    Effect of fluoride-containing solutions on the surface of cast commercially pure titanium

    Get PDF
    This study evaluated the effects of fluoride-containing solutions on the surface of commercially pure titanium (CP Ti) obtained by casting. CP Ti specimens were fabricated and randomly assigned to 5 groups (n=10): group 1: stored in distilled water at 37 ± 1ºC; group 2: stored in distilled water at 37 ± 1ºC and daily immersed in 0.05% NaF for 3 min; group 3: stored in distilled water at 37 ± 1ºC and daily immersed in 0.2% NaF for 3 min; group 4: stored in distilled water at 37 ± 1ºC; and immersed in 0.05% NaF every 15 days for 3 min; and group 5: stored in distilled water at 37 ± 1ºC and immersed in 0.2% NaF every 15 days for 3 min. Surface roughness was measured with a profilometer immediately after metallographic polishing of the specimens (T0) and at 15-day intervals until completing 60 days of experiment (T15, T30, T45, T60). Data were analyzed statistically by ANOVA and Tukey's test (α=0.05). There was no statistically significant difference (p>0.05) in surface roughness among the solutions. In conclusion, fluoride-containing solutions (pH 7.0) used as mouthwashes do not damage the surface of cast CP Ti and can be used by patients with titanium-based restorations.Este estudo avaliou o efeito de soluções para enxaguatório bucal contendo fluoreto sobre a superfície do titânio comercialmente puro (cp Ti) após fundição odontológica. As amostras (n=50) foram divididas igualmente: grupo A - armazenadas em água destilada a 37 ± 1ºC, grupo B - armazenadas em água destilada a 37 ± 1ºC e imersão diária em NaF a 0,05% durante 3 min, grupo C - armazenadas em água destilada a 37 ± 1ºC e imersão diária em NaF a 0,2% durante 3 min, grupo D - armazenadas em água destilada a 37 ± 1ºC e imersão em NaF a 0,05% a cada 15 dias por 3 min e grupo E - armazenadas em água destilada a 37 ± 1ºC e imersão em NaF a 0,2% a cada 15 dias durante 3 min. A rugosidade superficial foi medida logo após o polimento metalográfico das amostras (T0) e cada 15 dias de experiência até serem alcançados 60 dias (T15, T30, T45, T60). Os dados foram analisados usando ANOVA (α=0,05) e as diferenças não foram estatisticamente significantes (p>0,05) entre as diferentes soluções. Conclui-se que soluções contendo fluoreto (pH 7,0) não danificam a superfície do Ti cp e podem ser usadas como soluções para bochecho usadas por pacientes que possuem restaurações à base de titânio.FAPES

    Importance of a distal proximal contact on load transfer by implant-supported single adjacent crowns in posterior region of the mandible: a photoelastic study

    Get PDF
    OBJECTIVE: This study aimed to evaluate the importance of a distal proximal contact on the load transfer to the posterior region of the mandible by non-splinted adjacent implant-supported crowns using photoelastic stress analysis. MATERIAL AND METHODS: A rectangular model (68x30x15 mm) was made of polymethylmethacrylate resin to simulate half of the mandibular arch. One model was completed with resin replicas representing the first premolar and second molar and with two 3.75 mm dia.x11 mm internal hexagon threaded implants replacing the second premolar and first molar. The other model was manufactured in the same way but without the second molar. Both models were duplicated using photoelastic resin. The roots of the teeth replicas were covered with a layer of polyether impression material to simulate the periodontal ligament. Two different vertical loads were applied to the crowns as follows: 1 - single static point load alternately applied to the crowns replacing the second premolar and first molar (50 N); 2 - simultaneous static point loads applied to both of the crowns replacing the second premolar and first molar (100 N). The resulting isochromatic fringe pattern in the photoelastic model was monitored and photographed. RESULTS: All loading conditions studied showed that the presence of the second molar has changed the load transmission and the pattern of stresses. CONCLUSION: Results showed that the presence of a second molar proximal contact can help minimize the stresses around the implants

    Evaluation of screw loosening on new abutment screws and after successive tightening

