Application of a criterion for cold cracking to casting high strength aluminum alloys

Direct chill (DC) casting of high strength 7xxx series aluminium alloys is difficult mainly due to solidification cracking (hot cracks) and solid state cracking (cold cracks). Poor thermal properties along with extreme brittleness in the as-cast condition make DC-casting of such alloys a challenging process. Therefore, a criterion that can predict the catastrophic failure and cold cracking of the ingots would be highly beneficial to the aluminium industry. The already established criteria are dealing with the maximum principal stress component in the ingot and the plane strain fracture toughness (KIc) of the alloy under discussion. In this research work such a criterion was applied to a typical 7xxx series alloy which is highly prone to cold cracking. The mechanical properties, constitutive parameters, as well as the KIc values of the alloy were determined experimentally in the genuine as-cast condition and used as input data for the finite element package ALSIM5. Thermomechanical simulations were run for billets of various diameters and the state of residual thermal stresses was determined. Following the contour maps of the critical crack size gained from the model, the casting conditions were optimized to produce a crack-free billet.Materials Science & EngineeringMechanical, Maritime and Materials Engineerin

Cold cracking in DC-cast high strength aluminum alloy ingots: An intrinsic problem intensified by casting process parameters

For almost half a century the catastrophic failure of direct chill (DC) cast high strength aluminum alloys has been challenging the production of sound ingots. To overcome this problem, a criterion is required that can assist the researchers in predicting the critical conditions which facilitate the catastrophic failure of the ingots. This could be achieved at first glance by application of computer simulations to assess the level and distribution of residual thermal stresses. However, the simulation results are only able to show the critical locations and conditions where and when high stresses may appear in the ingots. The prediction of critical void/crack size requires simultaneous application of fracture mechanics. In this paper, we present the thermo-mechanical simulation results that indicate the critical crack size distribution in several DC-cast billets cast at various casting conditions. The simulation results were validated upon experimental DC-casting trials and revealed that the existence of voids/cracks with a considerable size is required for cold cracking to occur.Materials Science & EngineeringMechanical, Maritime and Materials Engineerin