Cinzas de cama sobreposta de suÃnos como adição mineral em argamassas de cimento
The sustainability of intensive swine production demands alternative destinations for the generated residues. Ashes from swine rice husk-based deep bedding were tested as a mineral addition for cement mortars. The ashes were obtained at 400 to 600ºC, ground and sieved through a 325 mesh sieve (# 0.045 mm). The characterization of the ashes included the determination of the index of pozzolanic activity with lime. The ashes were also tested as partial substitutes of Portland cement. The mortars were prepared using a cement:sand proportion of 1:1.5, and with water/cement ratio of 0.4. Three percentages of mass substitution of the cement were tested: 10, 20 and 30%. Mortar performances were assessed at 7 and 28 days determining their compressive strength. The chosen condition for calcinations at the laboratory scale was related to the maximum temperature of 600ºC since the resulting ashes contained vitreous materials and presented satisfactory values for the pozzolanic index under analysis. The pozzolanic activity indicated promising results for ashes produced at 600ºC as a replacement of up to 30% in cement masses.A sustentabilidade das regiões de produção intensiva de suÃnos requer destinos alternativos para os resÃduos gerados. Cinzas de cama sobreposta de suÃnos à base casca de arroz, foram testadas como adição mineral em substituição ao cimento. As cinzas foram obtidas nas temperaturas de 400 a 600ºC, moÃdas e passadas por peneira ABNT 325 (# 0,045 mm). A caracterização de cinzas incluiu a determinação do Ãndice de atividade pozolânica com a cal. As cinzas também foram testadas como substitutos parciais de cimento Portland. As argamassas foram preparadas na proporção cimento:areia de 1:1,5 e com fator água-cimento de 0,4. Três porcentagens de substituição do cimento comercial foram usadas: 10, 20 e 30% em massa. O desempenho das argamassas foi avaliado aos 7 e aos 28 dias com a determinação da resistência à compressão axial. A condição escolhida para calcinações em escala laboratorial foi associada à temperatura máxima de 600ºC, uma vez que as cinzas resultantes continham material vÃtreo e apresentavam valores satisfatórios para o Ãndice de pozolanicidade em análise. A atividade pozolânica indicou resultados promissores para as cinzas produzidas a 600ºC e com substituição de até 30% em massa de cimento.Capes ProcadCNP
Thermal and chemically modified plant fibres as reinforcement in cementitious matrices
The effect of hornification and hydrophobic silica (Si) coatings on the performances of plant fibre cement composites were assessed. Three macro fibres and a micro fibre, all from plant sources were used as reinforcement. Flexural results indicated that Si coated fibres increased the modulus of rupture (MOR), limit of proportionality (LOP) and modulus of elasticity (MOE) of cement composites but reduced specific energy (SE) while hornification decreased the above properties. Likewise, decreased water absorption, increased bulk density, pore volume and diameter were observed in Si coated fibre composites. Overall Si coatings on control and hornified fibres showed better pre peak behaviour in composites compared to purely hornified fibres which had a slightly better post peak performanc
Viabilidade Tecnica de Producao e Propiedades de Paineisde Particulas de Cascade Amendoim
No presente trabalho, considera-se o estudo do potencial de utilização de resÃduos da casca de amendoim, com o intuito de agregar valor a este material, por meio da fabricação de painéis de partÃculas aglomeradas com resina ureia-formaldeÃdo, prensados à temperatura de 100 oC. A qualidade dos painéis foi avaliada com base nas prescrições do documento normativo ASTM D 1037:2006 por meio de ensaios fÃsico-mecânicos de densidade, inchamento em espessura, absorção de água e flexão estática. Os painéis avaliados apresentaram densidade média variando de 0,69 a 0,83 g cm-3, MOR 4,37 a 5,34 MPa e MOE 590 a 700 MPa, para painéis com e sem tratamento preservativo. É possÃvel afirmar, baseando-se no documento normativo ANSI A208.1:1993, que o material apresenta potencial para utilização em ambientes internos, como revestimento superficial de residências, construções agrÃcolas, setor moveleiro e decorativo. Recomenda-se a intervenção no processo de fabricação do painel, para melhorar as propriedades mecânicas e possibilitar o uso estrutural do material.In this study, the potential use of residues of peanut husks was verified, in order to add value to these materials through the manufacture