Efeito da termociclagem e da técnica de inserção na infiltração de restaurações em resina composta

The objective of this study was to evaluate in vitro the effect on leakage of two incremental filling techniques and two composite resins with different elastic modulus and similar polymerization shrinkage. Eighty Class V cavities (4x4x2mm) were prepared in bovine incisors and were randomly restored with Z-250 (Z) or Durafill VS (D) + Single Bond in axial (a) or oblique (o) increments. The restorations were divided into two groups: Not Aged - N (4-hour-storage in water at 37ºC) and Aged - A (1-week storage in water at 37ºC + 1000 x - 5º-55ºC / 1-min dwell time). The specimens were covered with 2 coats of nail varnish so that only the restoration margins were exposed to silver nitrate 50% (2h) and developed under fluorescent light (8h). After they were sectioned twice in buccal-lingual direction, the four exposed surfaces were digitized (Vidcap) and the silver nitrate penetration was measured (ImageLab) at the incisal and gingival walls. Data were analyzed by a 3-way ANOVA (Resin, Filling Technique and Aging) separately for incisal and gingival walls (alpha=0.05). Resin and Aging were statistically significant either for the incisal and the gingival walls. The microfill composite resin infiltrated more than the hybrid composite. The thermal cycling caused an overall increase in silver nitrate penetration. The filling technique affected leakage depending on the composite resin and aging regimen.O objetivo deste estudo foi avaliar o efeito de duas técnicas incrementais de inserção na infiltração de restaurações de resinas compostas com módulos de elasticidade distintos e contração de polimerização semelhante. Para isto, foram preparadas 80 cavidades Classe V (4x4x2 mm) em incisivos bovinos que foram restauradas de modo aleatório com Z-250 (Z) ou Durafill VS (D) + Single Bond em incrementos axiais (a) ou oblíquos (o). As restaurações foram divididas em dois grupos: Não Envelhecidas - N (4 h em água destilada a 37º C) e Envelhecidas - E (1 semana de armazenagem em água a 37º C + 1000 x - 5º-55ºC / 1 min de imersão). Os espécimes foram recobertos com duas camadas de esmalte cosmético de modo que apenas as margens das restaurações ficassem expostas ao nitrato de prata (2h) seguido de imersão em revelador (8h) sob luz fluorescente. Posteriormente, eles foram secionados duas vezes no sentido vestíbulo-lingual, as superfïcies expostas (4) foram digitalizadas (Vidcap) e a penetração do nitrato de prata medido (ImageLab) nas paredes incisal e gengival. Os dados foram analisados por análise de variância de três fatores (Resina, Técnica de Inserção e Envelhecimento) separadamente para as paredes incisal e gengival. Resina e Envelhecimento foram significativos. A resina composta de micropartículas mostrou maior infiltração que a híbrida. A técnica de inserção influenciou a infiltração marginal dependendo da resina e do emprego ou não de ciclos térmicos

Qualitative SEM/EDS analysis of microleakage and apical gap formation of adhesive root-filling materials

Objective: The aim of this study was to compare the correspondence between gap formation and apical microleakage in root canals filled with epoxy resin-based (AH Plus) combined or not with resinous primer or with a dimethacrylate-based root canal sealer (Epiphany). Material and Methods: Thirty-nine lower single-rooted human premolars were filled by the lateral condensation technique (LC) and immersed in a 50-wt% aqueous silver nitrate solution at 37 degrees C (24 h). After longitudinal sectioning, epoxy resin replicas were made from the tooth specimens. Both the replicas and the specimens were prepared for scanning electron microscopy (SEM). The gaps were observed in the replicas. Apical microleakage was detected in the specimens by SEM/energy dispersive spectroscopy (SEM/EDS). The data were analyzed statistically using an Ordinal Logistic Regression model and Analysis of Correspondence (alpha=0.05). Results: Epiphany presented more regions containing gaps between dentin and sealer (p<0.05). There was correspondence between the presence of gaps and microleakage (p<0.05). Microleakage was similar among the root-filling materials (p>0.05). Conclusions: The resinous primer did not improve the sealing ability of AH Plus sealer and the presence of gaps had an effect on apical microleakage for all materials.CAPES (Coordenacao de Aperfeicoamento de Pessoal de Nivel Superior)/Institutional Qualification Program (PQI) [0090/03-4]CAPES (Coordenacao de Aperfeicoamento de Pessoal de Nivel Superior)/Institutional Qualification Program (PQI

Evaluation of the adhesive interface of restorations combining composite resins with different elastic modulus

