Substrate nanopatterning by e-beam lithography to growth ordered arrays of III-nitride nanodetectors, white light emitters, and solar cells
III-nitride nanorods have attracted much scientific interest during the last decade because of their unique optical and electrical properties [1,2]. The high crystal quality and the absence of extended defects make them ideal candidates for the fabrication of high efficiency opto-electronic devices such as nano-photodetectors, light-emitting diodes, and solar cells [1-3]. Nitride nanorods are commonly grown in the self-assembled mode by plasma-assisted molecular beam epitaxy (MBE) [4]. However, self-assembled nanorods are characterized by inhomogeneous heights and diameters, which render the device processing very difficult and negatively affect the electronic transport properties of the final device. For this reason, the selective area growth (SAG) mode has been proposed, where the nanorods preferentially grow with high order on pre-defined sites on a pre-patterned substrat
Selective area growth and characterization of InGaN nano-disks implemented in GaN nanocolumns with different top morphologies
This work reports on the morphology control of the selective area growth of GaN-based nanostructures on c-plane GaN templates. By decreasing the substrate temperature, the nanostructures morphology changes from pyramidal islands (no vertical m-planes), to GaN nanocolumns with top semipolar r-planes, and further to GaN nanocolumns with top polar c-planes. When growing InGaN nano-disks embedded into the GaN nanocolumns, the different morphologies mentioned lead to different optical properties, due to the semi-polar and polar nature of the r-planes and c-planes involved. These differences are assessed by photoluminescence measurements at low temperature and correlated to the specific nano-disk geometry
MBE growth and characterization of InGaN-based films and nanocolumns on Silicon substrates and GaN templates
InN layers: MBE growth issues
Growth of InN-based thin films: InN/InGaN QWS on GaN
Growth of InN-based nanorods
● Self Self-assembled assembled InN InN nanorods nanorods onon different different substrates substrates
● Self-assembled InGaN nanorods
● Broad- Broad-emission emission nanostructures
● Self Self--assembled assembled InGaN InGaN--based based Qdisks Qdisks
● Selective area growth (SAG) of InGaN Qdisk
E-beam nanopatterning for the selective area growth of III-V nitride nanorods
GaN/InGaN nanorods have attracted much scientific interest during the last decade because of their unique optical and electrical properties [1,2]. The high crystal quality and the absence of extended defects make them ideal candidates for the fabrication of high efficiency opto-electronic devices such as nano-photodetectors, light-emitting diodes, and solar cells [1-3]. Nitrides nanorods are commonly grown in the self-assembled mode by plasma-assisted molecular beam epitaxy (MBE) [4]. However, self-assembled nanorods are characterized by inhomogeneous heights and diameters, which render the device processing very difficult and negatively affect the electronic transport properties of the final device. For this reason, the selective area growth (SAG) mode has been proposed, where the nanorods preferentially grow on pre-defined sites on a pre-patterned substrate [5]
Recommended from our members
Critical aspects of substrate nanopatterning for the ordered growth of GaN nanocolumns
Precise and reproducible surface nanopatterning is the key for a successful ordered growth of GaN nanocolumns. In this work, we point out the main technological issues related to the patterning process, mainly surface roughness and cleaning, and mask adhesion to the substrate. We found that each of these factors, process-related, has a dramatic impact on the subsequent selective growth of the columns inside the patterned holes. We compare the performance of e-beam lithography, colloidal lithography, and focused ion beam in the fabrication of hole-patterned masks for ordered columnar growth. These results are applicable to the ordered growth of nanocolumns of different materials
E-beam nano-patterning for the ordered growth of GaN/InGaN nanorods
E-beam lithography was used to pattern a titanium mask on a GaN substrate with ordered arrays of nanoholes. This patterned mask served as a template for the subsequent ordered growth of GaN/InGaN nanorods by plasma-assisted molecular beam epitaxy. The mask patterning process was optimized for several holes configurations. The smallest holes were 30 nm in diameter with a pitch (center-to-center distance) of 100 nm only. High quality masks of several geometries were obtained that could be used to grow ordered GaN/InGaN nanorods with full selectivity (growth localized inside the nanoholes only) over areas of hundreds of microns. Although some parasitic InGaN growth occurred between the nanorods during the In incorporation, transmission electron microscopy and photoluminescence measurements demonstrated that these ordered nanorods exhibit high crystal quality and reproducible optical properties
Understanding the Selective Area Nucleation and Growth of GaN nanocolumns by MBE using Ti nanomasks
•Self- assembled Ga(In)N Nanorods and Nanostructures
•Ordered growth of GaN Nanorods: masks issues
•Ordered growth of GaN Nanorods: mechanisms
•White NanoLED
Efficient phosphor-free, white light emission from ordered arrays of GaN/InGaN nanocolumnar LEDs grown by Selective Area MBE
We fabricate and characterize novel LEDs based on InGaN/GaN nanocolumns grown on patterned substrates, leading to the periodically ordered growth of emitters directly producing white ligh
Control of the morphology on selective area growth of GaN nanocolumns by rf-plasma-assisted
Selective area growth (SAG) of GaN nanocolumns (NCs), making use of patterned or masked (nanoholes) substrates, yields a periodic, homogeneous distribution of nanostructures, that makes their processing much easier compared with self-assembled ones. In addition, the control on the diameter and density of NCs avoids dispersion in the electrooptical characteristics of the heterostructures based on this type of material (embedded InGaN/GaN quantum disks for example). Selective area growth using a mask with nanohole arrays has been demonstrated by rf-plasma-assisted MBE [1, 2]
Light-Emitting-Diodes based on ordered InGaN nanocolumns emitting in the blue, green and yellow spectral range
The growth of ordered arrays of InGaN/GaN nanocolumnar light emitting diodes by molecular beam epitaxy, emitting in the blue (441 nm), green (502 nm), and yellow (568 nm) spectral range is reported. The device active region, consisting of a nanocolumnar InGaN section of nominally constant composition and 250 to 500 nm length, is free of extended defects, which is in strong contrast to InGaN layers (planar) of similar composition and thickness. The devices are driven under pulsed operation up to 1300 A/cm2 without traces of efficiency droop. Electroluminescence spectra show a very small blue shift with increasing current, (almost negligible in the yellow device) and line widths slightly broader than those of state-of-the-art InGaN quantum wells