Structural Evaluation and Performance of Portland Cement Concretes After Exposure to High Temperatures

We evaluated the "residual" thermal conductivity of Portland cement concretes (with characteristic compressive strength at 28 days, f ck, of 20 MPa and 50 MPa) at room temperature after heat-treating at 180 °C, 300 °C and 600 °C. The description of the geometry of the structure was carried out using mercury intrusion porosimetry and nitrogen sorption. The results showed a decreasing tendency of residual thermal conductivity, which we attributed to heat-induced concrete degradation. Furthermore, the results from mercury intrusion porosimetry and nitrogen sorption tests showed that a coarser pore structure is produced with the raise of heat-treatment temperatures

Carbonation-Related Microstructural Changesin Long-Term Durability Concrete

This paper discusses the effects of carbonation on the microstructure of Portland cement concrete for long-term durability applications. A class C40 concrete (characteristic compression strength between 40 MPa and 44 MPa on the 28th day, according to Brazilian standard NBR 8953) was chosen for the experimental study of the carbonation effects, from which test samples were molded for accelerated test under a 100%-CO2 atmosphere after physical and mechanical characterization. It was observed that carbonation provoked a reduction of 5% to 12% of the concrete open porosity accessible to water. Flexural strength values obtained after the carbonation tests revealed a decrease of 12% and 25% in relation to the values obtained before tests on the 28th and 91st days, respectively