Double-Network Hydrogels Strongly Bondable to Bones by Spontaneous Osteogenesis Penetration

Implanting hydroxyapatite-mineralized tough hydrogel into osteochondral defects of rabbits, osteogenesis spontaneously penetrates into the gel matrix owing to the semi-permeablility of the hydrogel. The gradient layer (around 40 μm thick) contributes quite strong bonding of the gel to bone. This is the first success in realizing the robust osteointegration of tough hydrogels, and the method is simple and feasible for practical use

バイオミメティック超構造を有する生体高分子ゲルの創製 [全文の要約]

この博士論文全文の閲覧方法については、以下のサイトをご参照ください。【担当：理学部図書室】https://www.lib.hokudai.ac.jp/dissertations/copy-guides

Double-Hydrophobic-Coating through Quenching for Hydrogels with Strong Resistance to Both Drying and Swelling

In recent years, various hydrogels with a wide range of functionalities have been developed. However, owing to the two major drawbacks of hydrogels—air-drying and water-swelling—hydrogels developed thus far have yet to achieve most of their potential applications. Herein, a bioinspired, facile, and versatile method for fabricating hydrogels with high stability in both air and water is reported. This method includes the creation of a bioinspired homogeneous fusion layer of a hydrophobic polymer and oil in the outermost surface layer of the hydrogel via a double-hydrophobic-coating produced through quenching. As a proof-of-concept, this method is applied to a polyacrylamide hydrogel without compromising its mechanical properties. The coated hydrogel exhibits strong resistance to both drying in air and swelling in multiple aqueous environments. Furthermore, the versatility of this method is demonstrated using different types of hydrogels and oils. Because this method is easy to apply and is not dependent on hydrogel surface chemistry, it can significantly broaden the scope of next-generation hydrogels for real-world applications in both wet and dry environments

Double‐Hydrophobic‐Coating through Quenching for Hydrogels with Strong Resistance to Both Drying and Swelling

In recent years, various hydrogels with a wide range of functionalities have been developed. However, owing to the two major drawbacks of hydrogels—air-drying and water-swelling—hydrogels developed thus far have yet to achieve most of their potential applications. Herein, a bioinspired, facile, and versatile method for fabricating hydrogels with high stability in both air and water is reported. This method includes the creation of a bioinspired homogeneous fusion layer of a hydrophobic polymer and oil in the outermost surface layer of the hydrogel via a double-hydrophobic-coating produced through quenching. As a proof-of-concept, this method is applied to a polyacrylamide hydrogel without compromising its mechanical properties. The coated hydrogel exhibits strong resistance to both drying in air and swelling in multiple aqueous environments. Furthermore, the versatility of this method is demonstrated using different types of hydrogels and oils. Because this method is easy to apply and is not dependent on hydrogel surface chemistry, it can significantly broaden the scope of next-generation hydrogels for real-world applications in both wet and dry environments

Swim bladder collagen forms hydrogel with macroscopic superstructure by diffusion induced fast gelation

Marine collagen has been attracting attention as a medical material in recent times due to the low risk of pathogen infection compared to animal collagen. Type I collagen extracted from the swim bladder of Bester sturgeon fish has excellent characteristics such as high denaturation temperature, high solubility, low viscosity and an extremely fast rate to form large bundle of fibers under certain conditions. These specific characteristics of swim bladder collagen (SBC) permit us to create stable, disk shaped hydrogels with concentric orientation of collagen fibers by the controlled diffusion of neutral buffer through collagen solution at room temperature. However, traditionally used animal collagens, e.g. calf skin collagen (CSC) and porcine skin collagen (PSC), could not form any stable and oriented structure by this method. The mechanism of the superstructure formation of SBC by a diffusion induced gelation process has been explored. The fast fibrillogenesis rate of SBC causes a quick squeezing out of the solvent from the gel phase to the sol phase during gelation, which builds an internal stress at the gel-sol interface. The tensile stress induces the collagen molecules of the gel phase to align along the gel-sol interface direction to give this concentric ring-shaped orientation pattern. On the other hand, the slow fibrillogenesis rate of animal collagens due to the high viscosity of the solution does not favor the ordered structure formation. The denaturation temperature of SBC increases significantly from 31 degrees C to 43 degrees C after gelation, whereas that of CSC and PSC were found to increase a little. Rheology experiment shows that the SBC gel has storage modulus larger than 15 kPa. The SBC hydrogels with thermal and mechanical stability have potential as bio-materials for tissue engineering applications