Strength of hot isostatically pressed and sintered reaction bonded silicon nitrides containing Y2O3
The hot isostatic pressing of reaction bonded Si3N4 containing Y2O3 produced specimens with greater room temperature strengths than those by high pressure nitrogen sintering of the same material. Average room temperature bend strengths for hot isostatically pressed reaction bonded silicon nitride and high pressure nitrogen sintered reaction bonded silicon nitride were 767 and 670 MPa, respectively. Values of 472 and 495 MPa were observed at 1370 C. For specimens of similar but lower Y2O3 content produced from Si3N4 powder using the same high pressure nitrogen sintering conditions, the room temperature strength was 664 MPa and the 1370 C strength was 402 MPa. The greater strengths of the reaction bonded silicon nitride materials in comparison to the sintered silicon nitride powder material are attributed to the combined effect of processing method and higher Y2O3 content
Effect of Oxidation on Mechanical Properties of Fibrous Monolith Si 3 N 4 /BN at Elevated Temperatures in Air
Peer Reviewedhttp://deepblue.lib.umich.edu/bitstream/2027.42/65838/1/j.1151-2916.2002.tb00597.x.pd
Technical Change and the Wage Structure During the Second Industrial Revolution: Evidence from the Merchant Marine, 1865-1912*
ABSTRACT Using a large, individual-level wage data set, we examine the impact of a major technological innovation-the steam engine-on skill demand and the wage structure in the merchant shipping industry. We find that the technical change created a new demand for skilled workers, the engineers, while destroying demand for workers with skills relevant only to sail. It had a deskilling effect on production work-able-bodied seamen (essentially, artisans) were replaced by unskilled engine room operatives. On the other hand, mates and able-bodied seamen employed on steam earned a premium relative to their counterparts on sail. A wholesale switch from sail to steam would increase the 90/10 wage ratio by 40%, with most of the rise in inequality coming from the creation of the engineer occupation
ChemInform Abstract: OXIDATION OF SILICON NITRIDE SINTERED WITH RARE EARTH OXIDE ADDITIONS
Hot Isostatic Pressing of Silicon Nitride with Boron Nitride, Boron Carbide, and Carbon Additions
Improvement in the Oxidation Resistance of Oxide-Matrix Silicon Carbide-Particulate Composites by Mullite Infiltration
- …