    Get PDF
    This study evaluated the loss of the torque applied after use of new screws and after successive tightening. Four infrastructures (IE), using UCLA castable abutment type, were cast in cobalt-chromium alloy and new abutment screws (G1) were used in a first moment. Subsequently, the same abutment screws were used a second time (G2) and more than two times (G3). The values of the torques applied and detorques were measured with a digital torque wrench to obtain the values of initial tightening loss (%). Data were analyzed by ANOVA and Tukey's test (?=0.05). Significant differences were observed between the G1 (50.71% ± 11.36) and G2 (24.01% ± 3.33) (p=0.000) and between G1 (50.71% ± 11.36) and G3 (25.60% ± 4.64) (p=0.000). There was no significant difference between G2 and G3 (p=0.774). Within the limitations of the study, it may be concluded that the percentage of the initial torque loss is lower when screws that already suffered the application of an initial torque were used, remaining stable after application of successive torques.O objetivo deste estudo foi avaliar a perda do torque inicial, quando usados novos parafusos de pilares e após sucessivos apertos. Quatro infra-estruturas (IE), utilizando pilares calcináveis tipo UCLA, foram fundidas em liga de cobalto-cromo, onde novos parafusos de pilares foram utilizados (G1) em um primeiro momento. Posteriormente os mesmos parafusos de pilares foram utilizados em um segundo momento (G2), e depois por mais duas vezes (G3). Os valores de torque e detorque aplicados foram mensurados a partir de um torquímetro digital para obtenção dos valores de perda do torque inicial (%). Os dados foram coletados e submetidos à análise de variância e teste de Tukey (p<0,05). Foram observadas diferenças estatisticamente significantes entre os grupos G1 (50,71% ± 11,36) and G2 (24,01% ± 3,33) (p=0,000) and the groups G1 (50,71% ± 11,36) and G3 (25,60% ± 4,64) (p=0,000). Os maiores valores foram encontrados para o grupo G1. Não houve diferença estaticamente significante entre os grupos G2 e G3 (p=0,774). Dentro das limitações deste estudo, pôde-se observar que a porcentagem de perda de torque inicial foi menor quando os parafusos já haviam sofrido a aplicação do primeiro torque, se mantendo estáveis após os demais torques

    Abrasion wear resistance of different artificial teeth opposed to metal and composite antagonists

    Get PDF
    One of the most important properties of artificial teeth is the abrasion wear resistance, which is determinant in the maintenance of the rehabilitation's occlusal pattern. OBJECTIVES: This in vitro study aims to evaluate the abrasion wear resistance of 7 brands of artificial teeth opposed to two types of antagonists. MATERIAL AND METHODS: Seven groups were prepared with 12 specimens each (BIOLUX & BL, TRILUX & TR, BLUE DENT & BD, BIOCLER & BC, POSTARIS & PO, ORTHOSIT & OR, GNATHOSTAR & GN), opposed to metallic (M & nickel-chromium alloy), and to composite antagonists (C & Solidex indirect composite). A mechanical loading device was used (240 cycles/min, 4 Hz speed, 10 mm antagonist course). Initial and final contours of each specimen were registered with aid of a profile projector (20x magnification). The linear difference between the two profiles was measured and the registered values were subjected to ANOVA and Tukey's test. RESULTS: Regarding the antagonists, only OR (M = 10.45 ± 1.42 µm and C = 2.77 ± 0.69 µm) and BC (M = 6.70 ± 1.37 µm and C = 4.48 ± 0.80 µm) presented statistically significant differences (p < 0.05). Best results were obtained with PO (C = 2.33 ± 0.91 µm and M = 1.78 ± 0.42 µm), followed by BL (C = 3.70 ± 1.32 µm and M = 3.70 ± 0.61 µm), statistically similar for both antagonists (p>0.05). Greater result variance was obtained with OR, which presented the worse results opposed to Ni-Cr (10.45 ± 1.42 µm), and results similar to the best ones against composite (2.77 ± 0.69 µm). CONCLUSIONS: Within the limitations of this study, it may be concluded that the antagonist material is a factor of major importance to be considered in the choice of the artificial teeth to be used in the prosthesis

    Comparative study of chemical and mechanical retentive systems for bonding of indirect composite resin to commercially pure titanium