O objetivo deste estudo foi o de avaliar uma técnica teste para inserção de resinas compostas combinadas e duas técnicas convencionais, quanto à qualidade da interface adesiva, em restaurações classe V realizadas em dentes bovi nos. Foram utilizadas as resinas compostas (Z-250 e Durafill VS) com o sistema adesivo (Single Bond) em 30 preparos confeccionados nas superfícies vestibulares dos dentes (fator C= 3). Portanto, foram analisadas seis técnicas r estauradoras com 5 repetições: incremental vertical (Z-v e D-v), incremental oblíqua (Z-o e D-o), e teste [Z-t e D-t (forramento das paredes cavitárias com uma resina e preenchimento com a outra)]. Os espécimes foram armazenado s por 24 h em água a '37 GRAUS'C e secionados no sentido V-L, originando 4 superfícies para obtenção de dados por espécime, as quais foram condicionadas (ácido fosfórico a 37%, por 3s) e coradas (azul de metileno a 0,5%, por 2s ). Para mensurar o comprimento (c) e a largura (l) dos gaps, a interface adesiva foi examinada por microscopia ótica (400X). A largura média ('mü'm) dos gaps foi calculada através da equação lm = 'sigma' ('c IND. n' x 'l IND. n ') / 'sigma' 'c IND. n'. Os resultados obtidos pelo tratamento estatístico dos dados (ANOVA para Medidas Repetidas) mostraram que somente a Técnica e a Superfície de leitura foram significativas (p < 0,05). Concluiu-se com base n estes resultados que a técnica teste apresentou qualidade de interface inferior, ou seja, gaps mais largos e que, a largura média dos gaps relativa à seção central foi maior que a das superfícies externas medidasThe objective of this study was to evaluate the quality of the adhesive interface of an experimental placement technique, which combines different composite resins, and two conventional techniques used in class V restorations i n bovine teeth. Two composite resins were applied in this study (Z-250 and Durafill VS) with the adhesive system (Single Bond) in 30 cavity preparations made on the labial surface of the teeth (C-factor = 3). So, six restorativ e techniques were applied with 5 samples each: incremental vertical (Z-v e D-v), incremental oblique (Z-o e D-o), and experimental [Z-e and D-e (lining the cavity walls with one of the resins and bulk filling with the other)]. After 24-hour-storage in water (37° C), each specimen was sectioned (LB) generating 4 surfaces for gap assessment that were previously acid etched (phosphoric acid 37% for 3s) and stained (metilene blue 0.5% for 2s). The adhesi ve interface was examined by optic microscopy at 400X and both length (l) and width (w) of gaps were measured (´mü´m). The mean gap widths were calculated by the equation w = ´sigma´ (´c IND.n´ x ´l IND.n´) / ´sigma´ ´c IND. n´ . The results obtained from the data's statistical analysis (ANOVA for Repeated Measurements) showed that only Technique and Surface were significant (p < 0,05). Based in this results it was concluded that the experimental techni que showed the worst interface quality, which means that gap widths were larger and that the gap width means of the central section were higher than the measured external one

Evaluation of the adhesive interface of restorations combining composite resins with different elastic modulus

