Strong enhancement of Jc in binary and alloyed in-situ MgB2 wires by a new approach: Cold high pressure densification

Cold high pressure densification (CHPD) is presented as a new way to substantially enhance the critical current density of in situ MgB2 wires at 4.2 and 20 K at fields between 5 and 14 T. The results on two binary MgB2 wires and an alloyed wire with 10 wt.% B4C are presented The strongest enhancement was measured at 20K, where cold densification at 1.85 GPa on a binary Fe/MgB2 wire raised both Jcpara and Jcperp by more than 300% at 5T, while Birr was enhanced by 0.7 T. At 4.2K, the enhancement of Jc was smaller, but still reached 53% at 10 T. After applying pressures up to 6.5 GPa, the mass density dm of the unreacted (B+Mg) mixture inside the filaments reached 96% of the theoretical density. After reaction under atmospheric pressure, this corresponds to a highest mass density df in the MgB2 filaments of 73%. After reaction, the electrical resistance of wires submitted to cold densification was found to decrease, reflecting an improved connectivity. A quantitative correlation between filament mass density and the physical properties was established. Monofilamentary rectangular wires with aspect ratios a/b < 1.25 based on low energy ball milled powders exhibited very low anisotropy ratios, Gamma = Jcpara/Jcperp being < 1.4 at 4.2 K and 10T. The present results can be generalized to alloyed MgB2 wires, as demonstrated on a wire with B4C additives. Based on the present data, it follows that cold densification has the potential of further improving the highest Jcpara and Jcperp values reported so far for in situ MgB2 tapes and wires with SiC and C additives. Investigations are under work in our laboratory to determine whether the densification method CHPD can be applied to longer wire or tape lengths.Comment: Submitted to Superconductors Science and Technolog

Anisotropic magnetic properties of CeAg2_2Ge2_2 single crystal

In order to investigate the anisotropic magnetic properties of CeAg$_2$Ge$_2$, we have successfully grown the single crystals, for the first time, by high temperature solution growth (flux) method. We have performed a detailed study of the grown single crystals by measuring their electrical resistivity, magnetic susceptibility, magnetization, specific heat and magnetoresistance. A clear anisotropy and an antiferromagnetic transition at $T_{\rm N}$ = 4.6 K have been observed in the magnetic properties. The magnetic entropy reaches $R$ ln 4 at 20 K indicating that the ground state and the first excited state are very closely spaced (a quasi-quartet state). From the specific heat measurements and crystalline electric field (CEF) analysis of the magnetic susceptibility, we have found the level splitting energies as 5 K and 130 K. The magnetization measurements reveal that the a-axis is the easy axis of magnetization and the saturation moment is $\mu_{\rm s}$ = 1.6 $\mu_{\rm B}$/Ce, corroborating the previous neutron diffraction measurements on a polycrystalline sample.Comment: Submitted to Phys. Rev.

Evaluation of the hydrogen solubility and diffusivity in proton-conducting oxides by converting the PSL values of a tritium imaging plate

Proton-conducting oxides have potential applications in hydrogen sensors, hydrogen pumps, and other electrochemical devices including the tritium purification and recovery systems of nuclear fusion reactors. Although the distribution of hydrogen (H) in such oxide materials is an important aspect, its precise measurement is difficult. In the present study, the hydrogen solubility and diffusivity behavior of BaZr0.9Y0.1O2.95 (BZY), BaZr0.955Y0.03Co0.015O2.97 (BZYC), and CaZr0.9In0.1O2.95 (CZI) were studied using tritiated heavy water vapor i.e., DTO (~2 kPa, tritium (T) = 0.1%) by converting the photostimulated luminescence (PSL) values of the imaging plate (IP). The samples were exposed to DTO vapor at 673 K for 2 h or at 873 K for 1 h. The disc-shaped oxide specimens (diameter ~7.5 mm; thickness ~2.3 mm; theoretical density (TD) > 98 %) were prepared by conventional powder metallurgy. The IP images of the specimen surfaces of all the three materials T-exposed revealed that BZY showed the most uniform T distribution with the highest tritium activity. The cross-sectional T concentration profiles of the cut specimens showed that T diffused deeper into BZY and BZYC than into CZI. The hydrogen solubility and diffusivity in the CZI specimen were lower than that in the BZY and BZYC specimens. This suggested that barium zirconates were more favorable proton conductors than calcium zirconates.Comment: 19 pages, 12 figure

Orbital mass secondary to infantile acute lymphoblastic leukaemia

An 8-month-old Asian infant girl was referred with a 1-week history of left periorbital swelling on a background of a narrowed left palpebral aperture over the preceding 8 weeks. There was no history of chronic illness, fever or other systemic features. Examination revealed a tender and fluctuant medial canthal swelling with associated periorbital haematoma. There were no other ophthalmic findings and neurological examination was normal. A MRI scan of the brain and orbit demonstrated abnormal soft tissue with features of an aggressive tumour in the left orbital region with no globe invasion. Peripheral blood smear revealed blast cells, confirmed by bone marrow aspirate. A diagnosis of infant acute lymphoblastic leukaemia was made. The patient was started on risk-stratified chemotherapy according to the Interfant-06 Protocol The periorbital swelling resolved by day eight following a course of prednisolone, the patient continues on chemotherapy and is currently in molecular remission

B(E2) value of even-even 108-112Pd isotopes by interacting boson model-1*

This work studies the systematic reduced transition probabilities B(E2), intrinsic quadrupole moments and deformation parameters of Pd isotopes with even neutrons from N= 62 to 66. The downward reduced transition probabilities B(E2) from gamma transition 8+ to 6+, 6+ to 4+, 4+ to 2+ and 2+ to 0+ states of even-even 108-112Pd isotopes were calculated by the Interacting Boson Model (IBM-1) and compared with the available previous experimental results. The ratio of the excitation energies of the first 4+ and the first 2+ excited states, R4/2, is also studied for the classification of symmetry of these nuclei. Furthermore we have studied systematically the transition rate R of some of the low-lying quadrupole collective states in comparison with the available experimental data. The associated quadrupole moments and deformation parameters have been calculated. The results of this calculation are in good agreement with the corresponding available experimental data. The 108-112Pd isotopes show the O(6) symmetry