Influence of the Cement Film Thickness on the Push-Out Bond Strength of Glass Fiber Posts Cemented in Human Root Canals

The present study evaluated the influence of the cement film thickness on the push-out bond strength of glass fiber posts in the cervical, medium, and apical thirds of root canal spaces. Thirty roots were randomly divided into three groups, according to the fiber post system’s drills: (G1) #2; (G2) #3; (G3) #4. The posts were cemented using a self-adhesive cement, and a small amount of powdered Rhodamine B was used as a stain. Images of both sides of each slice were obtained before and after the push-out test. To determine the cement thickness, a macro routine was developed using the software KS 400. The data were analyzed statistically using Kruskal-Wallis and Dunn’s test. G2 (14.62±5.15 MPa) showed statistically higher bond strength values than G1 (10.04±5.13 MPa) and G3 (7.68±6.14 MPa). All groups presented higher bond strength values in the apical third. The bur diameter significantly influenced the results of the shear bond strength for the push-out test. The slight increase in the cement thickness allowed an increase in the values of shear bond strength when compared to very thin or very thick cement films

Caracterização de junta soldada por brasagem de liga de níquel-cromo utilizada como biomaterial odontológico

Foram obtidos os aspectos micrográficos das zonas de fusão e das zonas termicamente afetadas de juntas soldadas pelo método comumente utilizado por protéticos de uma liga Ni-Cr usada para a confecção de próteses dentárias conhecidas como pontes-fixas. O método consiste em soldagem por maçarico com gás liquefeito de petróleo (GLP) e oxigênio, metal de adição e fluxo, para soldas de liga à base de níquel comercialmente conhecida como FIT. Corpos de prova soldados da liga FITCAST- SB (261MPa, Ni 61% – Cr 25% – Mo10,5% – Si 1,5% – Ti<1%, dados do fabricante) foram  submetidos a preparação metalográfica, microscopia óptica e testes de microdureza. Os aspectos micrográficos revelaram uma zona de fusão com uma segunda fase precipitada que variava do esférico ao dendrítico e uma zona termicamente afetada fazendo uma interface nítidamente distinta da microestrutura do metal de base. A região soldada apresentou tendência a possuir menores valores para a microdureza Vickers, muito embora tal comportamento não possa ser extrapolado devido ao reduzido número de corpos de prova ainda avaliados. O método usual de soldagem dos protéticos (brasagem) parece gerar diferenças microestruturais e mecânicas significativas entre as regiões soldadas e as não soldadas das próteses à base de Ni-Cr

Aplicabilidades clínicas do sistema adesivo universal: relato de casos / Clinical applicability of universal bond system: cases report

Os sistemas adesivos revolucionaram a odontologia estética, proporcionando ao cirurgião-dentista a possibilidade de oferecer restaurações com estética agradável e adesão a diferentes substratos. Com o lançamento dos novos sistemas adesivos universais, é de grande importância mostrar ao clínico a sua correta forma de aplicação para garantir a longevidade das restaurações tanto diretas quanto indiretas. O objetivo desse trabalho foi relatar quatro casos clínicos descrevendo o protocolo de técnicas de aplicação desses sistemas adesivos, que podem ser utilizados de maneira autocondicionante ou convencional. Os sistemas adesivos universais são produtos versáteis e de fácil utilização, já que um mesmo produto possui diversas possibilidades técnicas, diminuindo assim o tempo operatório e a sensibilidade técnica. Estes adesivos ainda carecem de maior comprovação de qualidade

“Colagem de fragmentos” uma alternativa para reabilitação do sorriso de adolescentes / "Reattachment restoration" an alternative for rehabilitating the smile os adolescents

O tratamento descrito no presente relato foi realizado durante o projeto “Reabilitação social do sorriso de adolescentes de baixa renda”, desenvolvido na Faculdade de Odontologia da UERJ. Após traumatismos em dentes anteriores que ocasionam fraturas, podemos proceder com técnicas de restauração utilizando resina composta e também com a colagem de fragmentos, que quando possível de ser aplicada reproduz harmonia e promove resultados satisfatórios. O presente trabalho visa relatar caso de colagem de fragmento de uma fratura de coroa não complicada no incisivo central superior esquerdo decorrente de um impacto ocasionado durante uma atividade recreativa escolar. Para esse caso, foi realizado o condicionamento com ácido fosfórico à 37% do fragmento e do dente propriamente dito. Após isso, foi feita a lavagem abundante de ambos e posterior aplicação do sistema adesivo dentinário seguido do cimento resinoso (Variolink System). O fragmento foi então posicionado e o conjunto fotoativado. Como último passo, foi realizado o acabamento, polimento e alívio das forças oclusais a partir de desgaste no dente. O aspecto final foi satisfatório, devolvendo ao paciente estética, função e harmonia. Além disso, foi possível reinserir o paciente socialmente, visto que o mesmo estava sofrendo descriminalização em razão do dente fraturado. Portanto, a colagem de fragmentos é uma técnica eficaz e satisfatória que deve ser levada em conta durante a formulação do plano de tratamento

