11 research outputs found
Pt-Sn/C as a possible methanol-tolerant cathode catalyst for DMFC
An effective method was developed for preparing highly dispersed nano-sized Pt–Sn/C electrocatalyst synthesised by a modified polyol reduction method. From XRD patterns, the Pt–Sn/C peaks shifted slightly to lower 2θ angles when compared with commercial Pt/C catalyst, suggesting that Sn formed alloy with Pt. Based on HR-TEM images, the Pt–Sn/C nanoparticles showed small particle sizes and well dispersed onto the carbon support with a narrow particle distribution. The methanol oxidation reaction on the as-prepared Pt–Sn/C catalyst appeared at lower currents (+7.08 mA at +480 mV vs. Ag/AgCl) compared to the commercial Pt/C (+8.25 mA at +480 mV vs. Ag/AgCl) suggesting that the Pt–Sn/C catalyst has ‘methanol tolerance capabilities’. Pt–Sn/C HA Slurry pH3 catalysts showed better activity towards the oxygen-reduction reaction (ORR) than commercial Pt/C which could be attributed to smaller particle sizes. In our study, the Pt–Sn/C catalyst appears to be a promising methanol-tolerant catalyst with activity towards the ORR in the DMFC.Web of Scienc
Performance of ternary PtRuRh/C electrocatalyst with varying Pt:Ru:Rh ratio for methanol electro-oxidation
Spontaneous Bi-modification of polycrystalline Pt electrode: fabrication, characterization, and performance in formic acid electrooxidation
Effect of Cu(II) ligands on electroless copper deposition rate in formaldehyde solutions: An EQCM study
Insight into the Effect of Sn on CO and Formic Acid Oxidation at PtSn Catalysts
The role of Sn on the catalytic activity for CO and formic acid oxidation is studied by comparing the activities of differently treated PtSn/C and Pt/C catalysts. The catalysts are prepared by a microwave-assisted polyol synthesis method. As revealed by scanning tunneling and transmission electron microscopic (STM and TEM) characterization, the outcomes of the synthesis procedure for both Pt and PtSn are small particles, similar to 1.5 nm in diameter. Upon deposition on the carbon support, the particle size increases to similar to 2.5 nm due to sintering. X-ray diffraction (XRD) analysis shows that PtSn/C has a low alloying degree and is mainly composed of Pt and Pt3Sn phases. The remaining Sn is present in the form of very small tin oxide particles. Different surfaces are obtained by double-layer, oxide, and CO annealing of the Pt/C and PtSn/C catalysts and by modifying the CO-annealed surfaces with irreversibly adsorbed tin, Sn-irr. The presence of Sn in any form (oxide, alloyed, or Sn-irr) on the surface shifts the onset potential for the CO oxidation negatively by more than 0.4 V in comparison to equivalently treated Pt/C catalysts. For the CO-annealed PtSn/C catalyst, a so-called skeleton structure, Sn is present only in the subsurface layers. The subsurface Sn has a mild effect on the CO activity, and hence the onset potential is only marginally shifted to cathodic potentials by similar to 50 mV compared to that on Pt/C. The formic acid oxidation is enhanced at any of the PtSn/C surfaces with Sn in the surface layer. The activity enhancement is explained by a reduced CO poisoning of the surface Pt sites. As a consequence, the current is not entering plateau as on the Pt/C catalysts. Furthermore, the skeleton PtSn/C similar to 2 is times more active than similarly treated Pt/C. The results have been substantiated and explained by comprehensive density functional theory (DFT) simulations. The DFT results indicate that the increased oxidation rates are not only due to surface Sn but also due to a weakened CO binding in the vicinity of the surface SnOHx moieties and SnO2 particles