O objetivo deste estudo foi o de avaliar uma técnica teste para inserção de resinas compostas combinadas e duas técnicas convencionais, quanto à qualidade da interface adesiva, em restaurações classe V realizadas em dentes bovi nos. Foram utilizadas as resinas compostas (Z-250 e Durafill VS) com o sistema adesivo (Single Bond) em 30 preparos confeccionados nas superfícies vestibulares dos dentes (fator C= 3). Portanto, foram analisadas seis técnicas r estauradoras com 5 repetições: incremental vertical (Z-v e D-v), incremental oblíqua (Z-o e D-o), e teste [Z-t e D-t (forramento das paredes cavitárias com uma resina e preenchimento com a outra)]. Os espécimes foram armazenado s por 24 h em água a '37 GRAUS'C e secionados no sentido V-L, originando 4 superfícies para obtenção de dados por espécime, as quais foram condicionadas (ácido fosfórico a 37%, por 3s) e coradas (azul de metileno a 0,5%, por 2s ). Para mensurar o comprimento (c) e a largura (l) dos gaps, a interface adesiva foi examinada por microscopia ótica (400X). A largura média ('mü'm) dos gaps foi calculada através da equação lm = 'sigma' ('c IND. n' x 'l IND. n ') / 'sigma' 'c IND. n'. Os resultados obtidos pelo tratamento estatístico dos dados (ANOVA para Medidas Repetidas) mostraram que somente a Técnica e a Superfície de leitura foram significativas (p < 0,05). Concluiu-se com base n estes resultados que a técnica teste apresentou qualidade de interface inferior, ou seja, gaps mais largos e que, a largura média dos gaps relativa à seção central foi maior que a das superfícies externas medidasThe objective of this study was to evaluate the quality of the adhesive interface of an experimental placement technique, which combines different composite resins, and two conventional techniques used in class V restorations i n bovine teeth. Two composite resins were applied in this study (Z-250 and Durafill VS) with the adhesive system (Single Bond) in 30 cavity preparations made on the labial surface of the teeth (C-factor = 3). So, six restorativ e techniques were applied with 5 samples each: incremental vertical (Z-v e D-v), incremental oblique (Z-o e D-o), and experimental [Z-e and D-e (lining the cavity walls with one of the resins and bulk filling with the other)]. After 24-hour-storage in water (37° C), each specimen was sectioned (LB) generating 4 surfaces for gap assessment that were previously acid etched (phosphoric acid 37% for 3s) and stained (metilene blue 0.5% for 2s). The adhesi ve interface was examined by optic microscopy at 400X and both length (l) and width (w) of gaps were measured (´mü´m). The mean gap widths were calculated by the equation w = ´sigma´ (´c IND.n´ x ´l IND.n´) / ´sigma´ ´c IND. n´ . The results obtained from the data's statistical analysis (ANOVA for Repeated Measurements) showed that only Technique and Surface were significant (p < 0,05). Based in this results it was concluded that the experimental techni que showed the worst interface quality, which means that gap widths were larger and that the gap width means of the central section were higher than the measured external one

Micromorphological aspects, bond strength and adaptation to dentin as a function of the type of the adhesive and the smear layer characteristics

O objetivo do estudo foi avaliar o efeito de adesivos autocondicionantes com diferentes pHs aplicados em camadas de esfregaço (CE) fina e espessa na sua resistência de união (RU), adaptação marginal (AM) e micromorfologia. Foram utilizados 47 molares (n=5). A dentina oclusal foi exposta e cada dente foi seccionado em duas metades (unidade experimental) preparadas com lixa 600 (CE fina) e 60 (CE espessa). Os sistemas autocondicionantes foram selecionados conforme a acidez: Clearfil SE Bond (SE- fraco), Optibond Solo primer e adesivo (SO-intermediário), TYrian + One Step Plus (TYforte). Um sistema convencional, ScotchBond Multi-Uso (MP) também foi estudado. A aplicação dos adesivos foi aleatória e uma reconstrução da porção coronária foi realizada com resina Z-250. Após 24h, os palitos para microtração (0,8mm 2 ) foram preparados. Parte deles foi submetida à microtração (Kratos0,5mm/min). (Um índice de RU foi calculado levando-se em consideração a contribuição relativa dos tipos de fratura ocorridos). A outra parte foi avaliada em microscopia de luz (400x) quanto à AM tendo sido calculada a largura média de fendas (Lm) na interface de união. Para observação do padrão de condicionamento por MEV, os primers autocondicionantes e o H3PO4 foram aplicados à dentina tratada com lixa 60 e 600, removidos com banhos de álcool e acetona, fixados, desidratados com etanol, secos com HMDS e recobertos com ouro. Para observação dos prolongamentos resinosos, unidades experimentais restauradas" com Z-250 tiveram a dentina removida com HCl e NaHOCl e as amostras recobertas com ouro. Os dados de RU e AM foram submetidos a ANOVA de 2 fatores (p=0,05). Testes de regressão (p=0,05) foram aplicados para RU e Lm e de cada um com o pH dos primers autocondicionantes. Apenas o fator Adesivo foi significante para RU e Lm e não houve relação entre ambos. Observou-se que TY apresentou RU significativamente inferior aos demais sistemas, semelhantes entre si. A Lm foi tanto maior quanto menor a acidez do sistema autocondicionante e MP apresentou a menor Lm. Em condições de CE espessa, as Lm foram significativamente maiores. Notou-se que o sistema de acidez fraca foi o mais afetado pela CE espessa tanto no padrão de condicionamento como na formação de prolongamentos resinosos. Houve maior remoção da CE com o sistema de acidez forte. Concluiu-se que, nas condições experimentais testadas, apenas o sistema convencional conseguiu aliar altos valores de resistência de união a uma boa adaptação marginal, e ainda reunir aspectos de micromorfologia compatíveisThe objective of this study was to evaluate the effect of different pH self-etch adhesives applied to thick and thin smear layer (SL) on bond strength (BS), marginal adaptation (MA) and micromorphology. 47 molars (n=5) were used. The occlusal dentin was exposed and each tooth was sectioned in two halves (experimental unit) prepared with 600-grit SiC paper (thin SL) and 60-grit (thick SL). The self-etch adhesives were selected according to the acidity: Clearfil SE Bond (SE-mild), Optibond Solo primer and adhesive (SO-intermediary), Tyrian + One Step Plus (TY strong). An etch-&-rinse system, ScotchBond Multi-Purpose (MP) was also studied. The adhesives application was randomized and a resin composite build-up was made with Z-250. After 24h, the microtensile sticks (0.8 mm2) were prepared. Part of them was submitted to the microtensile bond strength test (Kratos-0.5 mm/min). (A BS index was calculated considering the relative contribution of the fracture types observed in the fractured sticks). The other part had the MA evaluated by light microscopy (400x) for the mean interfacial gap width (Gw) calculation. For the conditioning pattern SEM evaluation, the self-etch primers and the phosphoric acid was applied to dentin (60 and 600-grit), removed with baths of alcohol and acetone, fixed, dehydrated with ethanol, dried with HMDS and gold sputtered. For resin tags observation, restored experimental units were used. The dentin was removed with HCl and NaHOCl and gold sputtered. The BS and MA data was analyzed by 2-way ANOVA (p=0.05). The regression test (p=0.05) was performed for BS and Gw and for both with the self-etch primers pH. A regression test was applied for Gw and Li to evaluate their relationship (p=0.05). Only the Adhesive was significant for BS and Gw and no there was no relationship for them. TY presented significantly lower BS compared to the other adhesives that had similar BS. The higher the pH of the self-etch primers, the larger were the corresponding Gw (Gw x pH regression was significant). MP presented the lowest Gw. With thick SL, the Gw was significantly larger. The mild self-etch adhesive was affected by the thick SL in both the conditioning pattern and tags formation. The SL removal was more extensive with the strong self-etch. It was concluded that only the etch-&-rinse system achieved high BS and good MA with compatible micromorphological aspect

