Mineral trioxyde aggregate versus calcium hydroxide in apexification of non vital immature teeth: Study protocol for a randomized controlled trial

<p>Abstract</p> <p>Background</p> <p>Pulp necrosis is one of the main complications of dental trauma. When it happens on an immature tooth, pulp necrosis implies a lack of root maturation and apical closure. A therapy called apexification is required to induce the formation of a calcified apical barrier allowing a permanent and hermetic root filling. The aim of this prospective randomized clinical trial is to compare Mineral Trioxide Aggregate(MTA)with Calcium Hydroxide(CH)as materials used to induce root-end closure in necrotic permanent immature incisors.</p> <p>Methods/Design</p> <p>This study, promoted by AP-HP, was approved by the ethics committee(CPP Paris Ile de France IV). 34 children aged from 6 to 18 years and presenting a non-vital permanent incisor are selected. Prior to treatment, an appropriate written consent has to be obtained from both parents and from children. Patients are then randomly assigned to either the MTA(experimental)or CH(control)groups. Recalls are performed after 3, 6 and 12 months to determine the presence or absence of a calcified apical barrier through the use of clinical and radiographic exams. Additional criteria such as clinical symptoms, apical radiolucencies, periapical index(PAI)are also noted.</p> <p>Trial registration</p> <p>ClinicalTrials.gov no. <a href="http://www.clinicaltrials.gov/ct2/show/NCT00472173">NCT00472173</a> (First inclusion: May 10, 2007; Last inclusion: April 23, 2009; study completed: April 15, 2010)</p

Sealing ability of grar MTA AngelusTM, CPM TM and MBPc used as apical plugs

This study evaluated the sealing ability of apical plugs fabricated with gray MTA AngelusTM sealer, CPM TM sealer and MBPc sealer. The root canals of 98 extracted single-rooted human teeth were instrumented with #5 to #1 Gates Glidden drills according to the crown-down technique until the #1 drill could pass through the apical foramen. The specimens were then prepared with K-files, starting with an ISO 50 until an ISO 90 could be visualized 1 mm beyond the apex. After root canal preparation, the external surface of each root was rendered impermeable and roots were assigned to 3 experimental groups (n = 30), which received a 5-mm thick apical plug of gray MTA AngelusTM, CPM TM and MBPc, and two control groups (n=4). The remaining portion of the canal in the experimental groups was filled by the lateral condensation technique. The teeth of each group, properly identified, were fixed on utility wax by their crowns and were placed in plastic flasks, leaving the apex free and facing upward. The flasks were filled with 0.2% Rhodamine B solution, pH 7.0, so as to completely cover the root apex of all teeth. The sealing ability was analyzed by measuring 0.2% Rhodamine B leakage after all groups had been maintained in this solution for 48 hours. Data were analyzed statistically by Kruskal-Wallis test and Dunn test with a=5%. The results showed that, among the tested materials used for fabrication of apical plugs, MBPc sealer had the least amount of leakage with statistically significant difference (p<0.05)

In vitro sealing ability of white and gray mineral trioxide aggregate (MTA) and white Portland cement used as apical plugs

This study evaluated the sealing ability of apical plugs made of white and gray MTA-Angelus® and white Portland cement placed via the root canal and having different thicknesses (2, 5 and 7 mm). Ninety extracted human single-rooted teeth were instrumented using a size 40 K-file to standardize the foraminal opening by the stepback technique. The teeth were assigned to 3 groups (n=30), according to the material used for fabrication of the apical plugs: A = gray MTA; B = white MTA; C = white Portland cement. The groups were subdivided into groups of 10 teeth each according to the apical plug thickness (2, 5 and 7 mm). Marginal apical dye leakage was assessed using 0.2% Rhodamine B solution in which the specimens were immersed for 72 hours at 37ºC. The roots were sectioned longitudinally in a buccolingual direction for apical plug exposure, and digital photographs were taken and analyzed by Image Tool image-analysis software. Data were analyzed statistically by Kruskal-Wallis and Dunn's tests. Significance level was set at 5%. The least percent leakage was observed for 5- and 7-mm-thick plugs (p<0.05). No significant difference (p>0.05) was found between gray MTA and white Portland cement. Among the three materials analyzed, white MTA presented the highest marginal leakage (p<0.05). The findings of the present study showed that gray MTA and Portland cement had better sealing ability than white MTA when used as apical plugs. Dye leakage was smaller for 5- and 7-mm-thick plugs compared to 2-mm-thick plugs

Long-term observation of the mineral trioxide aggregate extrusion into the periapical lesion: a case series

One-step apexification using mineral trioxide aggregate (MTA) has been reported as an alternative treatment modality with more benefits than the use of long-term calcium hydroxide for teeth with open apex. However, orthograde placement of MTA is a challenging procedure in terms of length control. This case series describes the sequence of events following apical extrusion of MTA into the periapical area during a one-step apexification procedure for maxillary central incisor with an infected immature apex. Detailed long-term observation revealed complete resolution of the periapical radiolucent lesion around the extruded MTA. These cases revealed that direct contact with MTA had no negative effects on healing of the periapical tissues. However, intentional MTA overfilling into the periapical lesion is not to be recommended