The effect of SU-8 patterned surfaces on the response of the quartz crystal microbalance

In this work we present data showing the effect of patterning layers of SU-8 photoresist on a quartz crystal microbalance (QCM) and subsequent chemical treatment to increase their hydrophobicity. Patterns with 5 mu m diameter pillars spaced every 10 mu m have been fabricated with heights of 3, 5 and 10 mu m in addition to equivalent thickness flat layers. Contact angle measurements have been made before and after the hydrophobic chemical treatment. The change in resonant frequency of the QCM has been investigated as the surfaces were submerged in solutions of water/PEG with changing viscosity-density product

Super-hydrophobic transparent surface by femtosecond laser micro-patterned catalyst thin film for carbon nanotube cluster growth

10.1007/s00339-010-5887-6Applied Physics A: Materials Science and Processing1013503-508APAM

Investigation on the effects of milling atmosphere on synthesis of barium ferrite/magnetite nanocomposite

In this research, barium ferrite /magnetite nanocomposites synthesized via a mechano-chemical route. Graphite was used in order to reduce hematite content of barium ferrite to magnetite to produce a magnetic nanocomposite. The effects of processing conditions on the powder characteristics were investigated by XRD, VSM, and HRTEM techniques. XRD results revealed that milling under air and argon atmospheres resulted in the appearance of Fe3O4 peaks beside BaFe12O19 peaks after 15 and 20 hrs milling, respectively. The intensity of Fe3O4 peaks in the XRD patterns increased by increasing the milling time. VSM studies revealed that saturation magnetization of the 40-hrs milled samples under air and argon atmospheres was 31.25 and 36.42 emu/g, respectively. This difference might be due to more Fe3O4 content in the latter sample. By annealing of the 40-hrs milled sample in air, saturation magnetization increased to 139.12 emu/g.Nanostructured MaterialsApplied Science