Effect of light-activation methods and water storage on the flexural strength of two composite resins and a compomer Efeito da fotoativação e da armazenagem em água na resistência à flexão de duas resinas compostas e um compômero

The present study evaluated the flexural strength of three composite resins recommended for direct esthetic restorations: a polyacid modified composite (Dyract AP), a unimodal composite resin (Filtek Z250) and a hybrid composite resin (Point 4). The variation factors, apart from the type of composite resin, were the light activation method and the water storage period. The composite resins were light-cured in continuous mode (40 s, 500 mW/cm²) or in ramp mode (0-800 mW/cm² for 10 s followed by 30 s at 800 mW/cm²) and stored for 24 hours or 30 days in distilled water at 37°C. The data were analyzed by ANOVA and Tukey test for multiple comparisons (alpha = 0.05). The composite resin Z250 presented the highest mean flexural strength (166.74 MPa) and Dyract AP presented the lowest one (129.76 MPa). The storage for 30 days decreased the flexural strength in ramp mode (24 h: 156.64 MPa; 30 days: 135.58 MPa). The light activation method alone did not lead to different flexural strength values.<br>O presente estudo analisou a resistência à flexão de três compósitos recomendados para restaurações estéticas diretas: um compósito poliácido-modificado (Dyract AP), uma resina composta unimodal (Filtek Z250) e uma resina composta híbrida (Point 4). Os fatores de variação, além do tipo de compósito, foram o método de fotoativação e o período de armazenagem em água. Os materiais foram fotoativados continuamente por 40 s (500 mW/cm²) ou com intensidade de luz crescente (0-800 mW/cm² por 10 s seguidos de 30 s a 800 mW/cm²). Os períodos de armazenagem foram de 24 horas ou 30 dias em água destilada a 37°C. Os dados foram submetidos à análise de variância e ao teste de Tukey para comparações múltiplas (alfa = 0,05). A resina composta Z250 apresentou a maior média de resistência à flexão (166,74 MPa) e a Dyract AP, a menor (129,76 MPa). A armazenagem por 30 dias diminuiu a resistência à flexão para o método de fotoativação crescente (24 h: 156,64 MPa; 30 dias: 135,58 MPa). O método de fotoativação isoladamente não conduziu a diferentes valores de resistência à flexão