Influence of thermal and mechanical cycling on the flexural strength of ceramics with titanium or gold alloy frameworks

Objectives. The aim of this study was to evaluate the effect of thermal and mechanical cycling alone or in combination, on the flexural strength of ceramic and metallic frameworks cast in gold alloy or titanium. Methods. Metallic frameworks (25 mm x 3 mm x 0.5 mm) (N = 96) cast in gold alloy or commercial pure titanium (Ti cp) were obtained using acrylic templates. They were airborne particle-abraded with 150 mu m aluminum oxide at the central area of the frameworks (8 mm x 3 mm). Bonding agent and opaque were applied on the particle-abraded surfaces and the corresponding ceramic for each metal was fired onto them. The thickness of the ceramic layer was standardized by positioning the frameworks in a metallic template (height: I mm). The specimens from each ceramic-metal combination (N = 96, n = 12 per group) were randomly assigned into four experimental fatigue conditions, namely water storage at 37 degrees C for 24 h (control group), thermal cycling (3000 cycles, between 4 and 55 degrees C, dwell time: 10 s), mechanical cycling (20,000 cycles under 10 N load, immersion in distilled water at 37 degrees C) and, thermal and mechanical cycling. A flexural strength test was performed in a universal testing machine (crosshead speed: 1.5 mm/min). Data were statistically analyzed using two-way ANOVA and Tukey`s test (alpha = 0.05). Results. The mean flexural strength values for the ceramic-gold alloy combination (55 +/- 7.2MPa) were significantly higher than those of the ceramic-Ti cp combination (32 +/- 6.7 MPa) regardless of the fatigue conditions performed (p < 0.05). Mechanical and thermo-mechanical fatigue decreased the flexural strength results significantly for both ceramic-gold alloy (52 +/- 6.6 and 53 +/- 5.6 MPa, respectively) and ceramic-Ti cp combinations (29 +/- 6.8 and 29 +/- 6.8 MPa, respectively) compared to the control group (58 +/- 7.8 and 39 SA MPa, for gold and Ti cp, respectively) (p < 0.05) (Tukey`s test). While ceramic-Ti cp combinations failed adhesively at the metal-opaque interface, gold alloy frameworks exhibited a residue of ceramic material on the surface in all experimental groups. Significance. Mechanical and thermo-mechanical fatigue conditions decreased the flexural strength values for both ceramic-gold alloy and ceramic-Ti cp combinations with the results being significantly lower for the latter in all experimental conditions. (C) 2007 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved

Effect of mechanical cycling on the flexural strength of densely sintered ceramics

Objectives. The aim of this study was to evaluate the effect of mechanical cycling on the biaxial flexural strength of two densely sintered ceramic materials. Methods. Disc shaped zirconia (In-Ceram Zirconia) and high alumina (Procera AllCeram) ceramic specimens (diameter: 15 min and thickness: 1.2 mm) were fabricated according to the manufacturers' instructions. The specimens from each ceramic material (N = 40, n = 10/per group) were tested for flexural strength either with or without being subjected to mechanical cycling (20,000 cycles under 50 N load, immersion in distilled water at 37 degrees C) in a universal testing machine (1 mm/min). Data were statistically analyzed using two-way ANOVA and Tukey's test (alpha = 0.05). Results. High alumina ceramic specimens revealed significantly higher flexural strength values without and with mechanical cycling (647 +/- 48 and 630 +/- 143 MPa, respectively) than those of zirconia ceramic (497 +/- 35 and 458 +/- 53 MPa, respectively) (p <0.05). Mechanical cycling for 20,000 times under 50 N decreased the flexural strength values for both high alumina and Significance. High alumina ceramic revealed significantly higher mean flexural strength values than that of zirconia ceramic tested in this study either with or without mechanical cycling conditions. (C) 2005 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved

Influência do agente de união na resistência ao cisalhamento da interface titânio/polímero de vidro

