas AGPase, invertase, SuSy e SPS em 2007. Em 2008, por outro lado, observou-se tendência de menores atividades das enzimas supracitadas nas folhas da posição leste inferior, fato que pode estar associado com menor taxa de fotossíntese ao longo do dia, provavelmente em função de uma menor disponibilidade de luz nessa face