    Get PDF
    This study evaluated the effect of chemical and mechanical surface treatments for cast metal alloys on the bond strength of an indirect composite resin (Artglass) to commercially pure titanium (cpTi). Thirty cylindrical metal rods (3 mm diameter x 60 mm long) were cast in grade-1 cpTi and randomly assigned to 6 groups (n=5) according to the received surface treatment: sandblasting; chemical treatment; mechanical treatment - 0.4 mm beads; mechanical treatment - 0.6 mm beads; chemical/mechanical treatment - 0.4 mm; and chemical/mechanical treatment - 0.6 mm beads. Artglass rings (6.0 mm diameter x 2.0 mm thick) were light cured around the cpTi rods, according manufacturer's specifications. The specimens were invested in hard gypsum and their bond strength (in MPa) to the rods was measured at fracture with a universal testing machine at a crosshead speed of 2.0 mm/min and 500 kgf load cell. Data were analyzed statistically by one-way ANOVA and Tukey test (a=5%). The surface treatments differed significantly from each other (p<0.05) regarding the recorded bond strengths. Chemical retention and sandblasting showed statistically similar results to each other (p=0.139) and both had significantly lower bond strengths (p<0.05) than the other treatments. In conclusion, mechanical retention, either associated or not to chemical treatment, provided higher bond strength of the indirect composite resin to cpTi.Este estudo avaliou o efeito de tratamentos de superfície químico e mecânico para ligas metálicas fundidas sobre a resistência de união de uma resina composta indireta (Artglass) ao titânio comercialmente puro (Ti cp). Trinta varetas cilíndricas metálicas (3 mm diâmetro x 60 mm comprimento) foram fundidas em Ti cp grau 1 e igualmente divididas em grupos de acordo com os seguintes tratamentos de superfície: jateamento, químico, mecânico com esferas de 0,4 mm, mecânico com esferas de 0,6 mm, químico/mecânico com esferas de 0,4 mm e químico/mecânico com esferas de 0,6 mm. Anéis de Artglass (6 mm diâmetro X 2 mm espessura) foram fotopolimerizados ao redor das varetas, de acordo com as recomendações do fabricante. Os corpos-de-prova foram embutidos em gesso-pedra e a resistência de união (MPa) foi medida em uma máquina universal de ensaios com velocidade de 2,0 mm/min e célula de carga de 500 kgf. Os dados foram analisados estatisticamente por ANOVA a um critério e teste de Tukey (a=5%). Houve diferença estatisticamente significante (p<0,05) entre os tratamentos de superfície quanto à resistência adesiva. Retenção química e jateamento apresentaram resultados estatisticamente semelhantes (p=0,139), e ambos apresentaram menores valores de retenção que os demais tratamentos (p<0,05). Em conclusão, a retenção mecânica, associada ou não a tratamento químico, apresentou melhores resultados de resistência adesiva do compósito indireto ao Ti cp.(FAPESP) São Paulo Research Foundatio

    Comparative study of two commercially pure titanium casting methods

    Get PDF
    The interest in using titanium to fabricate removable partial denture (RPD) frameworks has increased, but there are few studies evaluating the effects of casting methods on clasp behavior. OBJECTIVE: This study compared the occurrence of porosities and the retentive force of commercially pure titanium (CP Ti) and cobalt-chromium (Co-Cr) removable partial denture circumferential clasps cast by induction/centrifugation and plasma/vacuum-pressure. MATERIAL AND METHODS: 72 frameworks were cast from CP Ti (n=36) and Co-Cr alloy (n=36; control group). For each material, 18 frameworks were casted by electromagnetic induction and injected by centrifugation, whereas the other 18 were casted by plasma and injected by vacuum-pressure. For each casting method, three subgroups (n=6) were formed: 0.25 mm, 0.50 mm, and 0.75 mm undercuts. The specimens were radiographed and subjected to an insertion/removal test simulating 5 years of framework use. Data were analyzed by ANOVA and Tukey's to compare materials and cast methods (&#945;=0.05). RESULTS: Three of 18 specimens of the induction/centrifugation group and 9 of 18 specimens of plasma/vacuum-pressure cast presented porosities, but only 1 and 7 specimens, respectively, were rejected for simulation test. For Co-Cr alloy, no defects were found. Comparing the casting methods, statistically significant differences (

    Morse taper implants at different bone levels: a finite element analysis of stress distribution

    Get PDF
    AIM: To explore the biomechanical effects of the different implantation bone levels of Morse taper implants, employing a finite element analysis (FEA). METHODS: Dental implants (TitamaxCM) with 4x13 mm and 4x11 mm, and their respective abutments with 3.5 mm height, simulating a screwed premolar metal-ceramic crown, had their design performed using the software AnsysWorkbench 10.0. They were positioned in bone blocks, covered by 2.5 mm thickness of mucosa. The cortical bone was designed with 1.5 mm thickness and the trabecular bone completed the bone block. Four groups were formed: group 11CBL (11 mm implant length on cortical bone level), group 11TBL (11 mm implant length on trabecular bone level), group 13CBL (13mm implant length on cortical bone level) and group 13TBL (13 mm implant length on trabecular bone level). Oblique 200 N loads were applied. Von Mises equivalent stresses in cortical and trabecular bones were evaluated with the same design program. RESULTS: The results were shown qualitatively and quantitatively by standard scales for each type of bone. By the results obtained, it can be suggested that positioning the implant completely in trabecular bone brings harm with respect to the generated stresses. Its implantation in the cortical bone has advantages with respect to better anchoring and locking, reflecting a better dissipation of the stresses along the implant/bone interfaces. In addition, the search for anchoring the implant in its apical region in cortical bone is of great value to improve stabilization and consequently better stress distribution. CONCLUSIONS: The implant position slightly below the bone in relation to the bone crest brings advantages as the best long-term predictability with respect to the expected neck bone loss