There is little information regarding bond strengths of polyglass to metal alloys. This study evaluated the influence of bonding system on shear bond strength of a composite resin (Artglass/Heraeus Kulzer) to cast titanium (Ti). Twenty metallic structures (4mm in diameter, 5mm thick) of titanium grade I were cast shaped and abraded with 250mm aluminum oxide and separated into two groups. For each group was applied one bonding system (Siloc or Retention Flow) before opaque and dentin polymer superposition. This procedure was managed using teflon matrices. They were manipulated and polymerized according to the manufacturer's recommendations. The samples were stored in distilled water for 24 hours at 37º and thermocycled (5º and 55ºC/500 cycles). Shear bond strength tests were performed by using an Instron Universal testing machine at a crosshead speed of 5mm/min. Results were analyzed statistically with one-way ANOVA (a=0,5) and they indicated that the Retention Flow system was statistically better than Siloc (20.74 MPa and 11.65 MPa , respectively). It was possible to conclude that the bonding agent influenced the adhesion between polymer and cast titanium.Há poucas informações em relação à efetividade da união entre compósitos e superfícies metálicas. Este estudo avaliou a influência de dois agentes de união na resistência ao cisalhamento da interface formada pelo titânio comercialmente puro (Ti cp) e um compósito (Artglass/ Heraeus Kulzer). Vinte estruturas metálicas (4mm de diâmetro e 5mm de altura) de titânio grau 1 foram fundidas, jateadas com partículas de óxido de alumínio (250ìm) e separadas em dois grupos. Para cada grupo foi utilizado um agente de união (Sistema Siloc-Pre ou Retention Flow) como procedimento anterior à aplicação do material opaco. Sobre este foram aplicados camadas do polímero referente à dentina com o auxílio de uma matriz de teflon. A manipulação e polimerização foram realizadas de acordo com as recomendações do fabricante. Os corpos-de-prova foram armazenados em água destilada por 24 horas à 37ºC e termociclados (5º e 55ºC/ 500ciclos). O teste de resistência ao cisalhamento foi realizado em uma máquina de ensaios universal (Instron) com velocidade de 5mm/min. Os dados foram tratados estatisticamente pela Análise de Variância one-way (á=0,5). Os resultados indicaram que o sistema adesivo Retention Flow foi estatisticamente melhor do que o Siloc, com médias de 20,74MPa e 11,65MPa, respectivamente. Foi possível concluir que o sistema de união influenciou na adesão entre o titânio grau I e o polímero de vidro estudado

Avaliação da albuminúria e da eletroforese de proteínas urinárias de cães com hiperadrenocorticismo e a relação com a pressão arterial sistêmica

O hiperadrenocorticismo é uma das endocrinopatias mais comuns em cães, sendo caracterizado pela exposição excessiva de glicocorticóides secretados pelas adrenais. A hipercortisolemia crônica pode promover várias complicações, incluindo hipertensão sistêmica e glomerulonefrite. A glomerulonefrite pode desencadear variáveis graus de proteinúria e uma tendência de evolução para doença renal crônica. A perda de proteínas na urina, principalmente da albumina, é uma característica das doenças glomerulares e a determinação de variáveis laboratoriais, como a razão proteína:creatinina urinária (RPC), albuminúria (teste de ELISA) e eletroforese das proteínas urinárias, são recomendadas para a elucidação do diagnóstico. Assim, o objetivo do estudo é avaliar a relação entre proteinúria e hipertensão arterial sistêmica em cães com hiperadrenocorticismo e verificar, pela avaliação da albuminúria e do peso molecular das proteínas urinárias, o segmento do néfron que foi comprometido ou lesado. Foram avaliados 30 cães com diagnóstico de hiperadrenocorticismo, subdivididos em 13 cães com hipertensão arterial sistêmica (grupo I) e 17 cães normotensos (grupo II). Foram determinados a RPC; a albuminúria pela avaliação da albumina normalizada e razão albumina:creatinina urinária (RAC) e a eletroforese de proteínas pela técnica em gel de poliacrilamida, contendo dodecil sulfato de sódio (SDS-PAGE). Os resultados foram comparados com os dados obtidos de 30 cães clinicamente saudáveis. Foi constatado que não houve influência da hipertensão arterial sistêmica nos cães com hiperadrenocorticismo em relação à quantificação da albuminúria, determinada pelo método ELISA, e nem na qualidade e quantidade das bandas de proteínas de baixo (<60 kDa) e de alto peso molecular (>60 kDa). No entanto foi determinado que cães com hiperadrenocorticismo podem desenvolver lesões glomerulares e tubulares, caracterizadas pela presença de albuminúria e de proteínas de alto e de baixo pesos moleculares, independentemente da presença de hipertensão arterial sistêmica. Conclui-se que a avaliação quantitativa (RPC e RAC) e qualitativa (SDS-PAGE) das proteínas urinárias traz informações adicionais que indicam os possíveis segmentos comprometidos dos néfrons que causaram as perdas de proteínas na urina