Memory effect in triglycine sulfate induced by a transverse electric field: specific heat measurement
The influence of a transverse electric field in the specific heat of
triglycine sulphate (TGS) has been studied. The specific heat of TGS has been
measured heating the sample from ferroelectric to paraelectric phase after
prolonged transverse electric field (i.e. perpendicular to the ferroelectric
axis). It is shown that the specific heat of TGS can remember the temperature
at which the transverse field was previously applied.Comment: ReVTeX4 Twocolumn 4 pages, 4 figure
Memory effect in triglycine sulfate induced by a transverse electric field: specific heat measurement
The influence of a transverse electric field on the specific heat of triglycine sulfate (TGS) has been studied. The specific heat of TGS has been measured on heating the sample from the ferroelectric to the paraelectric phase after prolonged application of transverse electric field (i.e. perpendicular to the ferroelectric axis). It is shown that the specific heat of TGS can 'remember' the temperature T(s) at which the transverse field was previously applied.España, Gobierno de España IS-2006-0404
Relationship Between Anti-DFS70 Autoantibodies and Oxidative Stress
Background: The anti-DFS70 autoantibodies are one of the most commonly and widely described agent of unknown clinical significance, frequently detected in healthy individuals. It is not known whether the DFS70 autoantibodies are protective or pathogenic. One of the factors suspected of inducing the formation of anti-DFS70 antibodies is increased oxidative stress. We evaluated the coexistence of anti-DFS70 antibodies with selected markers of oxidative stress and investigated whether these antibodies could be considered as indirect markers of oxidative stress. Methods: The intensity of oxidative stress was measured in all samples via indices of free-radical damage to lipids and proteins such as total oxidant status (TOS), concentrations of lipid hydroperoxides (LPH), lipofuscin (LPS), and malondialdehyde (MDA). The parameters of the non-enzymatic antioxidant system, such as total antioxidant status (TAS) and uric acid concentration (UA), were also measured, as well as the activity of superoxide dismutase (SOD). Based on TOS and TAS values, the oxidative stress index (OSI) was calculated. All samples were also tested with indirect immunofluorescence assay (IFA) and 357 samples were selected for direct monospecific anti DFS70 enzyme-linked immunosorbent assay (ELISA) testing. Results: The anti-DFS70 antibodies were confirmed by ELISA test in 21.29% of samples. Compared with anti-DFS70 negative samples we observed 23% lower concentration of LPH (P =.038) and 11% lower concentration of UA (P =.005). TOS was 20% lower (P =.014). The activity of SOD was up to 5% higher (P =.037). The Pearson correlation showed weak negative correlation for LPH, UA, and TOS and a weak positive correlation for SOD activity. Conclusion: In samples positive for the anti-DFS70 antibody a decreased level of oxidative stress was observed, especially in the case of samples with a high antibody titer. Anti-DFS70 antibodies can be considered as an indirect marker of reduced oxidative stress or a marker indicating the recent intensification of antioxidant processes
Rochelle salt in an inhomogeneous electric field
The parameters of the hysteresis loop in the ferroelectric Rochelle salt
were investigated using a sample with two pairs of electrodes: measurement
electrodes and the side ones. It has been shown that the difference between
the potentials of the measurement and the side electrodes (generating an
inhomogeneous electric field) leads to gradual decay in time t of the
remanent polarization Pr. The time required for the hysteresis loop to
disappear in the inhomogeneous electric field (not parallel to the
ferroelectric axis) decreases with temperature increase from 44±3 h
at – 9°C to 2.3±0.1 h at 21.9 °C. On the other hand, the
crystal placed for a sufficiently long time simultaneously in the measuring
electric field and in the constant inhomogeneous one may finally exhibit a
stationary hysteresis loop with a reduced remanent polarization and the
unchanged coercive field. It has been shown that the crystal as a whole does
not have to be polarized perpendicularly to the ferroelectric axis in order
for its hysteresis loop to be reduced