    Influence of Temporary Cements on the Bond Strength of Self-Adhesive Cement to the Metal Coronal Substrate

    Get PDF
    This research evaluated the influence of temporary cements (eugenol-containing [EC] or eugenol-free [EF]) on the tensile strength of Ni-Cr copings fixed with self-adhesive resin cement to the metal coronal substrate. Thirty-six temporary crowns were divided into 4 groups (n=9) according to the temporary cements: Provy, Dentsply (eugenol-containing), Temp Cem, Vigodent (eugenol-containing), RelyX Temp NE, 3M ESPE (eugenol-free) and Temp Bond NE, Kerr Corp (eugenol-free). After 24 h of temporary cementation, tensile strength tests were performed in a universal testing machine at a crosshead speed of 0.5 mm/min and 1 kN (100 kgf) load cell. Afterwards, the cast metal cores were cleaned by scraping with curettes and air jet. Thirty-six Ni-Cr copings were cemented to the cast metal cores with self-adhesive resin cement (RelyX U200, 3M ESPE In conclusion, the Provy eugenol-containing temporary cement was associated with the highest bond strength among the resin cements when Ni-Cr copings were cemented to cast metal cores. However, the eugenol cannot be considered a determining factor in increased bond strength, since the other tested cements (1 eugenol-containing and 2 eugenol-free) were similar

    Mechanical analysis of conventional and small diameter conical implant abutments

    Get PDF
    PURPOSE. The aim of the present study was to evaluate if a smaller morse taper abutment has a negative effect on the fracture resistance of implant-abutment connections under oblique compressive loads compared to a conventional abutment MATERIALS AND METHODS. Twenty morse taper conventional abutments (4.8 mm diameter) and smaller abutments (3.8 mm diameter) were tightened (20 Ncm) to their respective implants (3.5 x 11 mm) and after a 10 minute interval, implant/abutment assemblies were subjected to static compressive test, performed in a universal test machine with 1 mm/min displacement, at 45 degrees inclination. The maximum deformation force was determined. Data were statistically analyzed by student t test. RESULTS. Maximum deformation force of 4.8 mm and 3.8 mm abutments was approximately 95.33 kgf and 95.25 kgf, respectively, but no fractures were noted after mechanical test. Statistical analysis demonstrated that the evaluated abutments were statistically similar (P=.230). CONCLUSION. Abutment measuring 3.8 mm in diameter (reduced) presented mechanical properties similar to 4.8 mm (conventional) abutments, enabling its clinical use as indicated. [J Adv Prosthodont 2012;4:158-61

    Prosthetic misfit of implant-supported prosthesis obtained by an alternative section method

    Get PDF
    PURPOSE. Adequate passive-fitting of one-piece cast 3-element implant-supported frameworks is hard to achieve. This short communication aims to present an alternative method for section of one-piece cast frameworks and for casting implant-supported frameworks. MATERIALS AND METHODS. Three-unit implant-supported nickel-chromium (Ni-Cr) frameworks were tested for vertical misfit (n = 6). The frameworks were cast as one-piece (Group A) and later transversally sectioned through a diagonal axis (Group B) and compared to frameworks that were cast diagonally separated (Group C). All separated frameworks were laser welded. Only one side of the frameworks was screwed. RESULTS. The results on the tightened side were significantly lower in Group C (6.43 +/- 3.24 mu m) when compared to Groups A (16.50 +/- 7.55 mu m) and B (16.27 +/- 1.71 mu m) (P&lt;.05). On the opposite side, the diagonal section of the one-piece castings for laser welding showed significant improvement in the levels of misfit of the frameworks (Group A, 58.66 +/- 14.30 mu m; Group B, 39.4.8 +/- 12.03 mu m; Group C, 23.13 +/- 8.24 mu m) (P&lt;.05). CONCLUSION. Casting diagonally sectioned frameworks lowers the misfit levels. Lower misfit levels for the frameworks can be achieved by diagonally sectioning one-piece frameworks. [J Adv Prosthodont 2012;4:89-92