Nitrogen retention/enrichment of 316LN austenitic stainless steel welds
The development of nitrogen enriched austenitic stainless steels has been a source of recent interest due to the abundant availability of nitrogen and by the manner in which nitrogen contributes several beneficial material property effects over a wide service temperature range. It is widely recognised that, in the case of nitrogen enriched 316L, improvements in mechanical property and corrosion resistance are derived from the interstitial influence of nitrogen within the matrix. Consequently, having the best combination of strength, toughness and corrosion resistance relationships found in any group of steels, nitrogen strengthened austenitic stainless steels have tremendous scope for application in areas as diverse as the cryogenic, nuclear, power generation and chemical transportation industries
Arc pressure and weld metal fluid flow whilst using alternating shielding gases Part 1 : arc pressure measurement
As part of an ongoing process to fully evaluate the effects of an alternating shielding gas supply on gas shielded welding processes, a comparison between the arc pressures generated using argon, helium, alternating shielding gases and pulsed GTAW has been conducted. Arc pressure variation and peaking are two of the fundamental phenomena produced during the alternating shielding gas process and are said to help create a stirring action within the liquid weld metal. However, there is no published data on arc pressure measurements during an alternating shielding gas supply and, consequently, these phenomena are based solely on theoretical assumptions. The experimental measurements made have shown that alternating shielding gases produces considerably higher arc pressures than argon, helium and pulsed GTAW due to a surge at weld initiation. The transient arc pressure measurements made when using alternating shielding gases are also considerably different from the theoretical assumptions previously reported
Thin plate buckling mitigation and reduction challenges for naval ships
Thin plate buckling or distortion on ship structures is an ongoing issue for shipbuilders. It has been identified that a significant number of factors can be put in place based on prior knowledge and good practice. Additionally, research work aimed at reducing thin plate distortion has been relatively prolific, particularly in the area of simulation modelling. However, the uptake in the research findings by industry has been relatively low. A number of these findings are discussed and their application considered. For any further reductions in thin plate distortion to be generated there is a clear need for better interaction between the research institutes and the industry
Helium additions to MIG shielding gas - an economic option?
An investigation has been carried out to establish the technical and economic benefits of adding two levels of helium to a normal shielding gas. Technically no adverse issues were established using the two levels of helium, and the most significant positive one was the highly beneficial effects on travel speed increase and heat input decrease. Although helium gas carries a significant cost premium, the economic evaluation showed that overall this was a beneficial approach as the man-hour reduction associated with the welding process dominated the process cost effects
Arc pressure and weld metal fluid flow whilst using alternating shielding gases Part 2 : arc force determination
The transient variation of the shielding gas present in the alternating shielding gas process produces a dynamic action within the liquid weld metal. Flow vectors opposite in direction have been reported due to the various forces acting on the weld metal when argon and helium are present, however no data has been provided to substantiate this claim. This part of the study evaluates the various forces acting on the liquid weld metal when using argon and helium and their effects discussed. It was determined that argon produces a greater vertically downward force in the central region than helium for both the arc force and Lorentz force. While helium produces a greater radially outwards force at the pool surface than argon due to plasma shear stress and Marangoni convection. In addition, the buoyancy force, i.e. the vertically upward force in the central portion of the weld metal, was greater for helium
An evaluation of weld metal nitrogen retention and properties in 316NL austenitic stainless steel
A series of tests were conducted using varying levels of nitrogen and helium in a conventional argon shielding gas when welding 316LN austenitic stainless steel. The outcome was that a 15 per cent nitrogen addition to the argon shielding gas had the most significant effect on increasing the weld metal nitrogen. Subsequent additions of helium to the argon 15 per cent nitrogen shielding gas had very little overall benefit. Increasing the nitrogen content of the weld metal had the consequential effects of decreasing the ferrite content and the hardness. As a result of solid solution strengthening, the yield strength increased with increase in nitrogen content. There was an increase in impact toughness as the nitrogen content increased. This was related to the decreased ferrite content associated with the strong austenetizing potential of nitrogen. It was also shown that an almost fully austenitic weld metal could still have very good toughness. In combination with these effects there was no loss in corrosion resistance. The addition of nitrogen to a conventional argon shielding gas presents attractive cost and quality benefits over the established requirement to over alloy the weld filler material with expensive alloys such as nickel
Derivation of forces acting on the liquid weld metal based on arc pressure measurements produced using alternating shielding gases in the GTAW process
As part of an ongoing process to fully evaluate the effects of an alternating shielding gas supply on the gas tungsten arc and gas metal arc welding processes, a comparison between arc pressures produced using argon, helium, alternating gases and GTAW-P has been conducted. The alternating shielding gas process is reported to create a dynamic stirring action within the liquid weld metal as a result of three independent phenomena: a) variation in weld pool fluidity, b) arc pressure variation, and c) arc pressure peaking. These effects have been the basis of previous advantages associated with the process, however these phenomena have not previously been verified and are based solely on theoretical assumptions. Arc pressure measurements are presented which allowed for the numerical derivation of various forces acting on the liquid weld metal in order to estimate the flow vectors present when each shielding gas is present