Linear and nonlinear optical properties of trigonal borate crystals K7MIn2-xYbx(B5O10)3 (M = Ca, Sr, Ba; x=0…2) with isolated B5O10 units

Noncentrosymmetric borates K7MIn2−xYbx(B5O10)3 (M = Ca, Sr, Ba; x = 0…2) were synthesized by the solid state reaction and the crystals were successfully grown by the top seeded solution growth method using the K2O-B2O3-MF2 flux. According to Rietveld refinement, the crystal structure belongs to the noncentrosymmetric R32 space group. Also, the octahedrally coordinated In atoms are located at wide ranges ∼8 Å which may be promising for phosphor and laser applications. Samples with ytterbium show a characteristic emission band in the range of 950–1050 nm related to the 2F5/2 → 2F7/2 transition of Yb3+ ions that is commonly used for laser generation. IR, Raman and absorption spectra were obtained for the samples as well. The short cut edge of UV absorption, SHG intensity comparable with KDP and low concentration quenching of luminescence suggest that the K7MIn2−xYbx(B5O10)3 borates are promising self-frequency doubling materials

Synthesis and growth of rare earth borates NaSrR(BO3)2 (R = Ho− Lu, Y, Sc)

NaSrR(BO3)2(R = Ho-Lu, Y, Sc) compounds were obtained for the first time. Their structures exhibit disordered positions of Sr2+and Na+ atoms while RO6polyhedra are connected through the BO3 groups. Large distances between R atoms and high transparency in the range of 250-900 nm make them promising for phosphor applications. A pathway to obtain single crystals was shown by growing NaSrY(BO3)2and NaSrYb-(BO3)2by the top seeded solution growth method with Na2O-B2O3-NaFflux

Three-Hour Argon Inhalation Has No Neuroprotective Effect after Open Traumatic Brain Injury in Rats

In vivo studies of the therapeutic effects of argon in traumatic brain injury (TBI) are limited, and their results are contradictory. The aim of this study was to evaluate the effect of a three-hour inhalation of argon (70%Ar/30%O2) after an open TBI on the severity of the neurological deficit and the degree of brain damage in rats. The experiments were performed on male Wistar rats (n = 35). The TBI was simulated by the dosed open brain contusion injury. The animals were divided into three groups: sham-operated (SO, n = 7); TBI + 70%N2/30%O2 (TBI, n = 14); TBI + 70%Ar/30%O2 (TBI + iAr, n = 14). The Neurological status was assessed over a 14-day period (using the limb-placing and cylinder tests). Magnetic resonance imaging (MRI) scans and a histological examination of the brain with an assessment of the volume of the lesions were performed 14 days after the injury. At each of the time points (days 1, 7, and 14), the limb-placing test score was lower in the TBI and TBI + iAr groups than in the SO group, while there were no significant differences between the TBI and TBI + iAr groups. Additionally, no differences were found between these groups in the cylinder test scores (day 13). The volume of brain damage (tissue loss) according to both the MRI and histological findings did not differ between the TBI and TBI + iAr groups. A three-hour inhalation of argon (70%Ar/30%O2) after a TBI had no neuroprotective effect

Flux growth and optical properties of K7CaY2(B5O10)3 nonlinear crystal

Non-centrosymmetric borates K7CaY2(B5O10)3 have been synthesized by solid state reaction and the crystals were successfully grown by the top seeded solution growth method using K2O-B2O3-CaF2 flux. According to the single X-ray diffraction, the structure belongs to the R32 space group with lattice parameters a = 13.2516(2) Å and c = 14.9679(3) Å. IR, Raman, absorption spectra as well as data on melting temperature were obtained for the crystal. The short edge of UV absorption and SHG intensity comparable with KH2PO4 (KDP) suggests that this crystal is a promising nonlinear-optical material