of panels of particleboards. For this procedure, it was used urea- formaldehyde resin and the panels were mechanical pressed at a temperature of 100 oC. The quality of the panels was evaluated based on the prescriptions of the normative document ASTM D 1037:2006, through physical and mechanical tests of characteristics, such as: density, swelling in thickness, water absorption and static bending. The panels evaluated showed bulk density varying between 0,69 a 0,83 g cm-3, MOR and MOE between 4,37 - 5,34 MPa and 590 - 700 MPa respectively, for panels with and without preservative treatment. It is possible to claim, based in the normative document ANSI A208.1:1993, that the material presents a potential for use in internal areas as superficial covering of residential buildings, agricultural buildings, furniture and decorative sectors. Intervention in the board production process is recommended, in order to improve the mechanical properties of the material and enable its structural use.Fil: Gatani, Mariana Pilar. Consejo Nacional de Invest.cientif.y Tecnicas. Centro Cientifico Tecnol.conicet - Cordoba. Centro Experimental de la Vivienda Economica(i); Argentina;Fil: Fiorelli, Juliano. Universidade Do Sao Paulo. Faculdade de Zootecnia e Engenharia de Alimentos; Brasil;Fil: Medina, Juan Carlos. Universidad Nacional de Santiago del Estero. Facultad de Cs.forestales; Argentina;Fil: Arguello, Ricardo Gustavo. Consejo Nacional de Invest.cientif.y Tecnicas. Centro Cientifico Tecnol.conicet - Cordoba. Centro Experimental de la Vivienda Economica(i);Fil: Ruiz, Agustin Pascual. Universidad Nacional de Santiago del Estero. Facultad de Cs.forestales; Argentina;Fil: do Nascimento, Maria Fatima. Universidade Do Sao Paulo. Faculdade de Zootecnia e Engenharia de Alimentos; Brasil;Fil: Savastano Jr., Holmer. Universidade Do Sao Paulo. Faculdade de Zootecnia e Engenharia de Alimentos; Brasil
Microstructure and mechanical properties of gypsum composites reinforced with recycled cellulose pulp
Study of hygral behavior of non-asbestos fiber cement made by similar hatschek process
Modelación del módulo de la resistencia a la flexión de un material compuesto cementicio a partir de propiedades en estado fresco
En la presente investigación se estudió la relación entre las propiedades del estado fresco y el estado endurecido de un material compuesto formado por una matriz de cemento Pórtland reforzado con fibra de fique dispuestas al azar, las propiedades evaluadas en estado fresco fueron: ondulabilidad, fluidez, drenabilidad y en estado endurecido el módulo de la resistencia a la flexión. Las muestras se prepararon con diferentes materias primas (Fibra de fique, Bentonita, Pulpa, Humo de SÃlice y Acronal), las componentes se agregaron a una mezcladora a velocidad constante, luego se vertió la mezcla en una cámara de drenado donde se extrajo el agua y se conformó la lámina con dimensiones de 130x50x6 mm, luego se sumergió en una piscina de curado por 28 dÃas para ser evaluado el módulo de la resistencia a la flexión. El modelo de regresión lineal que se propuso para predecir el módulo de la resistencia a la flexión, en función de las propiedades en estado fresco, se realizó a través del análisis de las interacciones entre las variables de la formulación de la mezcla utilizada. Como resultado del modelo de regresión se obtuvo que existe una clara correlación entre el módulo de la resistencia a la flexión y las propiedades predictoras ondulabilidad, fluidez y drenabilidad, además estas tienen un efecto negativo sobre el módulo de la resistencia a la flexión
Evaluation of mechanical, physical and thermal performance of cement-based tiles reinforced with vegetable fibers
The objective of this work was to analyze mechanical, physical and thermal performance of roofing tiles produced with several formulations of cement-based matrices reinforced with sisal and eucalyptus fibers. The physical properties of the tiles were more influenced by the fiber content of the composite than by the type of reinforcement. The type of the fiber was the main variable for the achievement of the best results of mechanical properties. Exposure to tropical climate has caused a severe reduction in the mechanical properties of the composites. After approximately four months of age under external weathering the toughness of the vegetable fiber-cement fell to 53-68% of the initial toughness at 28 days of age. The thermal performance showed that roofing tiles reinforced with vegetable fiber are acceptable as substitutes of asbestos-cement sheets. (c) 2006 Elsevier Ltd. All rights reserved