Flexible White Light Emitting Diodes Based on Nitride Nanowires and Nanophosphors

International audienceWe report the first demonstration of a flexible white phosphor-converted light emitting diodes (LEDs) based on p-n junction core/shell nitride nanowires. GaN nanowires containing 7 radial In 0.2 Ga 0.8 N/GaN quantum wells were grown by metal-organic chemical vapor deposition on a sapphire substrate by a catalyst-free approach. To fabricate the flexible LED, the nanowires are embedded into a phosphor-doped polymer matrix, peeled off from the growth substrate and contacted using flexible and transparent silver nanowire mesh. The electroluminescence of a flexible device presents a cool-white color with a spectral distribution covering a broad spectral range from 400 to 700 nm. Mechanical bending stress down to a curvature radius of 5 mm doesnot yieldany degradation of the LED performance. The maximal measured external quantum efficiency (EQE) of the white LED is 9.3% and the wall plug efficiency is 2.4%

Direct van der Waals Epitaxy of Crack-Free AlN Thin Film on Epitaxial WS2

Van der Waals epitaxy (vdWE) has drawn continuous attention, as it is unlimited by lattice-mismatch between epitaxial layers and substrates. Previous reports on the vdWE of III-nitride thin film were mainly based on two-dimensional (2D) materials by plasma pretreatment or pre-doping of other hexagonal materials. However, it is still a huge challenge for single-crystalline thin film on 2D materials without any other extra treatment or interlayer. Here, we grew high-quality single-crystalline AlN thin film on sapphire substrate with an intrinsic WS2 overlayer (WS2/sapphire) by metal-organic chemical vapor deposition, which had surface roughness and defect density similar to that grown on conventional sapphire substrates. Moreover, an AlGaN-based deep ultraviolet light emitting diode structure on WS2/sapphire was demonstrated. The electroluminescence (EL) performance exhibited strong emissions with a single peak at 283 nm. The wavelength of the single peak only showed a faint peak-position shift with increasing current to 80 mA, which further indicated the high quality and low stress of the AlN thin film. This work provides a promising solution for further deep-ultraviolet (DUV) light emitting electrodes (LEDs) development on 2D materials, as well as other unconventional substrates

Direct van der Waals epitaxy of crack-free AlN thin film on epitaxial WS2

Van der Waals epitaxy (vdWE) has drawn continuous attention, as it is unlimited by lattice-mismatch between epitaxial layers and substrates. Previous reports on the vdWE of III-nitride thin film were mainly based on two-dimensional (2D) materials by plasma pretreatment or pre-doping of other hexagonal materials. However, it is still a huge challenge for single-crystalline thin film on 2D materials without any other extra treatment or interlayer. Here, we grew high-quality single-crystalline AlN thin film on sapphire substrate with an intrinsic WS2 overlayer (WS2/sapphire) by metal-organic chemical vapor deposition, which had surface roughness and defect density similar to that grown on conventional sapphire substrates. Moreover, an AlGaN-based deep ultraviolet light emitting diode structure on WS2/sapphire was demonstrated. The electroluminescence (EL) performance exhibited strong emissions with a single peak at 283 nm. The wavelength of the single peak only showed a faint peak-position shift with increasing current to 80 mA, which further indicated the high quality and low stress of the AlN thin film. This work provides a promising solution for further deep-ultraviolet (DUV) light emitting electrodes (LEDs) development on 2D materials, as well as other unconventional substrates