981 research outputs found

    Influence of atomic mixing and preferential sputtering on depth profiles and interfaces

    Get PDF
    Atomic mixing and preferential sputtering impose a depth resolution limit on the use of sputter sectioning to measure the composition of metal–semiconductor interfaces. Experimental evidence obtained with the Pt–Si system is used to demonstrate ion‐induced atomic mixing and then its effect on sputter etching and depth profiling. Starting with discrete layer structures, a relatively low ion dose (≳3×10^(15) cm^(−2)) first produced a mixed surface layer with thickness comparable to the ion range. Higher ion doses then result in successive sputter etching and continual atomic mixing over a constant surface layer thickness. A model is developed that is based on a sputter removal (including preferential sputtering) of atoms at the surface and a uniform mixing of atoms over a constant thickness. The model predicts the influences of atomic mixing and preferential sputtering on the depth profiling of thin‐film structures and interfaces

    Dissociation mechanism for solid-phase epitaxy of silicon in the Si <100>/Pd2Si/Si (amorphous) system

    Get PDF
    Solid-phase epitaxial growth (SPEG) of silicon was investigated by a tracer technique using radioactive 31Si formed by neutron activation in a nuclear reactor. After depositing Pd and Si onto activated single-crystal silicon substrates, Pd2Si was formed with about equal amounts of radioactive and nonradioactive Si during heating at 400 °C for 5 min. After an 1-sec annealing stage (450-->500 °C in 1 h) this silicide layer, which moves to the top of the sample during SPEG, is etched off with aqua regia. From the absence of radioactive 31Si in the etch, it is concluded that SPEG takes place by a dissociation mechanism rather than by diffusion

    Heterostructure by solid‐phase epitaxy in the Si〈111〉/Pd/Si (amorphous) system

    Get PDF
    When a thin film of Pd reacts with a 〈111〉 Si substrate, a layer of epitaxial Pd_2Si is formed. It is shown that Si can grow epitaxially on such a layer by solid‐phase reaction

    Depth dependence of atomic mixing by ion beams

    Get PDF
    Ion backscattering spectrometry has been used to investigate the depth dependence of atomic mixing induced by ion beams. Samples consisting of a thin Pt (or Si) marker a few tens of angstroms thick buried at different depths in a deposited Si (or Pt) layer were bombarded with Xe+ of 300 keV at 2×10^16 cm^–2 dose and Ar+ of 150 keV at 5×10^15cm^–2 dose. Significant spreading of the marker was observed as a result of ion irradiation. The amount of spreading was measured as a function of depth of the marker, which was then compared with the deposited energy distribution. Measurements of this kind promise new insight into the nature of the interaction between ion beams and solids

    Antimony doping of Si layers grown by solid-phase epitaxy

    Get PDF
    We report here that layers of Si formed by solid-phase epitaxial growth (SPEG) can be doped intentionally. The sample consists initially of an upper layer of amorphous Si (~1 µm thick), a very thin intermediate layer of Sb (nominally 5 Å), and a thin lower layer of Pd (~500 Å), all electron-gun deposited on top of a single-crystal substrate (1–10 Ω cm, p type, orientation). After a heating cycle which induces epitaxial growth, electrically active Sb atoms are incorporated into the SPEG layer, as shown by the following facts: (a) the SPEG layer forms a p-n junction against the p-type substrate, (b) the Hall effect indicates strong n-type conduction of the layer, and (c) Auger electron spectra reveal the presence of Sb in the layer

    Growth mechanism for solid-phase epitaxy of Si in the Si <100>/Pd2Si/Si(amorphous) system studied by a radioactive tracer technique

    Get PDF
    A tracer technique using radioactive 31Si (T1/2=2.62 h) was used to study solid-phase epitaxial growth (SPEG) of silicon. After depositing Pd and Si onto single-crystal substrates which had been activated in a nuclear reactor, Pd2Si was formed with about equal amounts of radioactive and nonradioactive silicon during heating at 400 °C for 5 min. After a second annealing stage (450 °C-->500 °C in 1 h) the silicide layer which moves to the top of the sample during SPEG was etched off with aqua regia. From the absence of radioactive 31Si in the etchant solution it is concluded that SPEG takes place by dissociation of the Pd2Si layer at the single-crystal interface to provide free Si for epitaxial growth, while new silicide is formed at the interface with the amorphous Si. These results were confirmed by evaporating radioactive silicon onto nonactivated silicon substrates before evaporation of Pd and stable amorphous Si and by measuring the activity in the SPEG sample before and after etching off the silicide layer