Analysis of the Chemical Modification of Dental Enamel Submitted to 35% Hydrogen Peroxide “In-Office” Whitening, with or without Calcium

Purpose. The purpose of this study was to evaluate changes in calcium and phosphorus content in dental enamel when subjected to “in-office” whitening for an extended time by using a 35% hydrogen peroxide solution, with and without calcium. Materials and Methods. 10 human teeth, from which the roots had been removed, were embedded in epoxy resin, and their surfaces were smoothed. The specimens were divided into two groups; in group 1, a whitening solution without calcium was used, while in group 2, the solution included calcium. Each specimen was evaluated at 6 different points before the bleaching treatment, and these points were reassessed after each session. A total of five sessions were carried out. Concentrations of calcium and phosphorus were measured by using the technique of X-ray fluorescence. Results. After performing a statistical analysis, it was found that there was no statistically significant loss of calcium and phosphorus during the whitening treatment, and the groups showed no statistical differences. Conclusion. Excessive use of hydrogen peroxide, with or without calcium, causes no loss of calcium and phosphorus

Possibilidades de diferentes protocolos de aplicação utilizando um fotoclareador com LED violeta e diferentes concentrações de peróxido de hidrogênio: Relato de uma série de casos / Possibilities of different application protocols using a photocell light with violet LED and different concentrations of hydrogen peroxide: Report of a series of cases

Os Clareamentos dentais de consultório são procedimentos minimamente invasivos com resultados estéticos extremamente favoráveis, porém com altas taxas de sensibilidade pós operatória. Com o aumento da busca por soluções para esse problema vários protocolos vem sendo testados. O objetivo desse trabalho foi apresentar o passo-a-passo de três possíveis protocolos para o clareamento de consultório visando otimizar a rotina do clínico no consultório

Assessment of superficial rugosity of cast titanium in fluoride solutions and artificial salive

The purpose of this study was to investigate the superficial rugosity of commercially pure titanium cast, under the action of different fluoride dental solutions and synthetic saliva. All specimens received the standard metallography procedure for titanium and were divided in groups: Group 1) synthetic saliva pH 7.0; Group 2) 1.23% APF gel pH 3.5;, Group 3) 2% NaF gel pH 6; Group 4) 0.05% NaF solution pH 4.0; and Group 5) 0.05% NaF solution pH 7.5. The specimens were exposed to these solutions for 16 minutes and immersed in synthetic saliva for 96 hours. The surfaces were analyzed in a roughness device and the results were statistically treated - Snededor 'F' and Bonferroni test. In addition, scanning electron microscopy was employed to observe the surface morphology after the test. The Group 2 was the only one which had a significant increase in the superficial roughness. Authors concluded that the fluoride solutions of dental use that have a high concentration of fluoride and low pH are harmful to the surface of cast titanium

Influence of surface treatment on shear bond strength of orthodontic brackets

INTRODUCTION: The shear bond strength of orthodontic brackets bonded to micro-hybrid and micro-particulate resins under different surface treatment methods was assessed. METHODS: Two hundred and eighty test samples were divided into 28 groups (n = 10), where 140 specimens were filled with Durafill micro-particulate resin and 140 with Charisma composite. In 140 samples, a coupling agent (silane) was applied. The surface treatment methods were: Phosphoric and hydrofluoric acid etching, sodium bicarbonate and aluminum oxide blasting, stone and burs. A Universal Instron Machine was used to apply an occlusal shear force directly to the resin composite bracket surface at a speed of 0.5 mm/min. The means were compared using analysis of variance and multivariate regression to assess the interaction between composites and surface treatment methods. RESULTS: Means and standard deviations for the groups were: Sodium bicarbonate jet 11.27±2.78; burs 9.26±3.01; stone 7.95±3.67; aluminum oxide blasting 7.04±3.21; phosphoric acid 5.82±1.90; hydrofluoric acid 4.54±2.87, and without treatment 2.75±1.49. An increase of 1.94 MPa in shear bond strength was seen in Charisma groups. Silane agent application reduced the Charisma shear bond strength by 0.68 Mpa, but increased Durafill means for bicarbonate blasting (0.83), burs (0.98) and stone drilling (0.46). CONCLUSION: The sodium bicarbonate blasting, burs and stone drilling methods produced adequate shear bond strength and may be suitable for clinical use. The Charisma micro hybrid resin composite showed higher shear bond means than Durafill micro particle composite