575 research outputs found

    Interface alloying and magnetic properties of Fe/Rh multilayers

    Get PDF
    Rh(20 Å)/57Fe(tFe) multilayers with Fe thicknesses tFe of 2, 5, 10, and 15 Å prepared by alternate evaporation in UHV have been investigated by x-ray diffraction (XRD), Mössbauer spectroscopy, and SQUID magnetometry. First- and second-order superstructure Bragg peaks (but no higher-order peaks) in small-angle XRD patterns suggest some compositional modulation. Mössbauer spectra taken at 4.2 K are characterized by a distribution P(Bhf) of hyperfine fields Bhf. Peaks observed in the P(Bhf) curves near 17 and 35 T are assigned to an fcc-RhFe interface alloy (~7–24 at. % Fe) with spin-glasslike properties and to a disordered ferromagnetic bcc-FeRh alloy (~96 at. % Fe), respectively. The magnetic transition temperature of the fcc alloy was found to be 23 and 45 K for tFe=2 and 5 Å, respectively, and Bhf follows a T3/2 law. For tFe=2 Å, spin-glasslike behavior was observed by magnetometry. Journal of Applied Physics is copyrighted by The American Institute of Physics

    MoS2 nanoparticle formation in a low pressure environment

    Get PDF
    Formation of MoS2 nanoparticles at pressures between 0.5 and 10 Torr has been studied. Two different chemistries for the particle nucleation are compared: one based on MoCl5 and H2S, and the other based on MoCl5 and S. In both cases particle formation has been studied in a thermal oven and in a radio-frequency discharge. Typically, the reaction rates at low pressures are too low for an efficient thermal particle production. At pressures below 10 Torr no particle production in the oven is achieved in H2S chemistry. In the more reactive chemistry based on sulfur, the optimal conditions for thermal particle growth are found at 10 Torr and low gas flows, using excess of hydrogen. In the radio-frequency discharge, nanoparticles are readily formed in both chemistries at 0.5 Torr and can be detected in situ by laser light scattering. In the H2S chemistry particles smaller than 100 nm diameter have been synthesized, the sulfur chemistry yields somewhat larger grains. Both in thermal and plasma-enhanced particle syntheses, using excess of hydrogen is beneficial for the stability and purity of the particles

    Interface alloying and magnetic properties of Fe/Rh multilayers

    Get PDF
    Rh(20 Å)/57Fe(tFe) multilayers with Fe thicknesses tFe of 2, 5, 10, and 15 Å prepared by alternate evaporation in UHV have been investigated by x-ray diffraction (XRD), Mössbauer spectroscopy, and SQUID magnetometry. First- and second-order superstructure Bragg peaks (but no higher-order peaks) in small-angle XRD patterns suggest some compositional modulation. Mössbauer spectra taken at 4.2 K are characterized by a distribution P(Bhf) of hyperfine fields Bhf. Peaks observed in the P(Bhf) curves near 17 and 35 T are assigned to an fcc-RhFe interface alloy (~7–24 at. % Fe) with spin-glasslike properties and to a disordered ferromagnetic bcc-FeRh alloy (~96 at. % Fe), respectively. The magnetic transition temperature of the fcc alloy was found to be 23 and 45 K for tFe=2 and 5 Å, respectively, and Bhf follows a T3/2 law. For tFe=2 Å, spin-glasslike behavior was observed by magnetometry. Journal of Applied Physics is copyrighted by The American Institute of Physics
    corecore