Multi-Triplet Magnons in SrCu(BO) Studied by Thermal Conductivity Measurements in Magnetic Fields
We have measured the thermal conductivity parallel to the a-axis of the
Zn-free and 1% Zn-substituted SrCuZn(BO) in magnetic fields
up to 14 T, in order to examine the thermal conductivity due to the
multi-triplet magnons. It has been found that the thermal conductivity peak
observed in the spin gap state is suppressed by the substitution of Zn for Cu
in high magnetic fields above 6 T, while it is not changed in low magnetic
fields below 6 T. The results suggest that the thermal conductivity peak in the
spin-gap state of SrCu(BO) is composed of not only thermal
conductivity due to phonons but also that due to the multi-triplet magnons in
high fields above 6 T.Comment: 7 pages, 2 figure
Single-crystal growth and dependences on the hole concentration and magnetic field of the magnetic ground state in the edge-sharing CuO chain system CaYCuO
We have succeeded in growing large-size single-crystals of
CaYCuO with and measured the
magnetic susceptibility, specific heat and magnetization curve, in order to
study the magnetic ground state in the edge-sharing CuO chain as a function
of hole concentration and magnetic field. In , it has been
found that an antiferromagnetically ordered phase with the magnetic easy axis
along the b-axis is stabilized and that a spin-flop transition occurs by the
application of magnetic fields parallel to the b-axis. The antiferromagnetic
transition temperature decreases with increasing and disappears around 1.4. Alternatively, a spin-glass phase appears around . At where the hole concentration is 1/3 per Cu, it appears that a
spin-gap state is formed owing to the formation of spin-singlet pairs. No sign
of the coexistence of an antiferromagnetically ordered state and a spin-gap one
suggested in CaCuO has been found in
CaYCuO.Comment: 13 pages, 12 figures, 1 tabl
Enhanced thermoelectric properties by Ir doping of PtSb2 with pyrite structure
The effects of Ir doping on the thermoelectric properties of Pt1-xIrxSb2 (x =
0, 0.01, 0.03, and 0.1) with pyrite structure were studied. Measurements of
electrical resistivity rho, Seebeck coefficient S, and thermal conductivity
kappa were conducted. The results showed an abrupt change from semiconducting
behavior without Ir (x = 0) to metallic behavior at x = 0.01. The sample with x
= 0.01 exhibited large S and low rho, resulting in a maximum power factor
(S^2/rho) of 43 muW/cmK^2 at 400 K. The peculiar "pudding mold"-type electronic
band dispersion could explain the enhanced thermoelectric properties in the
metallic state.Comment: 3 pages, 2 figure
Diurnal variations from muon data at Takeyama underground station
An underground station, Takeyama, is introduced, and some results of the solar diurnal and semi-diurnal variations for the period between 1967 and 1984 are presented. There are clear tendencies of double and single solar cycle variations in the daily variations which are in good accord with those detected by other underground and neutron monitor observations
- …