Electron tomography of (In,Ga)N insertions in GaN nanocolumns grown on semi-polar (112̄ 2) GaN templates

We present results of scanning transmission electron tomography on GaN/(In,Ga)N/GaN nanocolumns (NCs) that grew uniformly inclined towards the patterned, semi-polar GaN( 11 2 ̄ 2 ) substrate surface by molecular beam epitaxy. For the practical realization of the tomographic experiment, the nanocolumn axis has been aligned parallel to the rotation axis of the electron microscope goniometer. The tomographic reconstruction allows for the determination of the three-dimensional indium distribution inside the nanocolumns. This distribution is strongly interrelated with the nanocolumn morphology and faceting. The (In,Ga)N layer thickness and the indium concentration differ between crystallographically equivalent and non-equivalent facets. The largest thickness and the highest indium concentration are found at the nanocolumn apex parallel to the basal planes

Oxygen-deficient oxide growth by subliming the oxide source material: The cause of silicide formation in rare earth oxides on silicon

The fundamental issue of oxygen stoichiometry in oxide thin film growth by subliming the source oxide is investigated by varying the additionally supplied oxygen during molecular beam epitaxy of RE2O3 (RE = Gd, La, Lu) thin films on Si(111). Supplying additional oxygen throughout the entire growth was found to prevent the formation of rare earth silicides observed in films grown without an oxygen source. Postgrowth vacuum annealing of oxygen stoichiometric films did not lead to silicide formation thereby confirming that the silicides do not form as a result of an interface instability at growth temperature in vacuum but rather due to an oxygen deficiency in the source vapor. The average oxygen deficiency of the rare-earth containing species in the source vapor was quantified by the 18O tracer technique and correlated with that of the source material, which gradually decomposed during sublimation. Therefore, any oxide growth by sublimation of the oxide source material requires additional oxygen to realize oxygen stoichiometric films

Electron tomography of (In,Ga)N insertions in GaN nanocolumns grown on semi-polar (11(2)over-bar2) GaN templates

We present results of scanning transmission electron tomography on GaN/(In,Ga)N/GaN nanocolumns (NCs) that grew uniformly inclined towards the patterned, semi-polar GaN( 112̄ 2 ) substrate surface by molecular beam epitaxy. For the practical realization of the tomographic experiment, the nanocolumn axis has been aligned parallel to the rotation axis of the electron microscope goniometer. The tomographic reconstruction allows for the determination of the three-dimensional indium distribution inside the nanocolumns. This distribution is strongly interrelated with the nanocolumn morphology and faceting. The (In,Ga)N layer thickness and the indium concentration differ between crystallographically equivalent and non-equivalent facets. The largest thickness and the highest indium concentration are found at the nanocolumn apex parallel to the basal planes

Delayed crystallization of ultrathin Gd2O3 layers on Si(111) observed by in situ X-ray diffraction

We studied the early stages of Gd2O3 epitaxy on Si(111) in real time by synchrotron-based, high-resolution X-ray diffraction and by reflection high-energy electron diffraction. A comparison between model calculations and the measured X-ray scattering, and the change of reflection high-energy electron diffraction patterns both indicate that the growth begins without forming a three-dimensional crystalline film. The cubic bixbyite structure of Gd2O3 appears only after a few monolayers of deposition

On the origin of defects during III-Sb epitaxy on Si(001)

International audienc