    Limits of composition achievable by ion implantation

    Get PDF
    In high‐dose ion implantation for materials modification, the maximum concentration of the implanted species is determined by ion‐induced erosion (sputtering) of the implanted layer. In this review, we consider the influence of preferential sputtering and atomic mixing. The maximum concentration of the implanted species is given roughly by r/S and extends over a depth W where S is the sputtering yield, r is the preferential sputtering factor (1/2≲r≲2) and W is a depth comparable to the ion range. Good agreement between calculation and experiment is found for 150‐keV Au implanted into Cu or Fe. Surface conditions, such as oxide layers or carbon films, can alter sputtering yields and can lead to the mixing of surface contaminants throughout the implanted layer. Implantation of species A into a target material AB results in a different concentration limit, but again preferential sputtering and the total sputtering yield set this limit. Calculations for PtSi indicate that the concentration of Si is decreased by implantation of Si for S≳3

    Contrasting controls on seasonal and spatial distribution of marine cable bacteria (Candidatus Electrothrix) and Beggiatoaceae in seasonally hypoxic Chesapeake Bay

    Get PDF
    Marine cable bacteria (Candidatus Electrothrix) and large colorless sulfur-oxidizing bacteria (e.g., Beggiatoaceae) are widespread thiotrophs in coastal environments but may exert different influences on biogeochemical cycling. Yet, the factors governing their niche partitioning remain poorly understood. To map their distribution and evaluate their growth constraints in a natural setting, we examined surface sediments across seasons at two sites with contrasting levels of seasonal oxygen depletion in Chesapeake Bay using microscopy coupled with 16S rRNA gene amplicon sequencing and biogeochemical characterization. We found that cable bacteria, dominated by a single phylotype closely affiliated to Candidatus Electrothrix communis, flourished during winter and spring at a central channel site which experiences summer anoxia. Here, cable bacteria density was positively correlated with surface sediment chlorophyll, a proxy of phytodetritus sedimentation. Cable bacteria were also present with a lower areal density at an adjacent shoal site which supports bioturbating macrofauna. Beggiatoaceae were more abundant at this site, where their biomass was positively correlated with sediment respiration, but additionally potentially inhibited by sulfide accumulation which was evident during one summer. A springtime phytodetritus sedimentation event was associated with a proliferation of Beggiatoaceae and multiple Candidatus Electrothrix phylotypes, with cable bacteria reaching 1000 m length cm−2. These observations indicate the potential impact of a spring bloom in driving a hot moment of cryptic sulfur cycling. Our results suggest complex interactions between benthic thiotroph populations, with bioturbation and seasonal oscillations in bottom water dissolved oxygen, sediment sulfide, and organic matter influx as important drivers of their distribution

    Validation of vessel size imaging (VSI) in high-grade human gliomas using magnetic resonance imaging, image-guided biopsies, and quantitative immunohistochemistry.

    Get PDF
    To evaluate the association between a vessel size index (VSIMRI) derived from dynamic susceptibility contrast (DSC) perfusion imaging using a custom spin-and-gradient echo echoplanar imaging (SAGE-EPI) sequence and quantitative estimates of vessel morphometry based on immunohistochemistry from image-guided biopsy samples. The current study evaluated both relative cerebral blood volume (rCBV) and VSIMRI in eleven patients with high-grade glioma (7 WHO grade III and 4 WHO grade IV). Following 26 MRI-guided glioma biopsies in these 11 patients, we evaluated tissue morphometry, including vessel density and average radius, using an automated procedure based on the endothelial cell marker CD31 to highlight tumor vasculature. Measures of rCBV and VSIMRI were then compared to histological measures. We demonstrate good agreement between VSI measured by MRI and histology; VSIMRI = 13.67 μm and VSIHistology = 12.60 μm, with slight overestimation of VSIMRI in grade III patients compared to histology. rCBV showed a moderate but significant correlation with vessel density (r = 0.42, p = 0.03), and a correlation was also observed between VSIMRI and VSIHistology (r = 0.49, p = 0.01). The current study supports the hypothesis that vessel size measures using MRI accurately reflect vessel caliber within high-grade gliomas, while traditional measures of rCBV are correlated with vessel density and not vessel caliber
    corecore