Study of metal drilling solves problems of excessive burring, oversized holes, and out-of-round holes. Recommendations deal with using the proper chemical coolants, applying the coolants effectively, employing cutting oils, and dissipating the heat caused by drilling
An evaluation of the effects of stacking sequence and thickness on the fatigue life of quasi-isotropic graphite/epoxy laminates
Notched and unnotched geometries at 16, 32, and 64-ply thicknesses of a 90/45/0-45 (ns) laminate and a 45/0/-45/90 (ns) laminate were tested in compression-compression fatigue. The fatigue life and the initiation, type, and progression of damage were determined. Interlaminar stresses generated at straight, free edges of axially loaded laminates were used to interpret the test results. The fatigue lives of the notched specimens did not appear to be a strong function of laminate stacking sequence or specimen thickness. The stress concentration at the hole dominated over the interlaminar stresses at the straight free edge. The unnotched specimens of the 90/45/0/-45 (ns) laminate with tensile interlaminar normal stresses delaminated more readily than did the 45/0/-45/90 (ns) laminate with compressive interlaminar normal stress. The life of the 16-ply unnotched specimens was lower than the 32- and 64-ply specimens. Delaminations were located at the interface where the maximum shear stress occurred regardless of the sense or magnitude of the interlaminar normal stress. An antibuckling fixture was effective in preventing out-of-plane motion without overconstraining the specimen
Fracture behavior of thick, laminated graphite/epoxy composites
The effect of laminate thickness on the fracture behavior of laminated graphite epoxy (T300/5208) composites was studied. The predominantly experimental research program included the study of the 0/+ or - 45/90 sub ns and 0/90 sub ns laminates with thickness of 8, 32, 64, 96 and 120 plies and the 0/+ or - 45 sub ns laminate with thickness of 6, 30, 60, 90 and 120 plies. The research concentrated on the measurement of fracture toughness utilizing the center-cracked tension, compact tension and three point bend specimen configurations. The development of subcritical damage at the crack tip was studied nondestructively using enhanced X-ray radiography and destructively using the laminate deply technique. The test results showed fracture toughness to be a function of laminate thickness. The fracture toughness of the 0 + or - 45/90 sub ns and 0/90 sub ns laminates decreased with increasing thickness and asymptotically approached lower bound values of 30 ksi square root of in. (1043 MPa square root of mm and 25 ksi square root of in (869 MPa square root of mm respectively. In contrast to the other two laminates, the fracture toughness of the 0/+ or - 45 sub ns laminate increased sharply with increasing thickness but reached an upper plateau value of 40 ksi square root of in (1390 MPa square root of mm) at 30 plies. Fracture toughness was independent of crack size for both thin and thick laminates for all three laminate types except for the 0/90 sub 2s laminate which spilt extensively. The center cracked tension, three point bend and compact tension specimens gave comparable results
Models of dynamic extraction of lipid tethers from cell membranes
When a ligand that is bound to an integral membrane receptor is pulled, the
membrane and the underlying cytoskeleton can deform before either the membrane
delaminates from the cytoskeleton or the ligand detaches from the receptor. If
the membrane delaminates from the cytoskeleton, it may be further extruded and
form a membrane tether. We develop a phenomenological model for this processes
by assuming that deformations obey Hooke's law up to a critical force at which
the cell membrane locally detaches from the cytoskeleton and a membrane tether
forms. We compute the probability of tether formation and show that they can be
extruded only within an intermediate range of force loading rates and pulling
velocities. The mean tether length that arises at the moment of ligand
detachment is computed as are the force loading rates and pulling velocities
that yield the longest tethers.Comment: 16 pages, 7 figure
Surface crack analysis applied to impact damage in a thick graphite-epoxy composite
The residual tensile strength of a thick graphite/epoxy composite with impact damage was predicted using surface crack analysis. The damage was localized to a region directly beneath the impact site and extended only part way through the laminate. The damaged region contained broken fibers, and the locus of breaks in each layer resembled a crack perpendicular to the direction of the fibers. In some cases, the impacts broke fibers without making a visible crater. The impact damage was represented as a semi-elliptical surface crack with length and depth equal to that of the impact damage. The maximum length and depth of the damage were predicted with a stress analysis and a maximum shear stress criterion. The predictions and measurements of strength were in good agreement
Lewis Research Center spin rig and its use in vibration analysis of rotating systems
The Lewis Research Center spin rig was constructed to provide experimental evaluation of analysis methods developed under the NASA Engine Structural Dynamics Program. Rotors up to 51 cm (20 in.) in diameter can be spun to 16,000 rpm in vacuum by an air motor. Vibration forcing functions are provided by shakers that apply oscillatory axial forces or transverse moments to the shaft, by a natural whirling of the shaft, and by an air jet. Blade vibration is detected by strain gages and optical blade-tip motion sensors. A variety of analogy and digital processing equipment is used to display and analyze the signals. Results obtained from two rotors are discussed. A 56-blade compressor disk was used to check proper operation of the entire spin rig system. A special two-blade rotor was designed and used to hold flat and twisted plates at various setting and sweep angles. Accurate Southwell coefficients have been obtained for several modes of a flat plate oriented parallel to the plane of rotation
Data management study, volume 5. Appendix K - Contractor data package data management /DM/ Final report
Contractor data management system for Voyager projec
Laboratory upwelled radiance and reflectance spectra of Kerr reservoir sediment waters
Reflectance, chromaticity, and several other physical and chemical properties were measured for various water mixtures of bottom sediments taken from two sites at Kerr Reservoir, Virginia. Mixture concentrations ranged from 5 to 1000 ppm by weight of total suspended solids (TSS) in filtered deionized tap water. The two sets of radiance and reflectance spectra obtained were similar in shape and magnitude for comparable values of TSS. Upwelled reflectance was observed to be a nonlinear function of TSS with the degree of curvature a function of wavelength. Sediment from the downstream site contained a greater amount of particulate organic carbon than from the upstream site. No strong conclusions can be made regarding the effects of this difference on the radiance and reflectance spectra. Near-infrared wavelengths appear useful for measuring highly turbid water with concentrations up to 1000 ppm or more. Chromaticity characteristics do not appear useful for monitoring sediment loads above 150 ppm
Coal-shale interface detection system
A coal-shale interface detection system for use with coal cutting equipment consists of a reciprocating hammer on which an accelerometer is mounted to measure the impact of the hammer as it penetrates the ceiling or floor surface of a mine. A pair of reflectometers simultaneously view the same surface. The outputs of the accelerometer and reflectometers are detected and jointly registered to determine when an interface between coal and shale is being cut through
Study of the application of hydrogen fuel to long-range subsonic transport aircraft, volume 2
The feasibility, practicability, and potential advantages/disadvantages of using liquid hydrogen as fuel in long range, subsonic transport aircraft of advanced design were studied. Both passenger and cargo-type aircraft were investigated. To provide a valid basis for comparison, conventional hydrocarbon (Jet A) fueled aircraft were designed to perform identical missions using the same advanced technology and meeting the same operational constraints. The liquid hydrogen and Jet A fueled aircraft were compared on the basis of weight, size, energy utilization, cost, noise, emissions, safety, and operational characteristics. A program of technology development was formulated
- …