4 research outputs found
The effective role of alkali earth/alkali ratio on formation HCA nano particles for soda lime phospho silicate glass system
In the present work, we report on the effect of the CaO/Na2O ratio on Non-Bridging Oxygen/Bridging Oxygen (NBO/BO) ratio for sol-gel synthesised 58SiO2-(38-x)CaO-xNa2O-4P2O5 glasses and establish the correlation between Hydroxy Carbonated Apatite layer (HCA) forming ability and the dissolution behaviour in simulated body fluid (SBF) solution. Thermal stabilities were calculated as 221, 135, 153 and 77 °C respectively. It is inferred that thermal stabilities varied nonlinearly with CaO/Na2O ratio. Similarly NBO/BO ratios were obtained using Raman spectroscopic analysis as 0.6293, 0.7917, 0.2264 and 0.3513, respectively. All samples were soaked in the SBF solution for 7 days. The calculated weight losses of these samples were 55.32, 69.13, 18.09 and 20.08 for the corresponding NBO/BO ratios. The decrease in CaO/ Na2O ratio led to nonlinear variation of the NBO/BO ratios. Consequently the non linear variation in NBO/BO ratio led to the nonlinear variation of HCA forming ability of SBF treated samples
Effective role of CaO/P2O5 ratio on SiO2-CaO-P2O5 glass system
In the present work, the effect of the CaO/P2O5 ratio on the composition of sol-gel synthesized 58SiO2-(19 − x)P2O5–(23 + x)CaO (x = 0, 5, 10 and 15 mol%) glass samples was studied. Further, the effect of NBO/BO ratio on hydroxy carbonated apatite layer (HCA) forming ability based on dissolution behavior in simulated body fluid (SBF) solution was also investigated. CaO/P2O5 ratios of synthesized glass samples were 1.2, 2, 3.6, and 9.5, respectively. NBO/BO ratios were obtained using Raman spectroscopic analysis as 0.58, 1.20, 1.46, and 1.78, respectively. All samples were soaked in the SBF solution for 7 days. The calculated weight losses of these samples were 58%, 64%, 83%, and 89% for corresponding NBO/BO ratios. The increase in CaO/P2O5 ratio increases the NBO/BO ratios. However, the increase in NBO/BO ratio increases HCA forming ability of SBF treated samples. The HCA crystalline layer formation was confirmed through X-ray Diffraction (XRD), Transmission Electron Microscopy (TEM), Scanning Electron Microscopy (SEM), Raman and Infrared spectroscopic analysis. Higher CaO/P2O5 ratio favors the increase in HCA formation for SBF treated calcium phospho silicate glasses